BLEND POLYOL SDB10D
RIGID PU FOAM FOR PIPE INJECTION INSULATION
DESCRIPTION
SDB10D is a kind of blend polyol used for pipe insulation system for city heating or cooling.
When it combined with isocyanate(PM200) leads to the formation of rigid polyurethane foam by
using PU injection foam equipment .The foam formed has the characteristics as following:
n The thermal conductivity is low, which can meets the requirements of city heating and
energy saving.
n Service life of the foam is very long, over 30 years.
n High temperature resistance and good dimensional stability of the foam, the highest
temperature range is 140 ºC.
TYPICAL PHYSICAL PROPERTIES
Physical Properities Test Method Metric Value
Core Density GB/T 6343-2009 kg/m3 ≥60
 
 Radial Compressive
Strength		 GB/T 8813-2008 MPa ≥0.3 
 Initial Thermal
Conductivity(50°C)		 GB/T 10294-2008 W/(m·K) ≤0.033
        
Close Cell Content GB/T 10799-2008 % ≥88
Water Absorption GB/T 8810-2005 % ≤10
Air bubbles GB/T 29047 mm 1/3Insulation thickness.
Average cell size. GB/T 29047 mm ≤0.5
Importance: The above mentioned are typical test values, and the specific data may vary slightly
due to environmental conditions.For our products, the data are not legally binding.
Other unmentioned matters and TDS&MSDS.Please visit our official website shundapu.en.made-in-china.com
Or please contact us for information:

 