Stainless Steel Welding Electrodes Welding Rod E312-16 E308-16

China Stainless Steel Welding Electrodes Welding Rod E312-16 E308-16, Find details about China Stainless Steel Welding Electrodes, E312-16 Welding Electrodes from Stainless Steel Welding Electrodes Welding Rod E312-16 E308-16

Slag Characteristic
Acidic
Stainless Steel Welding Rod Type
Chromium Nickel Stainless Steel
Function
Surfacing Electrode
Welding Power
AC
Sample
Free
Delivery Time
15 Days
Trademark
Stone bridge brand
Transport Package
20kg Per Carton
Specification
2.5mm 3.2mm 4.0mm 5.0mm
Origin
China
HS Code
831110
Slag Characteristic
Acidic
Stainless Steel Welding Rod Type
Chromium Nickel Stainless Steel
Function
Surfacing Electrode
Welding Power
AC
Sample
Free
Delivery Time
15 Days
Trademark
Stone bridge brand
Transport Package
20kg Per Carton
Specification
2.5mm 3.2mm 4.0mm 5.0mm
Origin
China
HS Code
831110

 

 

 

Product Description

  Factory sale stainless steel welding electrodes AWS E312-16 GBE312-16 

  Size available: 2.5mm  3.2mm 4.0mm 5.0mm 

  Package : 1kg or 5kg per plastic box & 20kg per carton 

 Stainless Steel Welding Electrodes Welding Rod E312-16 E308-16

  

Dual-phase Stainless Steel Electrode  AWS E312-16  GB E312-16

Introduction: A1002 is a kind of dual-phase steel electrode with lime-titania type coating. Due to the 40% ferrite in the deposited metal, it has excellent crack-resistance. It has excellent welding performance.

Uses: Used for welding high-carbon steel, tool steel, high temperature steel, armor steel, dissimilar steel, etc.

Chemical Composition of Deposited Metal (%)

Chemical Composition

C

Mn

Si

S

P

Ni

Cr

Guarantee Value

≤0.15

0.5~2.5

≤0.90

≤0.030

≤0.040

8.0~10.5

28.0~32.0

 

Mechanical Properties of Deposited Metal

Test Item

Rm(MPa)

A(%)

Guarantee Value

≥660

≥22

 

Reference Current (AC, DC+)

Electrode Diameter(mm)

φ2.5

φ3.2

φ4.0

φ5.0

Welding Current (A)

50~80

80~110

110~160

160~220

 

Instructions:
     1.The electrodes should be baked under about 250°C for an hour before welding.

2.Direct current had better be used and the current should not be too strong.


Welding Positions:

H OH HF F VU

 

 

Applications: 

Suitable for welding of Heavy machinery parts, earth moving equipments, automobile spring, trumnions ofcement mill and other allied components, parts subject to corrosion and impact. Joining and surfacing of High Carbon, low and high alloy steel, tool steel, spring steel, manganese steel, case hardening steel, high speed steel, cost steel etc   

Feature:   

1.Brand:Stone bridge brand  

2.Certificate: ISO9001-2008, CE,SGS  

3.OEM: Acceptable  

4.Package: 5kgs/pvc box; 4 pieces of inner box(20kg)/carton; 1 ton/pallet  

5.packaging can be changed according to your needs.  

6.Sample: free  

Advantages:

1.Little Spatter   

2. Excellent  welding process  

3. Very good for machinable  



Packaging & Shipping :   

1. 5kg/pvc box(shrink bag+pvc box)
    4 pvc boxes(20kgs)/carton
    50 carton(1 ton)/pallet

2. As clients' requirement 

 Stainless Steel Welding Electrodes Welding Rod E312-16 E308-16Stainless Steel Welding Electrodes Welding Rod E312-16 E308-16


Stainless Steel Welding Electrodes Welding Rod E312-16 E308-16
 

Time: Normally ready goods within 8 to 25 days. 

Term: CIF CFR FOB EXW  



Our Services
  • OEM is acceptable 
  • Sample Free 
Stainless Steel Welding Electrodes Welding Rod E312-16 E308-16