Paper Coating Chemical, Zirconia Beads Chemical Used in Paper Coating Machine

China Paper Coating Chemical, Zirconia Beads Chemical Used in Paper Coating Machine, Find details about China Chemical, Powder Chemical from Paper Coating Chemical, Zirconia Beads Chemical Used in Paper Coating Machine

Basic Info.

Model NO.

JRX

Usage Stage

Manufacturing Stage

Trademark

JRX

Origin

China

Model NO.

JRX

Usage Stage

Manufacturing Stage

Trademark

JRX

Origin

China

Product Desciption

Ceramics Manufacturer Zircon Oxide Beads as Grinding Media (size: 0.4mm~30mm)
beads have high fracture toughness and nice impact resistant that causes no break under high speed impact

The beads have 30-50 times higher wear-resistance as glass beads, 5times higher as Zirconium Silicate beads and 6-8 times higher as Al2O3 beads

Because of the high density and excellent grinding efficiency of our TZP beads , they greatly apply to grinding and dispersing high viscosity materials

Popular size :Ø0.1,Ø0.2,Ø0.4~0.8,Ø0.8~1.0,Ø1.0~Ø1.2,Ø1.2~Ø1.4,Ø0.4~Ø1.6,Ø1.6~Ø1.8,Ø1.8~Ø2,Ø2~Ø2.5

Other Alumina ceramic grinding ball introduction :

This product are featured by high density and hardness, low wear lost, corrosion-resistance etc. They are the perfect high-efficient grinding media for milling glaze/frit, pigment, ceramic materials, and various mine ore powder, they are using ceramics, cements, paints, refractories, inorganic mineral powders etc...

Applied for dry grinding , wet grinding ,mineral grinding , quartz grinding , lineston grinding , iron ore grinding , cement grinding , ceramics plants grinding , pigment grinding , mineral ore grinding , breaking platns .

Applied for ball mill,grinding machine , pot mill , librating mill , pebble mill , Attrition Mill,rod mill , grinding mill , grinding machine , ball grinding mill

Size:1mm, 3mm, 6mm, 9mm, 13mm, 16mm, 20mm, 25mm, 30mm , 40mm, 50mm, 60mm, 70mm,95mm

Other grinding ball like alumina grinding ball itroduced :

1: 92% 95% 68% Alumina content series

A) Al2O3 ≥ 92%
B) Water absorption <0.01%
C) Bulk density ≥ 3.63 g/cm3
D) Mosh hardness: 9
E) Color: White

2: 95% High-alumina grinding ball

A) Al2O3 ≥ 95% Sio2<3.8%, others:~3%
B) Water absorption <0.01%
C) Bulk density ≥ 3.7 g/cm3
D) Mosh hardness: 9
E) Color: White
F) self abrasion loss : <0.008%

3: 68% Medium alumina grinding ball series :

A) Al2O3 : 65%~75%
B) Bulk density ≥ 2.93g/cm3
C) Mosh hardness: 8 grade
D) self abrasion loss :0.01
E) Color : white or brown

Item	Al2O3	SiO2	Others
92% ball	92%	<6.5%	~2 %
95% ball	95%	<3.6~3.7 %	~2%
68% ball	68%	<21.2%	~10.18%

B.Physical Analysis

Item	Alumina Content	Mohs hardness	Abrasion loss (24hours)	Density (g/cm3)	Water absorption
92% ball	92%	9	<0.01%	3.6	<0.01%
95% ball	95%	9	<0.01%	3.74	<0.01%
68% ball	68%	7-8	<0.03%	3	<0.02%
Producing way ::cool-isostatic pressing , or by rolling