Low Shrinkage Tin Cured Liquid Silicone material Making Mold
China Low Shrinkage Tin Cured Liquid Silicone material Making Mold, Find details about China Liquid Silicone Mold, Tin Cure Silicone from Low Shrinkage Tin Cured Liquid Silicone material Making Mold
Basic Info.
Model NO.
902-40, 902-30, H8225, H8230
Trademark
XD silicone
Specification
10KG, 20KG, 40KG, 50KG
Origin
Beijing
HS Code
3910000000
Model NO.
902-40, 902-30, H8225, H8230
Trademark
XD silicone
Specification
10KG, 20KG, 40KG, 50KG
Origin
Beijing
HS Code
3910000000
Product Desciption
Appilications:
1. sculpture, cement / gypsum product, architectural and furniture elements
2. resin crafts, casting wax, art objects
Features:
High temperature resistance, acid and alkali-resistance, aging resistance.
Low shrinkage, high hardness and no-deformation
High tensile and tear strength, easy to de-molding
Technical data sheet:
How to use:
1.A and B must be mixed evenly into a clean plastic or metal container, The bottom and walls of the container must be scraped well to ensure that the silicone is mixed with the curing agent.
2.The pre-operation time of the mixed is 30-40 minutes at room temperature, and the product prototype is poured by vacuum defrosting.The product can be cured completely at room temperature of 3-4 hours and heated at 80-120ºC for 30 minutes.
3. When pouring or brushing mold for medium or large products, it is recommended to pour or brush 2-3mm thick silica gel on the surface of the product to fully and completely contact with the prototype.
4.At 25ºC, A/B is fully mixed and stored safely for 30-40 minutes.The higher the temperature, the shorter the storage time.
Package: 10KG, 20KG, 25KG, 200KG or according to customer requirements.
1. sculpture, cement / gypsum product, architectural and furniture elements
2. resin crafts, casting wax, art objects
Features:
High temperature resistance, acid and alkali-resistance, aging resistance.
Low shrinkage, high hardness and no-deformation
High tensile and tear strength, easy to de-molding
Technical data sheet:
| Model | 902-40 | 902-30 | H8225 | H8230 |
| Mixing ratio (A:B) | 100:2~3 | 100:2~3 | 1:1 | 1:1 |
| Hardness (Shore A)≥ | 25 | 30 | 25 | 30 |
| Tear-strength (kgf/c m²)≥ | 21 | 22 | 25 | 26 |
| Viscosity ( mixed 25°C mpa.S) | 25000±2000 | 25000±2000 | 18000±2000 | 20000±2000 |
| Shrinkagerate (%)≤ | 0.2 | 0.2 | 0.1 | 0.1 |
| Elongation(%) | 450 | 400 | 450 | 400 |
How to use:
1.A and B must be mixed evenly into a clean plastic or metal container, The bottom and walls of the container must be scraped well to ensure that the silicone is mixed with the curing agent.
2.The pre-operation time of the mixed is 30-40 minutes at room temperature, and the product prototype is poured by vacuum defrosting.The product can be cured completely at room temperature of 3-4 hours and heated at 80-120ºC for 30 minutes.
3. When pouring or brushing mold for medium or large products, it is recommended to pour or brush 2-3mm thick silica gel on the surface of the product to fully and completely contact with the prototype.
4.At 25ºC, A/B is fully mixed and stored safely for 30-40 minutes.The higher the temperature, the shorter the storage time.
Package: 10KG, 20KG, 25KG, 200KG or according to customer requirements.
You Might Also Like
Plastic Paving Concrete Mold DIY Walkway Stones Mould Landsc......
Baroque Freshwater Pearl Necklace fashion Jewelry Jewellery ......
China Professional Made Super Big Size Ductile Iron Flange P......
Supermarket Storage Container Plastic Folding Stackable Coll......
Plastic Disposable Hitachi Beckman Sample Cup
Bulk Pen Drive Wood USB Flash Drive
Debo 5 Years Warranty HPL Toilet Cubicle Board
Luxury Hotel 1500 Supreme Collection Bed Sheet Set
Sodium Hyaluronic Acid Gel Injection for Lip, Face, Nose, Br......
Fenugreek Seed Extract 4-Hydroxyisoleucine for Improve Insul......
Rechargeable Battery 25ah 3.2V LiFePO4 Battery Cell
Radial Truck Tyre 10.00r20 11.00r20 12.00r20, TBR