China Inconel 800 Incoloy 800ht Inconel 825 Nickel Alloy Plate, Find details about China Inconel 800 Nickel Plate, Inconel 800 Sheet from Inconel 800 Incoloy 800ht Inconel 825 Nickel Alloy Plate
Incoloy 800, 800H, and 800HT are nickel-iron-chromium alloys with good strength and excellent resistance to oxidation
and carburization in high-temperature exposure. These nickel steel alloys are identical except for the higher level of carbon
in alloy 800H, and the addition of up to 1.20 percent aluminum and titanium in alloy 800HT. Incoloy 800 was the first of these
alloys and it was slightly modified into Incoloy 800H. This modification was to control carbon (.05-.10%) and grain size to
optimize stress rupture properties. Incoloy 800HT has further modifications to the combined titanium and aluminum levels
(.85-1.20%) to ensure optimum high temperature properties. The nickel alloy is dual certified (800H/HT) and combines the
properties of both forms. Incoloy 800H/HT alloy was intended for high temperature structural applications. The nickel content
makes the alloys highly resistant to both chloride stress-corrosion cracking and to embrittlement from precipitation of sigma
phase. The general corrosion resistance is excellent. In the solution annealed condition, alloys 800H and 800HT have
superior creep and stress rupture properties. Today, most suppliers, including Mega Mex, only carry the dual certified 800H/HT alloy.
Incoloy 800 is primarily used in applications with temperatures up to 1100° F, where alloys 800H and 800HT are normally
used in temperatures above 1100° F where resistance to creep and rupture is required. The chemical balance allows the
nickel steel alloy to exhibit excellent resistance to carburization, oxidation and nitriding atmospheres. Incoloy 800HT will not
become embrittled even after long periods of usage in the 1200-1600° F range where many stainless steels become brittle.
Excellent cold forming characteristics typically associated with the nickel-chromium alloys are exhibited with 800HT. When
cold formed extensively the grain size produces a visibly undulated surface called "orange peel". Incoloy 800HT can be
welded by the common techniques used on stainless steels.
What are the characteristics of Incoloy 800H/HT?
In what applications is Incoloy 800H/HT used?
Ni | Cr | Fe | C | Al | Ti | Al+Ti |
30-35 | 19-23 | 39.5min | 0.1max | 0.15-0.6 | 0.15-0.6 | 0.3-1.2 |
Ni | Cr | Fe | C | Al | Ti | Al+Ti |
30-35 | 19-23 | 39.5min | 0.05-0.1 | 0.15-0.6 | 0.15-0.6 | 0.3-1.2 |
Ni | Cr | Fe | C | Al | Ti | Al+Ti |
30-35 | 19-23 | 39.5min | 0.06-0.1 | 0.25-0.6 | 0.25-0.6 | 0.85-1.2 |