China Elastic Putty, Elastic Paint, The External Wall Insulation System, etc, Find details about China Elatic Coating Emulsion, Acrylic Emulsion from Elastic Putty, Elastic Paint, The External Wall Insulation System, etc
Silicone modified acrylate emulsion----HN-314T | ||
HN-314T | Appearance | Light blue liquid |
Solid content | 48±1wt% | |
Viscosity.Cps(25ºC) | 1000-3000 | |
Particle Size(nm) | 100-500 | |
PH | 7.0-8.0 | |
Glass Transition Temperature (Tg) | -15ºC | |
Minimum Film Formation Temperature(MFT) | 0ºC | |
Ca2+ stability 5%CaCl2:Emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass |
HN-101 | Appearance | Light blue liquid |
Solid content | 47±2wt% | |
Viscosity.Cps(25ºC) | 1000-4000cps | |
Particle Size(nm) | 90-150 | |
PH | ||
Glass Transition Temperature (Tg) | 26ºC | |
Minimum Film Formation Temperature(MFT) | 22-24ºC | |
Ca2+ stability 5%CaCl2:Emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass | |
HN-102 | Appearance | Light blue liquid |
Solid content | 48±1wt% | |
Viscosity.Cps(25ºC) | 500-3000 | |
Particle Size(nm) | 100-180 | |
PH | 7.0-8.0 | |
Glass Transition Temperature (Tg) | 24ºC | |
Minimum Film Formation Temperature(MFT) | 21-23ºC | |
Ca2+ stability 5%CaCl2:Emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass | |
HN-996 | Appearance | Light blue liquid |
Solid content | 49±1wt% | |
Viscosity.Cps(25ºC) | 500-3000 | |
Particle Size(nm) | 90-150 | |
PH | 7.0-8.0 | |
Glass Transition Temperature (Tg) | 22ºC | |
Minimum Film Formation Temperature(MFT) | 18-20ºC | |
Ca2+ stability 5%CaCl2:Emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass | |
HN-4208A | Appearance | Translucency and light blue liquid |
Solid content | 46±2wt% | |
Viscosity.Cps(25ºC) | 3000-6000 | |
Particle Size(nm) | 60-100 | |
PH | 7.0-8.0 | |
Glass Transition Temperature (Tg) | 23ºC | |
Minimum Film Formation Temperature(MFT) | 22ºC | |
HN-4208 | Appearance | Translucency and light blue liquid |
Solid content | 42±1wt% | |
Viscosity.Cps(25ºC) | 1000-3000 | |
Particle Size(nm) | 90-120 | |
PH | 7.0-8.0 | |
Minimum Film Formation Temperature(MFT) | 7-10ºC | |
HN-01F | Appearance | Light blue liquid |
Solid content | 29±1wt% | |
Viscosity.Cps(25ºC) | ≤500cps | |
Particle Size(nm) | 80-120 | |
PH | 7.5-8.5 | |
Minimum Film Formation Temperature(MFT) | 10ºC | |
HN-314T | Appearance | Light blue liquid |
Solid content | 48±1wt% | |
Viscosity.Cps(25ºC) | 1000-3000 | |
Particle Size(nm) | 100-500 | |
PH | 7.0-8.0 | |
Glass Transition Temperature (Tg) | -15ºC | |
Minimum Film Formation Temperature(MFT) | 0ºC | |
Ca2+ stability 5%CaCl2:Emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass | |
HN-519NT | Appearance | Light blue liquid |
Solid content | 48±1wt% | |
Viscosity.Cps(25ºC) | 100-1000 | |
Particle Size(nm) | 90-160 | |
PH | 7.0-8.0 | |
Glass Transition Temperature (Tg) | -40ºC | |
Minimum Film Formation Temperature(MFT) | 0ºC | |
Ca2+ stability 5%CaCl2:Emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass | |
HN-340T | Appearance | Milk white liquid |
Solid content | 56±1wt% | |
Viscosity.Cps(25ºC) | 1000-3000 | |
Particle Size(nm) | 300-400 | |
PH | 7.0-8.0 | |
Minimum Film Formation Temperature(MFT) | 0ºC | |
Ca2+ stability 5%CaCl2:Emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass | |
HN-332T | Appearance | Milky white with a hint of green |
Solid content | 56±1wt% | |
Viscosity.Cps(25ºC) | 1000-3000 | |
Particle Size(nm) | 200-300 | |
PH | 7.0-8.0 | |
Minimum Film Formation Temperature(MFT) | 0ºC | |
Ca2+ stability 5%CaCl2:Emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass |