China Water Base Acrylic Resin for External Wall Colorful Sand Real Stone Lacquer, Find details about China Building Material, Spray Paint from Water Base Acrylic Resin for External Wall Colorful Sand Real Stone Lacquer
Silicone modified acrylate emulsion----HN-4208 | ||
HN-4208A | Appearance | Light blue liquid |
Solid content | 42±1wt% | |
Viscosity.Cps(25ºC) | 1000-3000 | |
Particle Size(nm) | 90-120 | |
PH | 7.0-8.0 | |
Minimum Film Formation Temperature(MFT) | 7-10ºC | |
Ca2+ stability 5%CaCl2:Emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass |
HN-101 | Appearance | Light blue liquid |
Solid content | 47±2wt% | |
Viscosity.Cps(25ºC) | 1000-4000cps | |
Particle Size(nm) | 90-150 | |
PH | ||
Glass Transition Temperature (Tg) | 26ºC | |
Minimum Film Formation Temperature(MFT) | 22-24ºC | |
Ca2+ stability 5%CaCl2:Emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass | |
HN-102 | Appearance | Light blue liquid |
Solid content | 48±1wt% | |
Viscosity.Cps(25ºC) | 500-3000 | |
Particle Size(nm) | 100-180 | |
PH | 7.0-8.0 | |
Glass Transition Temperature (Tg) | 24ºC | |
Minimum Film Formation Temperature(MFT) | 21-23ºC | |
Ca2+ stability 5%CaCl2:Emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass | |
HN-996 | Appearance | Light blue liquid |
Solid content | 49±1wt% | |
Viscosity.Cps(25ºC) | 500-3000 | |
Particle Size(nm) | 90-150 | |
PH | 7.0-8.0 | |
Glass Transition Temperature (Tg) | 22ºC | |
Minimum Film Formation Temperature(MFT) | 18-20ºC | |
Ca2+ stability 5%CaCl2:Emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass | |
HN-4208A | Appearance | Translucency and light blue liquid |
Solid content | 46±2wt% | |
Viscosity.Cps(25ºC) | 3000-6000 | |
Particle Size(nm) | 60-100 | |
PH | 7.0-8.0 | |
Glass Transition Temperature (Tg) | 23ºC | |
Minimum Film Formation Temperature(MFT) | 22ºC | |
HN-4208 | Appearance | Translucency and light blue liquid |
Solid content | 42±1wt% | |
Viscosity.Cps(25ºC) | 1000-3000 | |
Particle Size(nm) | 90-120 | |
PH | 7.0-8.0 | |
Minimum Film Formation Temperature(MFT) | 7-10ºC | |
HN-01F | Appearance | Light blue liquid |
Solid content | 29±1wt% | |
Viscosity.Cps(25ºC) | ≤500cps | |
Particle Size(nm) | 80-120 | |
PH | 7.5-8.5 | |
Minimum Film Formation Temperature(MFT) | 10ºC | |
HN-314T | Appearance | Light blue liquid |
Solid content | 48±1wt% | |
Viscosity.Cps(25ºC) | 1000-3000 | |
Particle Size(nm) | 100-500 | |
PH | 7.0-8.0 | |
Glass Transition Temperature (Tg) | -15ºC | |
Minimum Film Formation Temperature(MFT) | 0ºC | |
Ca2+ stability 5%CaCl2:Emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass | |
HN-519NT | Appearance | Light blue liquid |
Solid content | 48±1wt% | |
Viscosity.Cps(25ºC) | 100-1000 | |
Particle Size(nm) | 90-160 | |
PH | 7.0-8.0 | |
Glass Transition Temperature (Tg) | -40ºC | |
Minimum Film Formation Temperature(MFT) | 0ºC | |
Ca2+ stability 5%CaCl2:Emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass | |
HN-340T | Appearance | Milk white liquid |
Solid content | 56±1wt% | |
Viscosity.Cps(25ºC) | 1000-3000 | |
Particle Size(nm) | 300-400 | |
PH | 7.0-8.0 | |
Minimum Film Formation Temperature(MFT) | 0ºC | |
Ca2+ stability 5%CaCl2:Emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass | |
HN-332T | Appearance | Milky white with a hint of green |
Solid content | 56±1wt% | |
Viscosity.Cps(25ºC) | 1000-3000 | |
Particle Size(nm) | 200-300 | |
PH | 7.0-8.0 | |
Minimum Film Formation Temperature(MFT) | 0ºC | |
Ca2+ stability 5%CaCl2:Emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass |