China Single Sided Margin Metalized PP Film For Capacitor Use, Find details about China Metallized Film, Capacitor Film from Single Sided Margin Metalized PP Film For Capacitor Use
Properties | Unit | Typical value |
Density | g/cm3 | 0.905±0.005 |
Thickness | μm | 2.2~15 |
Tensile Strength | MD(MPa) | >=100 |
Elongation at Break | (%) | 20~200 |
Elastic Modulus | MD(MPa) | 2800 |
Heat Shrinkage | (%) | <=5(120ºC,10min) |
Wetting Tension | mN/m | 38(Corona treated side) |
Surface Roughness | μm | 0.08 |
Melting Point | ºC | 172 |
Volume Resistivity | Ω.m | >1015 |
Break-down Voltage | V/μm | >=350(23ºC,DC) |
Dielectric Constant | 2.2(20ºC,1KHz) | |
Dissipation Factor | <=4×10-4(20ºC,1KHz) | |
RC | Ω F | >=5×104 |
Properties | Unit | Typical value |
Density | g/cm3 | 1.4 |
Thickness | μm | <5 5~12 >=12 |
Tensile Strength | MD(MPa) | >=84 >=108 >=120 |
Elongation at Break | (%) | >=22 >=33 >=44 |
Elastic Modulus | MD(MPa) | 3500 |
Break-down Voltage | V/μm | >=200(23ºC,DC) >=250(23ºC,DC) |
Heat Shrinkage | (%) | <=2.5(150ºC,10min) |
Surface Roughness | μm | 0.095 |
Melting Point | ºC | 256 |
Volume Resistivity | Ω.m | >1015 |
Dielectric Constant | 3.2 | |
Dissipation Factor | - | <=60×10-4 |
RC | Ω F | >=1×104 |