Red Cable Silane Crosslinked Polyethylene Insulation Material XLPE
China Red Cable Silane Crosslinked Polyethylene Insulation Material XLPE, Find details about China Cable Jacket Material, Chemical from Red Cable Silane Crosslinked Polyethylene Insulation Material XLPE
Basic Info.
Model NO.
YJG-10
Classification
Inorganic Insulation Material
Certification
ISO9001, CPR/Rosh
Color
Red
Brand
Jsxd
Original Tensile Strength
20 MPa
Original Breakage Elongation
500 %
Change Rate of Tensile Strength After AG
2 %
Change Rate of Elongation at Break After
-6.8 %
Relative Dielectric Constant
1.9
20degree Centigrade Volume Resistivity
2.0*10^14
Dielectric Strength
30 Mv/M
Trademark
JSXD
Transport Package
Aluminum Foil Bag Inside and Kraft Bag Outside
Specification
25 kg(23.75kg+1.25kg)
Origin
China
HS Code
3901909000
Model NO.
YJG-10
Classification
Inorganic Insulation Material
Certification
ISO9001, CPR/Rosh
Color
Red
Brand
Jsxd
Original Tensile Strength
20 MPa
Original Breakage Elongation
500 %
Change Rate of Tensile Strength After AG
2 %
Change Rate of Elongation at Break After
-6.8 %
Relative Dielectric Constant
1.9
20degree Centigrade Volume Resistivity
2.0*10^14
Dielectric Strength
30 Mv/M
Trademark
JSXD
Transport Package
Aluminum Foil Bag Inside and Kraft Bag Outside
Specification
25 kg(23.75kg+1.25kg)
Origin
China
HS Code
3901909000
Product Desciption
Red Cable Silane crosslinked polyethylene insulation material XLPE
Description:
Silane cross-linked polyethylene insulation material (XLPE) has high insulation resistance and voltage strength, excellent dielectric properties, copper oxidation resistance, environmental stress cracking and heat resistance, good physical and mechanical properties, such as tensile resistance, bending resistance, torsion resistance, etc. The material can completely replace PVC. When using the product, the cable production equipment shall have: 1. The maximum allowable operating temperature is 90ºC; 2.The maximum allowable short-circuit temperature is 250ºC; 3. The maximum emergency temperature allowed is 130ºC.
Processing:
Most single screw extruders that process thermoplastics can process this product. The screw compression ratio is generally 2.5-3, the aspect ratio is about 25, and the screw is the common type with equal distance and unequal depth. The processing reference temperature is 150ºC-180ºC-190ºC-200ºC-210ºC-220ºC. The cooling water temperature is recommended to adopt step-by-step cooling to reduce the internal stress of insulating material.
Packing:
Net weight 25kg: Inner aluminum foil/polyethylene composite film bag, outer kraft paper composite bag,divided into A, B bags.
Bag A :Material A with 23.75 kg
Bag B :Material B with 1.25 kg
Storage:
The product should be stored in a clean, dry and ventilated warehouse, and should not be damaged by sun, rain, water and other abnormal conditions. Storage temperature should not be lower than 0ºC. The storage period of the product shall not exceed 6 months from the date of production.
Silane cross-linked polyethylene insulation material (XLPE) has high insulation resistance and voltage strength, excellent dielectric properties, copper oxidation resistance, environmental stress cracking and heat resistance, good physical and mechanical properties, such as tensile resistance, bending resistance, torsion resistance, etc. The material can completely replace PVC. When using the product, the cable production equipment shall have: 1. The maximum allowable operating temperature is 90ºC; 2.The maximum allowable short-circuit temperature is 250ºC; 3. The maximum emergency temperature allowed is 130ºC.
Processing:
Most single screw extruders that process thermoplastics can process this product. The screw compression ratio is generally 2.5-3, the aspect ratio is about 25, and the screw is the common type with equal distance and unequal depth. The processing reference temperature is 150ºC-180ºC-190ºC-200ºC-210ºC-220ºC. The cooling water temperature is recommended to adopt step-by-step cooling to reduce the internal stress of insulating material.
Packing:
Net weight 25kg: Inner aluminum foil/polyethylene composite film bag, outer kraft paper composite bag,divided into A, B bags.
Bag A :Material A with 23.75 kg
Bag B :Material B with 1.25 kg
Storage:
The product should be stored in a clean, dry and ventilated warehouse, and should not be damaged by sun, rain, water and other abnormal conditions. Storage temperature should not be lower than 0ºC. The storage period of the product shall not exceed 6 months from the date of production.
You Might Also Like
Triac 0-10V Dali Dimmable Recessed LED Downlight/ COB LED Ce......
GMP Factory Supply Food Grade Phycocyanin Spirulina Extract
Table Tennis Racket with Rubber + Bag Ping Pong Bat
3mh Cool Giant Fat Inflatable Cat Cartoon for Advertising
Mslfp14 17*17 Wired Box Size X-ray Digital Flat Panel Detect......
Portable Glass Shape Edge Polishing Machine
A4 A3 Paper Wrapping Machine
Stainless Steel Angle Tube Strainer
Sinchold 9220/20/45 Forged Steel Welded Crane Rail Clips
Warehouse Tent Made by Superb Tent
Thyristor Rectified CO2 MIG Mag Arc Welding Machine