1j80 High Permeability Soft Magnetic Alloy Permalloy 80 Wire

China 1j80 High Permeability Soft Magnetic Alloy Permalloy 80 Wire, Find details about China Permalloy 80, Permalloy Wire from 1j80 High Permeability Soft Magnetic Alloy Permalloy 80 Wire

Model NO.
permalloy 80
Resisivity
0.62
Density
8.5 Cm3
Curie Point
330 C
Name
Ni80cr3
Hardness
130~240 Hv
Tensile Strength
560~930 MPa
Yield Strength
150~885 MPa
Elongation
4~40 %
Use
High Frequency Inductive Components
Trademark
HUONA
Transport Package
Wooden Case
Specification
0.1~10mm
Origin
Shanghai
HS Code
750522000
Model NO.
permalloy 80
Resisivity
0.62
Density
8.5 Cm3
Curie Point
330 C
Name
Ni80cr3
Hardness
130~240 Hv
Tensile Strength
560~930 MPa
Yield Strength
150~885 MPa
Elongation
4~40 %
Use
High Frequency Inductive Components
Trademark
HUONA
Transport Package
Wooden Case
Specification
0.1~10mm
Origin
Shanghai
HS Code
750522000
1j80 High Permeability Soft Magnetic Alloy Permalloy 80 Wire
Soft magnetic alloys 1J80 / FeNi 80 / Ni80Cr3Si:

Mainly used  in two areas for energy conversion and information processing

In the power industry, mainly in the high magnetic field has a high magnetic induction and low core loss of the alloy. In the electronics industry, mainly at low or medium alloy having a high magnetic permeability and low coercive force. At high frequencies shall be made on a thin strip or alloy higher resistivity. Usually with sheet or strip.

Soft magnetic materials in exchange for use, due to the alternating magnetic eddy currents are induced inside the material, resulting in the loss, the smaller the resistance of the alloy, the greater the thickness, the higher the frequency of the alternating magnetic field, eddy current losses greater, magnetic reduce more. For this, the material must be made thinner sheet (tape), and the surface coated with an insulating layer, or the use of certain methods to the surface to form an oxide insulating layer, such alloys commonly used magnesium oxide electrophoresis coating.

Iron-nickel alloy mostly in the alternating magnetic field use, mainly for yoke iron, relay, Small Power Transformers and Magnetically shielded.
 
compositionCPSMnSi
≤
Content(%)0.030.020.020.60~1.101.10~1.50
 
compositionNiCrMoCuFe
Content(%)79.0~81.52.60~3.00-≤0.2Bal


If you have any questions about our product 1J80, Tankii glad to answer all at any time!

Have a good day!
1j80 High Permeability Soft Magnetic Alloy Permalloy 80 Wire1j80 High Permeability Soft Magnetic Alloy Permalloy 80 Wire1j80 High Permeability Soft Magnetic Alloy Permalloy 80 Wire1j80 High Permeability Soft Magnetic Alloy Permalloy 80 Wire
 

You Might Also Like