Cu Ni Wire/strip (CuNi1/CuNi2/CuNi5/ CuNi6 /CuNi8/CuNi10/CuNi14/CuNi19, CuNi23, CuNi34, CuNi40/CuNi44/CuNi45

China Cu Ni Wire/strip (CuNi1/CuNi2/CuNi5/CuNi6/CuNi8/CuNi10/CuNi14/CuNi19, CuNi23, CuNi34, CuNi40/CuNi44/CuNi45, Find details about China CuNi14, Copper Nickel Alloy Wire from Cu Ni Wire/strip (CuNi1/CuNi2/CuNi5/CuNi6/CuNi8/CuNi10/CuNi14/CuNi19, CuNi23, CuNi34, CuNi40/CuNi44/CuNi45

Basic Info.

Model NO.

Cu Ni

Serves

Small Order Accepted

Sample

Sample Available

Size

0.01-3mm*0.3-600mm

Density

8.9g/cm3

Elongation

25%

Diameter

0.01-10mm

OEM

YES

standard

GB/ASTM/JIS/BIS/DIN

surface

Bright

State

Soft 1/4hard 1/2hard hard T-hard

Trademark

TANKII

Transport Package

Packing in Coil Cartons, Pallet, Spools, Coils

Specification

0.001mm~3mm*5mm~250mm

Origin

China

HS Code

74082200

Model NO.

Cu Ni

Serves

Small Order Accepted

Sample

Sample Available

Size

0.01-3mm*0.3-600mm

Density

8.9g/cm3

Elongation

25%

Diameter

0.01-10mm

OEM

YES

standard

GB/ASTM/JIS/BIS/DIN

surface

Bright

State

Soft 1/4hard 1/2hard hard T-hard

Trademark

TANKII

Transport Package

Packing in Coil Cartons, Pallet, Spools, Coils

Specification

0.001mm~3mm*5mm~250mm

Origin

China

HS Code

74082200

Product Desciption

Cu Ni Wire/strip (CuNi1/CuNi2/CuNi5/CuNi6/CuNi8/CuNi10/CuNi14/CuNi19, CuNi23, CuNi34)

General Description
Due to has high tensile strength and increased resistivity values, TANKII copper nickel alloy wires are the first choice for applications as resistance wires. With the different nickel amount in this product range, the characteristics of the wire can be chosen according to your requirements. Copper nickel alloy wires are available as bare wire, or enamelled wire with any insulation and self-bonding enamel. Furthermore, litz wire made of enamelled copper nickel alloy wire are available.

Characteristic	Resistivity ( 200C μΩ.m)	Max.working Temperature ( 0C)	Tensile Strength (Mpa)	Melting point (0C)	Density ( g/cm3)	TCR x10-6/ 0C (20~600 0C)	EMF vs Cu (μV/ 0C) (0~100 0C)
Alloy Nomenclature
NC020(CuNi14)	0.2	300	≥310	1115	8.9	<30	-28

Copper Nickel Resistance Alloy-CuNi10
Chemical Content, %

Ni	Mn	Fe	Si	Cu	Other	ROHS Directive
						Cd	Pb	Hg	Cr
10	0.3	-	-	Bal	-	ND	ND	ND	ND

Mechanical Properties

Max Continuous Service Temp	250ºC
Resisivity at 20ºC	0.15±5%ohm mm2/m
Density	8.9 g/cm3
Thermal Conductivity	50 (Max)
Melting Point	1100ºC
Tensile Strength,N/mm2 Annealed,Soft	210~370 Mpa
Tensile Strength,N/mm2 Cold Rolled	420~740 Mpa
Elongation(anneal)	25%(Min)
Elongation(cold rolled)	2% (Min)
EMF vs Cu, μV/ºC (0~100ºC)	-25
Micrographic Structure	austenite
Magnetic Property	Non