Steel Round Bar AISI4140 42CrMo 1.7225 Alloy Steel Bar
China Steel Round Bar AISI4140 42CrMo 1.7225 Alloy Steel Bar, Find details about China 42CrMo Alloy Steel Bar, Steel Round Bar from Steel Round Bar AISI4140 42CrMo 1.7225 Alloy Steel Bar
Basic Info.
Model NO.
alloy steel bar
Special Use
Cold Heading Steel
Application
Structural Steel Bar
Main Grade
AISI4140 42CrMo Scm440 Scm435 1.7225
Material
Alloy Steel Bar
Hot Rolled Steel Bar Size
16-310mm
Forged Steel Bar Size
200-800mm
Cold Drawn Steel Bar
5-100mm
Trademark
dajin
Transport Package
Anti-Rust Packaging
Specification
5-800mm
Origin
China
Model NO.
alloy steel bar
Special Use
Cold Heading Steel
Application
Structural Steel Bar
Main Grade
AISI4140 42CrMo Scm440 Scm435 1.7225
Material
Alloy Steel Bar
Hot Rolled Steel Bar Size
16-310mm
Forged Steel Bar Size
200-800mm
Cold Drawn Steel Bar
5-100mm
Trademark
dajin
Transport Package
Anti-Rust Packaging
Specification
5-800mm
Origin
China
Product Desciption
steel round bar AISI4140 42CrMo 1.7225 Alloy steel bar
AISI4140 ALLOY STEEL BAR
1.GENERAL CHARACTERISTICS OF 4140 ALLOY STEEL
AISI or SAE 4130 grade is a low-alloy steel containing chromium and molybdenum as strengthening agents. Its chemical composition is as follows
AISI/SAE 4140 grade is a versatile alloy with good atmospheric corrosion resistance and reasonable strength. It shows good overall combinations of strength, toughness, wear resistance and fatigue strength.
2.APPLICATIONS of 4140 alloy steel bar
This alloy finds many applications as forgings for the aerospace and oil and gas industries, along with myriad uses in the automotive, agricultural and defense industries, Typical uses are forged gears and shafts, spindles, fixtures, jigs and collars.
3.Chemical composition of 4140 steel bar
4.Supplied size of alloy steel bar:16-310mm with hot rolled supply condition
Ready stock:1000tons
5.Producition process of hot rolled alloy steel bar 4140 4130
6.4140 1430 4150 Alloy steel bar Supply condition
Surface Treatment: Peeling, Turning, Grinding, Milling, Drilling, Boring
Heat Treatment: Normalizing, Annealing, Quenching+ Tempering
7.HEAT TREATMENT
Heat treatment is carried out after hot working to render the steel suitable for machining, and to meet the mechanical property ranges specified for the steel's particular applications.
8.ANNEALING
Forgings of 4140 grade may be annealed by transferring the parts straight from the forging operation to a furnace held at a suitable temperature, between 1450 and 1550 º F (790 and 840 º C), holding for a suitable time then furnace cooling, forming a structure suitable for machining. This kind of treatment is best used for parts with simple shapes. If some areas of a forging will finish much colder than others then a uniform structure will not be obtained, in which case a spheroidizing anneal at around 1380 º F (750 º C) may be used. It is safe to say that experience alone will decide the best type of annealing treatment to be used prior to machining.
9.NORMALIZING
This process is defined as heating a steel to a temperature above the ferrite to austenite transformation range and then cooling in air to a temperature well below this transformation range. This treatment may be carried out on forged products as a conditioning treatment prior to final heat treatment. Normalizing also serves to refine the structure of forgings that might have cooled non-uniformly from their forging operation. The nominal normalizing temperature for 4140 grade is 1600 º F (870 º C), but production experience may necessitate a temperature either 50 º F (10 º C) above or below this figure. In fact when forgings are normalized before, say, carburizing or hardening and tempering, the upper range of normalizing temperatures is used. When normalizing is the final heat treatment, the lower temperature range is used.
AISI4140 ALLOY STEEL BAR
1.GENERAL CHARACTERISTICS OF 4140 ALLOY STEEL
AISI or SAE 4130 grade is a low-alloy steel containing chromium and molybdenum as strengthening agents. Its chemical composition is as follows
AISI/SAE 4140 grade is a versatile alloy with good atmospheric corrosion resistance and reasonable strength. It shows good overall combinations of strength, toughness, wear resistance and fatigue strength.
2.APPLICATIONS of 4140 alloy steel bar
This alloy finds many applications as forgings for the aerospace and oil and gas industries, along with myriad uses in the automotive, agricultural and defense industries, Typical uses are forged gears and shafts, spindles, fixtures, jigs and collars.
3.Chemical composition of 4140 steel bar
| CHEMICAL ANALYSIS | |
| C% | Carbon 0.38 - 0.43 |
| Mn% | Manganese 0.75 - 1.00 max |
| P% | Phosphorus 0.035 max |
| S% | Sulfur 0.040 max |
| Si% | Silicon 0.20 - 0.35 |
| Cr% | Chromium 0.80 - 1.10 |
| Mo% | Molybdenum 0.15 - 0.25 |
Ready stock:1000tons
5.Producition process of hot rolled alloy steel bar 4140 4130
6.4140 1430 4150 Alloy steel bar Supply condition
Surface Treatment: Peeling, Turning, Grinding, Milling, Drilling, Boring
Heat Treatment: Normalizing, Annealing, Quenching+ Tempering
7.HEAT TREATMENT
Heat treatment is carried out after hot working to render the steel suitable for machining, and to meet the mechanical property ranges specified for the steel's particular applications.
8.ANNEALING
Forgings of 4140 grade may be annealed by transferring the parts straight from the forging operation to a furnace held at a suitable temperature, between 1450 and 1550 º F (790 and 840 º C), holding for a suitable time then furnace cooling, forming a structure suitable for machining. This kind of treatment is best used for parts with simple shapes. If some areas of a forging will finish much colder than others then a uniform structure will not be obtained, in which case a spheroidizing anneal at around 1380 º F (750 º C) may be used. It is safe to say that experience alone will decide the best type of annealing treatment to be used prior to machining.
9.NORMALIZING
This process is defined as heating a steel to a temperature above the ferrite to austenite transformation range and then cooling in air to a temperature well below this transformation range. This treatment may be carried out on forged products as a conditioning treatment prior to final heat treatment. Normalizing also serves to refine the structure of forgings that might have cooled non-uniformly from their forging operation. The nominal normalizing temperature for 4140 grade is 1600 º F (870 º C), but production experience may necessitate a temperature either 50 º F (10 º C) above or below this figure. In fact when forgings are normalized before, say, carburizing or hardening and tempering, the upper range of normalizing temperatures is used. When normalizing is the final heat treatment, the lower temperature range is used.
You Might Also Like
Aluminum Alloy Armored Power Cables
LHD Power Steering Gear for Mazda Bt-50 4WD Ford Ranger (UC2......
Caterpillar 308c 308e Crawler 8 Ton Mini Second Hand Japan C......
Food Handing Kitchen Use Disposable Plastic LDPE Gloves HDPE......
2 USB UV Oil Plastic Travel Charger
20t High Efficiency Movable Frame Gantry Crane for Your Best......
Front End Shovel Loader Agriculture Machinery Equipment with......
Polished Edge 6.38mm, 8.38mm, 12.38mm Laminated Glass
Fast Switch Speed Water Oil Pressure Switch
1j79 Soft Strip for Magnetic Head
180mm End Carriage Wheel for Heady Duty Overhead Crane 3ton