High Temperature Machinable Zirconia Zro2 Ceramic Blocks, Find details about China Zirconia Ceramic, Ceramics from High Temperature Machinable Zirconia Zro2 Ceramic Blocks
1.High strength and hardness
2. Good wear resistance
3. Insulation, corrosion resistance
4. High lubrication and low resistance
Name of the materials | 99% aluminium oxide | 95% aluminium oxide | Zirconia | ||
Main ingredients | 99% Al2O3 | 95% Al2O3 | ZrO2 | ||
The material properties | Density | g/cm3 | 3.9 | 3.6 | 6 |
sintering temperature | ºC | 1700 | 1680 | 1600 | |
physical property | Hardness | HV | 1700 | 1500 | 1300 |
rupture strength | kgf/cm2 | 3500 | 3000 | 11000 | |
compressive strength | kgf/cm2 | 30000 | 25000 | 25000 | |
fracture toughness | Mpa.m3/2 | 4 | 3-4 | 3-4 | |
thermodynamic property | maximum servise temperature | ºC | 1500 | 1450 | 1300 |
Heat resisting impact | T(ºC) | 200 | 220 | 360 | |
pyroconductivity | w/m.k | 31.4 | 25 | 3 | |
(25ºC-300ºC) | 15.9 | 14 | 14 | ||
Appliance property | Volume Resistance /20ºC | Ω/cm2 | >1012 | >1012 | >1012 |
Volume Resistance /100ºC | 1012-1013 | 1012-1013 | 1012-1013 | ||
Volume Resistance /300ºC | >1012 | >1012 | 5x109 | ||
Dielectric Strength | kv/mm | 18 | 18 | 18 | |
Dielectric constant(100MHZ) | (E) | 10 | 9.5 | 9.5 | |
Dielectric tangent | (tgδ) | 0.4x10-3 | 0.4x10-3 | 0.4x10-3 |