Copolymer Polypropylene PP Resins

China Copolymer Polypropylene PP Resins, Find details about China Polypropylene, PP from Copolymer Polypropylene PP Resins

V30g
Mfr:14-19g/10min
Z30s
Mfr:26-30g/10min
Hy2040
Mfr:23-45g/10min
Hy-3500tml
Mfr:1.5-6g/10min
Hy-4808tml
Mfr:5-10g/10min
Hy-4912tml
Mfr:10-16g/10min
Hy-4818tml
Mfr:16-22g/10min
Hy-4930tml
Mfr:22-30g/10min
Hy-9018
Mfr:60-63G/10min
Mt25
Mfr:25g/10min
Mt35
Mfr:35g/10min
Mt55
Mfr:45g/10min
Trademark
HY brand
Transport Package
25kg/1000kg Per Woven Bag
Specification
25Kg
Origin
Shandong China
HS Code
3902100090
V30g
Mfr:14-19g/10min
Z30s
Mfr:26-30g/10min
Hy2040
Mfr:23-45g/10min
Hy-3500tml
Mfr:1.5-6g/10min
Hy-4808tml
Mfr:5-10g/10min
Hy-4912tml
Mfr:10-16g/10min
Hy-4818tml
Mfr:16-22g/10min
Hy-4930tml
Mfr:22-30g/10min
Hy-9018
Mfr:60-63G/10min
Mt25
Mfr:25g/10min
Mt35
Mfr:35g/10min
Mt55
Mfr:45g/10min
Trademark
HY brand
Transport Package
25kg/1000kg Per Woven Bag
Specification
25Kg
Origin
Shandong China
HS Code
3902100090


Orient hongye Polypropylene is a thermoplastic made by polymerization of polypropylene, a by-product of petroleum refining.Various techniques can alter the physical, chemical or mechanical properites of polypropylene.

Orient hongye Polypropylene fabricates with standard woodworking tooling.It can be butt welded, extrusion welded, fusion welded, and spun welded.It can be machined with ordinary wood or metalworking equipment.

Orient hongye Polypropylene offers a good balance of thermal, chemical and electrical properties with moderate strength.It is a good strength to weight ratio.Because it has such a hard, high gloss surface, Polypropylene is ideally suited to environments where there is concern for bacteria build up or build up that can interfere with flow.
Copolymer Polypropylene PP Resins
As a homopolymer, polypropylene uses temperatures in the range of 30° to 210°F depending on specific chemistry, copolymers in the range of -20° to 180°F.

Homopolymer Polypropylene

PP Homopolymer Powder
MFR range-------------------------------------------------------------0.5~100 g/10min (2.16kg)
Stacking Density-------------------------------------------------------------------0.4~0.5 g/m³
Ash Content----------------------------------------------------------------------≤100 mg/kg
Isotacticity------------------------------------------------------------------------------≥97%
Tensile Strength----------------------------------------------------------------------≥30 Mpa
Tensile Elongation at Break-----------------------------------------------------------------≥35%
Flexural Strength---------------------------------------------------------------------≥45 Mpa
Flexural Modulus-------------------------------------------------------------------≥1100 Mpa
IZOD Impact Strength at 23ºC----------------------------------------------------------≥2.5 kJ/m²

Applications:Modification, Injection and Wiredrawing

Detailed Usage including:Monofilament, (Lacerate) Film, Packing Bag, Backing of Carpet, Thread, Rope, Packing Belt, Silk Spinning for Woven Bag, Cast Film or Tube Film, Lamination, The Inner Drum and Base of Washing Machine, Household and Packing or Industry Fiber etc.
TypePP-H-012PP-H-045PP-H-075PP-H-140PP-H-225-PP-H-225+PP-H-300-PP-H-300+PP-H-425-PP-H-425+PP-H-550
MFR0.5-2.22-65-1110-1614-1917-2524-3028-3532-3542-55>55
Stacking density0.4-0.50.4-0.50.4-0.50.4-0.50.4-0.50.4-0.50.4-0.50.4-0.50.4-0.50.4-0.50.4-0.5
Ash content100100100100100100100100100100100
Isotacticity9795979597979797979797
Tensile strength3036303530303030303030
Elongation at break3535353535353535353535
Flexural strength4545454545454545454545
Flexural Modulus13001300130013001100110011001100110011001100
IZOD Impact Strength2.52.52.52.52.52.52.52.52.52.52.5

Homopolymer polypropylene is a light density thermoplastic (.91-92gm/cm³).It can be stabilized to enhance prolonged use at
elevated temperature, prolonged life in exposure to ultra-violet light and improved flame retardancy.
 
