Product Desciption
POLYMERIC MDI 44V20L/PM200 /MR 200/ 5005S
Application
44V20L is a diisocyanate-diphenylmethane(MDI)-based composition containing some higher functionality isocyanates. The functionality is about 2.6-2.7. It is abrown liquid at ambient temperatures.
44V20L can be widely used in the production of rigid PU foam heat-insulating materials; also used in isocyanurate foam, paints, adhesives, structural foam,cellular integral skin foam, automotive bumper and interior parts, high-resilience foam and synthetic wood, etc. Due to its unique composition structure, 44V20L can provide better flowability. It is, therefore, particularly suitable for the production which require strict flowability of systems...
Typical Physical and Chemical Properties
Package(s)
210L iron drums, 250kg/drum
Storage
Since 44V20L is a reactive chemical, reaction with atmospheric moisture happens easily and leads to the formation of insoluble ureas and carbon dioxide gas, which can result in pressure build-up in closed containers and viscosity increase of the product.Containers must therefore be absolutely dry and carefully sealed after congested with nitrogen.
Containers of 44V20L should be kept properly closed and stored indoors at ambient temperature (15-35ºC) in a well-ventilated area. Storage at low temperature (below5ºC) may lead to some crystallization; this material must, therefore, be protected from frost.If crystallization does occur, the material should be heated by rolling the drum in a hot air oven at 70-80ºC to melt it out, and should then be thoroughly agitated before use. Melting in a water bath is not recommended.
Extended storage at temperatures above 50ºC is not recommended to prevent from the formation of insoluble solids and viscosity increase.
Shelf Life
Under recommended storage conditions, the shelf life of 44V20L is one year since the date of production.
The above information is for reference only. The specific value still provided by the manufacturer. Our company is not responsible for any legal liability.
Application44V20L is a diisocyanate-diphenylmethane(MDI)-based composition containing some higher functionality isocyanates. The functionality is about 2.6-2.7. It is abrown liquid at ambient temperatures.
44V20L can be widely used in the production of rigid PU foam heat-insulating materials; also used in isocyanurate foam, paints, adhesives, structural foam,cellular integral skin foam, automotive bumper and interior parts, high-resilience foam and synthetic wood, etc. Due to its unique composition structure, 44V20L can provide better flowability. It is, therefore, particularly suitable for the production which require strict flowability of systems...
Typical Physical and Chemical Properties
| Test Item(s) | Specification(s) |
| Appearance | Brown Liquid |
| Viscosity at 25ºC, mPa.S | 150-250 |
| NCO, % | 30.5-32.0 |
| Density 25ºC, g/cm3 | 1.220-1.250 |
| Acidity (HCl), % | ≤0.05 |
| Hydrolysable Chlorinea, % | ≤0.2 |
Package(s)
210L iron drums, 250kg/drum
Storage
Since 44V20L is a reactive chemical, reaction with atmospheric moisture happens easily and leads to the formation of insoluble ureas and carbon dioxide gas, which can result in pressure build-up in closed containers and viscosity increase of the product.Containers must therefore be absolutely dry and carefully sealed after congested with nitrogen.
Containers of 44V20L should be kept properly closed and stored indoors at ambient temperature (15-35ºC) in a well-ventilated area. Storage at low temperature (below5ºC) may lead to some crystallization; this material must, therefore, be protected from frost.If crystallization does occur, the material should be heated by rolling the drum in a hot air oven at 70-80ºC to melt it out, and should then be thoroughly agitated before use. Melting in a water bath is not recommended.
Extended storage at temperatures above 50ºC is not recommended to prevent from the formation of insoluble solids and viscosity increase.
Shelf Life
Under recommended storage conditions, the shelf life of 44V20L is one year since the date of production.
The above information is for reference only. The specific value still provided by the manufacturer. Our company is not responsible for any legal liability.
You Might Also Like
Triac 0-10V Dali Dimmable Recessed LED Downlight/ COB LED Ce......
GMP Factory Supply Food Grade Phycocyanin Spirulina Extract
Table Tennis Racket with Rubber + Bag Ping Pong Bat
3mh Cool Giant Fat Inflatable Cat Cartoon for Advertising
Mslfp14 17*17 Wired Box Size X-ray Digital Flat Panel Detect......
Portable Glass Shape Edge Polishing Machine
A4 A3 Paper Wrapping Machine
Stainless Steel Angle Tube Strainer
Sinchold 9220/20/45 Forged Steel Welded Crane Rail Clips
Warehouse Tent Made by Superb Tent
Thyristor Rectified CO2 MIG Mag Arc Welding Machine