Yellow Insulation Polymer Materials XLPE

China Yellow Insulation Polymer Materials XLPE, Find details about China XLPE, Cable Jacket Material from Yellow Insulation Polymer Materials XLPE

Basic Info.

Model NO.

XLPE-YJG(XD02)

Wire Core Material

None

Certification

ISO, CE, RoHS

Model

Yjg(Xd02)

Brand

Jsxd

Original Tensile Strength

20 MPa

Original Breakage Elongation

500 %

Change Rate of Tensile Strength After AG

5.0 %

Change Rate of Elongation at Break After

-6.0 %

Relative Dielectric Constant

1.9

20degree Centigrade Volume Resistivity

2.0*10^14

Dielectric Strength

30 Mv/M

Trademark

JSXD

Transport Package

Aluminum Foil Bag Inside and Kraft Bag Outside

Specification

25 kg(23.75kg+1.25kg)

Origin

China

HS Code

3901909000

Model NO.

XLPE-YJG(XD02)

Wire Core Material

None

Certification

ISO, CE, RoHS

Model

Yjg(Xd02)

Brand

Jsxd

Original Tensile Strength

20 MPa

Original Breakage Elongation

500 %

Change Rate of Tensile Strength After AG

5.0 %

Change Rate of Elongation at Break After

-6.0 %

Relative Dielectric Constant

1.9

20degree Centigrade Volume Resistivity

2.0*10^14

Dielectric Strength

30 Mv/M

Trademark

JSXD

Transport Package

Aluminum Foil Bag Inside and Kraft Bag Outside

Specification

25 kg(23.75kg+1.25kg)

Origin

China

HS Code

3901909000

Product Desciption

Yellow Insulation Polymer materials XLPE

Description:
Two processes silane crosslinked insulating material, mainly used for the insulation of low - and medium-voltage aerial cables produced through a extruded pipe die. The working voltage of wire and cable is 10KV and below, the highest working temperature is 90ºC; The default color of the product is black, and the color can also be customized according to customer requirements.

Processing:
Most single screw extruders that process thermoplastics can process this product. The screw compression ratio is generally 2.5-3, the aspect ratio is about 25, and the screw is the common type with equal distance and unequal depth. The reference temperature of barrel temperature is 150ºC-195ºC,Die Temperature is 180ºC-200ºC. The cooling water temperature is recommended to adopt step-by-step cooling to reduce the internal stress of insulating material.

Packing:
Net weight 25kg: Inner aluminum foil/polyethylene composite film bag, outer kraft paper composite bag,divided into A, B bags.
Bag A :Material A with 23.75 kg
Bag B :Material B with 1.25 kg

Storage:
The product should be stored in a clean, dry and ventilated warehouse, and should not be damaged by sun, rain, water and other abnormal conditions. Storage temperature should not be lower than 0ºC. The storage period of the product shall not exceed 6 months from the date of production.

Yellow Insulation Polymer Materials XLPE