Copolymer Polypropylene PP Resins
Copolymer Polypropylene PP Resins
Copolymer Polypropylene PP Resins


Homopolymer Polypropylene granules

T30S

Property:
MFR (2.16kg)---------------------------------------------------------------------3~5 g/10min
Isotacticity-----------------------------------------------------------------------------≥95%
Tensile Strenght--------------------------------------------------------------------->30 Mpa
Ash Content---------------------------------------------------------------------------≤0.03%
Yellow Index-----------------------------------------------------------------------------≤4

Description:A polymer used for general purpose with perfect property in Anti-impact, exhibits excellent processing performance in long-term usage.

Applications:The spinning of woven bag wire, Production of cast film and tube film, Package Material, Carpet, Artificial grass, Rope or mono-silk for packing etc.
 
V30G

Property:
MFR (2.16kg )-------------------------------------------------------------------14~19g/10min
Isotacticity-----------------------------------------------------------------------------≥95%
Tensile Strenght--------------------------------------------------------------------->30 Mpa
Ash Content---------------------------------------------------------------------------≤0.03%
Notched IZOD Impact Strength at 23ºC----------------------------------------------------≥2 kJ/m²
Flexural Modulus------------------------------------------------------------------>1000 Mpa
Yellow Index-----------------------------------------------------------------------------≤4

Description:High strength, High thermal resistance, Good resistance to flexure, High tensile strength, High inflexibility, High wearability, Good environmental stress crack resistance, Low creep behavior.

Applications:Plastic toys, Containers for packing and Housewares.
 
Z30S

Property:
MFR (2.16kg)-------------------------------------------------------------------26~30 g/10min
Isotacticity-----------------------------------------------------------------------------≥95%
Tensile Strength--------------------------------------------------------------------->30 Mpa
Ash Content---------------------------------------------------------------------------≤0.03%
Notched IZOD Impact Strength at 23ºC----------------------------------------------------≥2 kJ/m²
Flexural Modulus------------------------------------------------------------------>1000 Mpa
Yellow Index-----------------------------------------------------------------------------≤4

Description:Good fluidity, Narrow molecular weight distribution, Low ash content, Good tensile, High cleanness.

Applications:The fields of high textile rate and high elongation such as carpet or belt material, fibers of sport clothing and heavy clothing.
 Copolymer Polypropylene PP Resins
HY9018

Property:
MFR (2.16kg)------------------------------------------------------------------>65 g/10min
Isotacticity-----------------------------------------------------------------------------≥98%
Tensile Strenght--------------------------------------------------------------------->36 Mpa
Ash Content---------------------------------------------------------------------------≤0.03%
Notched IZOD Impact Strength at 23ºC---------------------------------------------------≥1.5 kJ/m²
Flexural Modulus------------------------------------------------------------------>1300 Mpa
Yellow Index-----------------------------------------------------------------------------≤4

Description:High flowing rate, High rigidity, Good thermal resistance, Good fineness in surface, Easy forming reapidly.

Applications:DVD packing box, Disposable snack food box, Thin wall product.

Polypropylene can be use in direct contact with food.

Random Copolymers

HY-N4200F
Change in the way the material is polymerized can show dramatic improvements in certain mechanical properties, example, random copolymers block copolymers.
Copolymerization of an additional resin group can enhance physical properties.Addition of fillers can improve mechanical or thermal stability.
Property:
Exterior------------------------------------------------------------------------White Powder
MFR-----------------------------------------------------------------0.26~0.3 g/10min, 2.16kg
Ash Content---------------------------------------------------------------------------≤0.03%
Tensile Strength--------------------------------------------------------------------->23 Mpa
Tensile Elongation at Break---------------------------------------------------------------≥400%
Notched IZOD Impact Strength at 23ºC---------------------------------------------------≥17 kJ/m²
Flexural Modulus------------------------------------------------------------------->650 Mpa
Melting Point--------------------------------------------------------------------------<146ºC

Description:PP Random Copolymer Excellent mechanical property and thermal property, Good processability, High impact resistance, And Stable performance in long-term processing.

