Thermal Insulation Cross Linked Polypropylene Foam

China Thermal Insulation Cross Linked Polypropylene Foam, Find details about China Polypropylene Foam, Closed Cell Foaming Material from Thermal Insulation Cross Linked Polypropylene Foam

Model NO.
CYG-1069
Color
Nude
Density
25~330 Kg/M3
Shore Hardness
15~80 Degree
Wide
60 mm ~1800 mm
Thickness
0.1~100 mm
Length
Customized
Trademark
CYG
Transport Package
Poly Bags
Specification
customized
Origin
China
HS Code
3921199000
Model NO.
CYG-1069
Color
Nude
Density
25~330 Kg/M3
Shore Hardness
15~80 Degree
Wide
60 mm ~1800 mm
Thickness
0.1~100 mm
Length
Customized
Trademark
CYG
Transport Package
Poly Bags
Specification
customized
Origin
China
HS Code
3921199000
Radiation crosslinking Polypropylene Foam material (IXPP)
 

Radiation crosslinking Polypropylene Foam material (IXPP): The product is mixing the polypropylene with various fillers, auxiliaries, blowing agents, through granulation, extrusion, molding, irradiation crosslinking by accelerator. High-temperature foaming made a high-performance closed-cell foam material. It can be widely used in automotive interiors, aerospace, shipbuilding machinery, sports and leisure industries. It has below merits:

  •  Excellent mechanical properties, high strength at the same density conditions;
  •  Good toughness, easy to shape, breaking elongation rate can above 300%;
  •  Resistance to high temperature , small heat reduction, 120° shrinkage less than 2% under temperature 120 degree;
  •  High temperature foaming, low odor, less VOC volatile.


The INDEX of IXPP
 
PHYSICAL PROPERTIESIndexStandard
 10B(1m m)15B(2mm)20B(3mm)25B(3mm)

GB/T6344 (MPa)
Density(kg/m3)100±1566±750±540±5GB/T6344 (MPa)
Tensile strength(Mpa)TT >1.3>0.9>0.6>0.5GB/T6344 (MPa)
 LL >2.1>1.6>0.9>0.7GB/T6344 (MPa)
Elongation (%)T>250>250>250>200GB/T6344 (MPa)
 L>300>250>250>200GB/T6344 (MPa)
Compressed Distortions (Mpa,25%)
>200
>100
>75
>60		JIS K6767
 
 

What's the difference between IXPP / IXPE / XPE?

XPE - crosslinked by chemical cross-linked agent (DCP), bubble is big, surface is rough.
IXPP / IXPE - cross-linked by electron accelerator irradiation, bubble is uniform and small, foam has more excellent mechanical performance, thermal forming properties and smooth surface.
Compared with IXPE/XPE, IXPP has better mechanical performance, resistance to higher temperature up to 120 degree. It's better forming depth, ideal foam material for automotive interior products.

A new type of polymer foaming material. It's made of polypropylene resin (PP) with other filler and foaming agent.



It has good thermal stability (maximum service temperature up to 130 ºC);
IXPP materials environmentally friendly, low VOC (with industry test reports).

The main applications of IXPP
 
Thermal Insulation Cross Linked Polypropylene FoamThermal Insulation Cross Linked Polypropylene Foam
 
 
It can be widely used in automotive interior, aerospace, ship machinery, leisure and
other industries.
Dashboard, door panel, console, decorative surface


IXPP material benefits
 

 

    •  Good thermal stability (max over 130°C)
    •  Size stability at high temperature
    •  High toughness
    •  High tensile strength
    •  Impact strength and other excellent mechanical properties
    •  Compliant surface
    •  Excellent microwave adaptability
    •  Environmental protection


Thermal Insulation Cross Linked Polypropylene Foam
Thermal Insulation Cross Linked Polypropylene Foam


Thermal Insulation Cross Linked Polypropylene Foam
Thermal Insulation Cross Linked Polypropylene Foam

 

You Might Also Like