18CrNiMo7-6  18CrNiMo7 18NCD6 1.6587 820A16 Forged Steel Round Square bar UT Tested

1.18CrNiMo7-6 18CrNiMo7 18NCD6 1.6587 820A16 forged steel bar sizes we can offer;
Round bar: 200-1000mm
Square bar:150×150-600×600mm

2.Supply condition for 18CrNiMo7-6 18CrNiMo7 18NCD6 1.6587 820A16  Forged steel bars:
Black /Rough Machined /Rough turned

3.Futhur heat treatment for 18CrNiMo7-6 18CrNiMo7 18NCD6 1.6587 820A16  forged steel :
Normalized
Annealed
Q&T(Quenched&Tempered)

4.18CrNiMo7-6 18CrNiMo7 18NCD6 1.6587 820A16  Forged Steel round bar tolerance:
Black surface
Forged sizes up to 500mm (-0/+5mm)
Forged sizes above 500mm in diameter (-0/+8mm)
Machined surface to all sizes (-0/+3mm)

5.18CrNiMo7-6 18CrNiMo7 18NCD6 1.6587 820A16 Equivalent 
 
6.Chemical composition of  18CrNiMo7-6 18CrNiMo7 18NCD6 1.6587 820A16
7.HEAT TREATMENT OF 18CrNiMo7-6 18CrNiMo7 18NCD6 1.6587 820A16  FORGED STEEL

• Soft Annealing: Heat 17CrNiMo6 to 650-700oC, cool slowly in furnace. This will produce a maximum Brinell hardness of 229.

• Normalizing: 850-880oC, air.
• Hardening: Carburising: 880-980oC. Core Hardening: 830-870oC, water. Case Hardening: 780-820oC, water.
• Tempering:Temperature: 150-200oC

8.Quality control:
1. Melting Process: EAF/BOF+LF+VD resulting in ingots
2. Both ends cut by saw
3. Ratio of forging:minimum 3:1
4. Grain size of final product: according to ASTM E112 more than 5,preferred more than 8
5. Ultrasonic test: As per SEP1921 Class C/c or D/d

9.MOQ: one piece per size/grade

10.Payment term: FOB CIF CFR EXW and so on

11.Delivery time : 7 to 30 days after deposit received.

12.Mark on both ends
Heat number, size, Length,grades, Weight,Origin (as per contract), or other as required










18CrNiMo7-6 18CrNiMo7 18NCD6 1.6587 820A16
18CrNiMo7-6 18CrNiMo7 18NCD6 1.6587 820A16
18CrNiMo7-6 18CrNiMo7 18NCD6 1.6587 820A16