China High-End Custom Plastic Hook Maded by Nylon and Polymers Injection Hook, Find details and Price about China Nylon, Clothing from High-End Custom Plastic Hook Maded by Nylon and Polymers Injection Hook
composition | Hook :100% polyamide |
Weft and warp ,PA 6 | |
Hook ,PA66 | |
Base PA6 | |
Coating type: Polyurethane adhesive | |
Mono-Filament | |
Loop : 100% polyamide | |
Weft and Warp ,PA6 | |
Loop ,PA 6 | |
Base PA6 | |
Coating type: Polyurethane adhesive | |
Multi-filament | |
construction | woven with cold-cut sewing edges |
Shade range | Custom made |
Available widths (mm) | 16, 20, 25, 30, 38, 50, 100,150,160 |
Width Tolerance (mm) | 16,20,25mm: ±1.0mm |
30,38,50mm: ±1.5mm | |
100mm: -1.0/+2.0mm | |
resistance to heat | softening point 180°C, melting point 200-215°C |
resistance to temperature | no change at -30°C to +140°C |
strength in water | retain 50% of closure strength in water and recovers 100% after drying |
resistance to chemicals | resistance against diluted acids & alkalines at low temperature, trichloroethylene & solvents used for dry cleaning |
influence of insects, mold | not affected |
influence of humidity | in humidity over 90% RH, closure strength is somewhat reduced |
resistance to UV | limited resistance, use polyester tape if exposure to high UV light |
shrinkage after washing at 60°C /30 min. | hook & loop (lengthwise/widthwise): max. 2% |
Test method: ISO 6330 | |
Fraying | None |
Tensile strength (N/cm) | Hook :200.0-384.0 |
ISO 13934-1:2013 | Loop:200.0-301.0 |
Minimum for H&L: 200 | |
Average: 300 | |
Stretch at breaking (%) | 35%- 50% |
ISO 13934-1:2013 | Minimum: 30% |
Actual or Average: 40% | |
Quality ISO | GB/T 19001-2008/ ISO9001:2008 |
Reach | Confirmed |
dyestuffs | no harmful AZO dyestuffs |
Dimethylfumarate (DMFu) | Do not contain |
Joints type | Hot melt |
No of joints per roll | Most of no any joints ,very few roll have one or two joints |