Applications:Applied as the engineering plastic for rope, board, sheet, store tank etc, And also can be used as the shell material of electrical equipment, Insulating material, Or the modification of plastic for improving the tenacity.
 
HY-N4600F

Property:
Exterior------------------------------------------------------------------------White Powder
MFR------------------------------------------------------------------0.3~0.5 g/10min, 2.16kg
Ash Content---------------------------------------------------------------------------≤0.03%
Tensile Strength--------------------------------------------------------------------->23 Mpa
Tensile Elongation at Break---------------------------------------------------------------≥400%
Notched IZOD Impact Strength at 23ºC---------------------------------------------------≥17 kJ/m²
Flexural Modulus------------------------------------------------------------------->650 Mpa
Melting Point--------------------------------------------------------------------------<146ºC

Description:PP Random Copolymer, Excellent mechanical property and thermal property, Good processability, High impact resistance, And Stable performance in long-term processing.

Applications:Applied as the engineering plastic for rope, board, sheet, store tank etc, And also can be used as the shell material of electrical equipment, Insulating material, Or the modification of plastic for improving the tenacity.
Resistance to chemicals and solvents is very good.It has good resistance to aqueous salts, acids or alkaline.It also has very low pereability to water vapor and gases.Because of its excellent resistance to solvents, it finds extensive use in the semi-conductor industry.It performs well in the presence of DI water.Care must be taken in the presence of active oxidizing agents, especially with fabricated parts.Mumerous chemical resistance charts are based solely on press molded plaques and don't take fabricated parts into consideration.The resins are attacked however, by halogens, and other active oxidizing agents, and by aromatic and chlorinated hydrocarbons at high temperatures.

HY-N4200L

Property:
Exterior----------------------------------------------------------------------Natural Granule
MFR-----------------------------------------------------------------0.25~0.28 g/10min, 2.16kg
Tensile Strength---------------------------------------------------------------------≥23 Mpa
Tensile Elongation at Break---------------------------------------------------------------≥400%
Notched IZOD Impact Strength at 23ºC---------------------------------------------------≥50 kJ/m²
Flexural Modulus--------------------------------------------------------------------≥750 Mpa
Melting Point--------------------------------------------------------------------------<146ºC
Oxidation Induction Time (at 210ºC)-------------------------------------------------------≥30min

Description:PP Random Copolymer, Excellent mechanical property and thermal property, Good processability, High impact resistance, And Stable performance in long-term processing.

Applications:Applied as the engineering plastic for rope, board, sheet, store tank etc, And also can be used as the shell material of electrical equipment, Insulating material, Or the modification of plastic for improving the tenacity.
 
Copolymer Polypropylene PP Resins
Copolymer Polypropylene PP Resins
Copolymer Polypropylene PP Resins


HY-N4600L

Property:
Exterior----------------------------------------------------------------------Natural Granule
MFR------------------------------------------------------------------0.3~0.5 g/10min, 2.16kg
Tensile Strength---------------------------------------------------------------------≥23 Mpa
Tensile Elongation at Break---------------------------------------------------------------≥400%
Notched IZOD Impact Strength at 23ºC----------------------------------------------------≥50kJ/m²
Flexural Modulus--------------------------------------------------------------------≥750 Mpa
Melting Point--------------------------------------------------------------------------<146ºC
Oxidation Induction Time (at 210ºC)-------------------------------------------------------≥30min

Description:PP Random Copolymer, Excellent mechanical property and thermal property, Good processability, High impact resistance, And Stable performance in long-term processing.

