Low Voc High Strength Me Glue Structural Adhesive

China Low Voc High Strength Me Glue Structural Adhesive, Find details about China Ms Glue, Ms Silicone Glue from Low Voc High Strength Me Glue Structural Adhesive

Basic Info.

Model NO.

Megaglue MS667

Classification

Room Curing

Characteristic

Weatherability

Color

White

Component

One Component

Density g/cm3

1.50

Tack Free Time/ Min

20 ~ 40

Cure Rate (mm/24 Hrs)

About 4

Cure Condition

Humidity, 23ºC, Rh 50%

Hardness (Shore a)

Tensile Strength (MPa)

About 3.0

Tensile Shear Strength (MPa)

2.3 (3 Series Aluminum)

Elongation at Break (Speed 200 mm/Min, %

About 220

Shelf Life

12 Months

Trademark

MegaGlue

Transport Package

600ml/ Sausage, 20 Sauaeges/Box, 45 Boxes/ Pallet

Specification

600ml/ sausage

Origin

Shanghai

Model NO.

Megaglue MS667

Classification

Room Curing

Characteristic

Weatherability

Color

White

Component

One Component

Density g/cm3

1.50

Tack Free Time/ Min

20 ~ 40

Cure Rate (mm/24 Hrs)

About 4

Cure Condition

Humidity, 23ºC, Rh 50%

Hardness (Shore a)

Tensile Strength (MPa)

About 3.0

Tensile Shear Strength (MPa)

2.3 (3 Series Aluminum)

Elongation at Break (Speed 200 mm/Min, %

About 220

Shelf Life

12 Months

Trademark

MegaGlue

Transport Package

600ml/ Sausage, 20 Sauaeges/Box, 45 Boxes/ Pallet

Specification

600ml/ sausage

Origin

Shanghai

Product Desciption

MegaGlue® MS667 is one-component sealant based on Silica modified polymers, which cures by reaction with moisture to an elastic product. The skin formation and curing times are dependent on humidity and temperature, and the curing time also depends on joint depth. By increasing the temperature and moisture these times can be reduced; low temperature as well as low moisture retard the process. MegaGlue® MS667 is particularly sag-resistant leading to a high position tack after matching of the parts to be bonded. MegaGlue® MS667 is free of solvents, isocyanates, silicones and PVC. It demonstrates good adhesion to many substrates. MegaGlue® MS667 allows accelerated curing as two-component material.

Low Voc High Strength Me Glue Structural Adhesive

Product Detail
Main Material	Modified Silica
Color	White/Gray/Black
Appearance	Paste, thixotropy
Component	One component
Density g/cm3	1.50 ± 0.05
Tack free time/ min	20 ~ 40
Cure rate (mm/24 hrs)	About 4
Cure condition	Humidity, 23ºC, RH 50%
Hardness (Shore A)	50
Tensile strength (MPa)	About 3.0
Tensile shear strength (MPa)	2.3 (3 series aluminum // 3 series aluminum) 2.3 (Stainless steel // Stainless steel) 2.3 (Glass // Glass)
Elongation at break (speed 200 mm/min, %)	About 220
Shelf Life	12 months
Features	MegaGlue® MS667 is one-component sealant based on silicamodified polymers, which cures by reaction with moisture to an elastic product. The skin formation and curing times are dependent on humidity and temperature, and the curing time also depends on joint depth. By increasing the temperature and moisture these times can be reduced; low temperature as well as low moisture retard the process. MegaGlue® MS667 is particularly sag-resistant leading to a high position tack after matching of the parts to be bonded. MegaGlue® MS667 is free of solvents, isocyanates, silicones and PVC. It demonstrates good adhesion to many substrates. MegaGlue® MS667 allows accelerated curing as two-component material.
Application	MegaGlue® MS667 is suitable for bonding of metals and plastics, such as side panels and roof covers in the manufacture of vehicles and caravans.

Package
Cartridge 300ml(hard)
600ml(hose)

Storage
The goods are recommended to be kept in the temperature ranging from 10ºC to 30ºC. Direct sunlight, heat, frost should be avoided. The storage environment must be dehumidified, In original sealed buckets, it has a shelf life of 12 months.