Turquoise Cable Silane Crosslinked Polyethylene Insulation Material XLPE

China Turquoise Cable Silane Crosslinked Polyethylene Insulation Material XLPE, Find details about China Cable Jacket Material, Chemical from Turquoise Cable Silane Crosslinked Polyethylene Insulation Material XLPE

Basic Info.

Model NO.

YJG-10

Classification

Inorganic Insulation Material

Certification

ISO9001, CPR/Rosh

Color

Turquoise

Brand

Jsxd

Original Tensile Strength

20 MPa

Original Breakage Elongation

500 %

Change Rate of Tensile Strength After AG

2 %

Change Rate of Elongation at Break After

-6.8 %

Relative Dielectric Constant

1.9

20degree Centigrade Volume Resistivity

2.0*10^14

Dielectric Strength

30 Mv/M

Trademark

JSXD

Transport Package

Aluminum Foil Bag Inside and Kraft Bag Outside

Specification

25 kg(23.75kg+1.25kg)

Origin

China

HS Code

3901909000

Model NO.

YJG-10

Classification

Inorganic Insulation Material

Certification

ISO9001, CPR/Rosh

Color

Turquoise

Brand

Jsxd

Original Tensile Strength

20 MPa

Original Breakage Elongation

500 %

Change Rate of Tensile Strength After AG

2 %

Change Rate of Elongation at Break After

-6.8 %

Relative Dielectric Constant

1.9

20degree Centigrade Volume Resistivity

2.0*10^14

Dielectric Strength

30 Mv/M

Trademark

JSXD

Transport Package

Aluminum Foil Bag Inside and Kraft Bag Outside

Specification

25 kg(23.75kg+1.25kg)

Origin

China

HS Code

3901909000

Product Desciption

Turquoise Cable Silane crosslinked polyethylene insulation material XLPE

Description:
Silane cross-linked polyethylene insulation material (XLPE) has high insulation resistance and voltage strength, excellent dielectric properties, copper oxidation resistance, environmental stress cracking and heat resistance, good physical and mechanical properties, such as tensile resistance, bending resistance, torsion resistance, etc. The material can completely replace PVC. When using the product, the cable production equipment shall have: 1. The maximum allowable operating temperature is 90ºC; 2.The maximum allowable short-circuit temperature is 250ºC; 3. The maximum emergency temperature allowed is 130ºC.

Processing:
Most single screw extruders that process thermoplastics can process this product. The screw compression ratio is generally 2.5-3, the aspect ratio is about 25, and the screw is the common type with equal distance and unequal depth. The processing reference temperature is 150ºC-180ºC-190ºC-200ºC-210ºC-220ºC. The cooling water temperature is recommended to adopt step-by-step cooling to reduce the internal stress of insulating material.

Packing:
Net weight 25kg: Inner aluminum foil/polyethylene composite film bag, outer kraft paper composite bag,divided into A, B bags.
Bag A :Material A with 23.75 kg
Bag B :Material B with 1.25 kg

Storage:
The product should be stored in a clean, dry and ventilated warehouse, and should not be damaged by sun, rain, water and other abnormal conditions. Storage temperature should not be lower than 0ºC. The storage period of the product shall not exceed 6 months from the date of production.

Turquoise Cable Silane Crosslinked Polyethylene Insulation Material XLPE