Applications:Applied as the engineering plastic for rope, board, sheet, store tank etc, And also can be used as the shell material of electrical equipment, Insulating material, Or the modification of plastic for improving the tenacity.
It can be processed via extrusion, injection molding, blow molding, compression molding, and rotational molding.It is extremely stable and relatively easy to process.
It is available in various forms such as, but not llimited to, films, sheets, blocks, pipes, hollow tubes, round rods, square rods, profiles, fittings and valves.
Nonstandard shapes are possible through pressure, thermo or vacuum forming.
Great care shoudl be used in designing with polypropylene, taking into consideration its coefficient of thermal expansion, modulus of elasticity, and its compressive strength. 
Copolymer Polypropylene PP Resins
HY-3500TML

Property:
Exterior-------------------------------------------------------------------Transparent Granule
MFR--------------------------------------------------------------------1.5~6 g/10min, 2.16kg
Tensile Strength---------------------------------------------------------------------≥29 Mpa
Notched Charpy Impact Strength at 23ºC---------------------------------------------------≥8 kJ/m²
Flexural Modulus--------------------------------------------------------------------≥900 Mpa
Melting Point--------------------------------------------------------------------------<140ºC
Haze Ratio-----------------------------------------------------------------------------<18%
Yellow Index-----------------------------------------------------------------------------≤4

Description:PP random copolymer of high transparency, Perfect transparency and fineness, Good sensory taste, Excellent balance of tenacity and rigidity, High crystallization temperature.

Applications:Widely used for the thermoforming products by technology of 1 or 2 steps method, including high transparent pallet, cups for milk tea or other food containers, furniture product and thin package material, medicine bottle or transparent cup lid by injection, blowing and extrusion method, sheets, stationery product, high transparency and gloss woven bag, and the modification of other polypropylene by blending.
Copolymer Polypropylene PP Resins
HY-4808TML

Property:
Exterior-------------------------------------------------------------------Transparent Granule
MFR--------------------------------------------------------------------5~12 g/10min, 2.16kg
Tensile Strength---------------------------------------------------------------------≥29 Mpa
Notched Charpy Impact Strength at 23ºC---------------------------------------------------≥5 kJ/m²
Flexural Modulus--------------------------------------------------------------------≥900 Mpa
Melting Point--------------------------------------------------------------------------<140ºC
Haze Ratio-----------------------------------------------------------------------------<20%
Yellow Index-----------------------------------------------------------------------------≤4

Description:High transparency random copolymer, low haze ratio.

Applications:Applied to the product of high transparency, The daily transparent necessaries, Medical syringe, Storage box, Transparent lid, sheet and containers.
Copolymer Polypropylene PP Resins
HY-4818TML

Property:
Exterior-------------------------------------------------------------------Transparent Granule
MFR-------------------------------------------------------------------12~20 g/10min, 2.16kg
Tensile Strength----------------------------------------------------------------------≥27Mpa
Notched Charpy Impact Strength at 23ºC---------------------------------------------------≥5 kJ/m²
Flexural Modulus--------------------------------------------------------------------≥900 Mpa
Melting Point--------------------------------------------------------------------------<140ºC
Haze Ratio-----------------------------------------------------------------------------<20%
Yellow Index-----------------------------------------------------------------------------≤4

Description:Random copolymer of high transparency, High resistance to impact, High flowing performance, High speed in forming, Odor free, High gloss, Low haze ratio.

Applications:Suitable to the product requiring a high transparency such as storage container, Disposable syringe, Sports cup, Feeding bottle, Lunch-box, Crisper, Electronic accessories.
Copolymer Polypropylene PP Resins
Company Profile
As professional manufacturer of polyolefin, we, Shandong Orient Hongye Chemical Co., Ltd had been specialized in this industry for about 9 years from 2009 when it was registered with a capital of 164000000 CNY.We have 2 factories of polypropylene with granulation equipments of which the annual yield per line is about 180,000.00 metric tons.Besides, we have 2 polymerizing unit of polybutylene of the which the total output per year is 50,000 metric tons.Our products including PP homopolymer, PP random copolymer and polybutylene (PB-1), are all underwriting of CPIP.


Advantages
1.We are a company with LPG further processing unit from which some of stock can be acquired, that make our cost some low.
2.Located at the crucial node of the Blue Economy Zone of Shandong Peninsula, the High-end Industry Gathering Zone of Jaodong Peninsula and the High-efficiency Economy Zone of Huanghe Delta, we have the advantages of convenient transportation and conspicuous location policy.
3.We have our own patents of product design and processing.
4.The professional R/D advantages of our company from the cooperation with the major national experiment institute in rubber and plastic industry.
 