1100 3003 Hot Rolling Aluminum Circle for Pots

China 1100 3003 Hot Rolling Aluminum Circle for Pots, Find details about China Aluminum Circle for Pots, Hot Rolling Aluminum Circle from 1100 3003 Hot Rolling Aluminum Circle for Pots

Basic Info.

Model NO.

1100 3003

Alloy

Alloy No.

3003 1100

Tempers

O, H12, H14

Thickness

0.36-10mm

Diameter

20-1200mm

Applications

Producing Cookware,Utensil,Pots,Pans,Kettles.

Port of Loading

Qingdao,Shanghai

Trademark

Signi aluminum

Transport Package

Wooden Case

Specification

China Standard

Origin

Henan, China

HS Code

76071190

Model NO.

1100 3003

Alloy

Alloy No.

3003 1100

Tempers

O, H12, H14

Thickness

0.36-10mm

Diameter

20-1200mm

Applications

Producing Cookware,Utensil,Pots,Pans,Kettles.

Port of Loading

Qingdao,Shanghai

Trademark

Signi aluminum

Transport Package

Wooden Case

Specification

China Standard

Origin

Henan, China

HS Code

76071190

Product Desciption

1100 3003 hot rolling Aluminum Circle for Pots

Specification of aluminum circle

Aluminium circles

The properties of aluminum circles (or shaped blanks) make them ideal for use in a number of markets including the cookware, automotive and lighting industries:

Alloy	Temper	Thickness	Diameter
1050, 1060, 1070, 1100, 3003	O, H12, H14	0.36~10mm	20~1200
Remark: special specifications can be produced according to your requirement

Dimensions
Parameter	Range	Tolerance
Thickness for circles (mm)	0.71 - 6.35	for 0.71 to 1.4 +/-0.08
		for 1.41 to 2.5 +0.1, -0.13
		for 2.51 to 4.0 +/-0.13
		for 4.01 to 5.00 +/-0.15
		for 5.01 to 6.35 +/-0.20
Thickness for ovals (mm)	1.75 - 3.00	for 1.75 to 2.5 +0.1, -0.13
		for 2.51 to 3.00 +/-0.13
Diameter (mm)	102 - 1250	(a) sheared circles +2, -0
		(b) punched circles +0.5, -0
Earing	<5% for 'O' temper <9% for H12, H14, H16, H18

Mechanical properties
Alloy (AA)	Temper	%E (min) (at 50 mm gauge length)	UTS (mpa)		Bend test: radius of bend (T=material thickness)
Alloy (AA)	Temper	%E (min) (at 50 mm gauge length)	Min	Max	Bend test: radius of bend (T=material thickness)
1050	O	29	55	95	close
	H14	6	95	125	1/2T
	H18	4	125	-	1T
1070	O	29	95	-	close
	H14	6	95	120	1/2T
	H18	4	120	-	1T
3003	O	25	90	130	close
	H14	5	130	180	1/2T
	H16	4	150	195	1T
	H18	3	170	-	3T

Chemical composition
Alloy (%)	AA 1050	AA 1070	AA 1100	AA 3003
Fe	0.40	0.25	1.00	0.70
Si	0.25	0.20	(Fr + Si)	0.60
Mg	0.05	0.03	-	-
Mn	0.05	0.03	0.05	1.00 - 1.50
Cu	0.05	0.04	0.05	0.05 - 0.20
Zn	0.05	0.04	0.10	0.10
Ti	0.03	0.03	0.05	0.10 (Ti + Zr)
Cr	-	-	-	-
Each (others)	0.03	0.03	0.05	0.05
Total (Others)	-	-	0.125	0.15
Al	99.50	99.70	99.00	Remaining

Surface quality of aluminum circle

Free from scratches, pit marks, rolling bands

Applicable standards

ASTM - B - 209M, Aluminium association - aluminium standards and data, Hindalco manufacturing limits (as applicable).

Packing

The circles are packed in boxes or pallets with interleave paper, polythene, foam / thermocol. Pallets and boxes are strapped with hoop iron and clips. Silica gel packets are placed in the boxes for moisture protection.