Ar500 Ar400 Mn13 Wear Plate/Abrasion Resistant Steel Plate

China Ar500 Ar400 Mn13 Wear Plate/Abrasion Resistant Steel Plate, Find details about China Wear Steel Plate, Xar450 Steel Plate from Ar500 Ar400 Mn13 Wear Plate/Abrasion Resistant Steel Plate

Basic Info.

Model NO.

steel plate

Hardness Range

360hb-500hb

Alloy Steel Plate

Hot Rolled Plate

Ready Stock

Yes

Cutting and Bending

Yes

Trademark

DaJin

Specification

2mm-150mm

Origin

Shandong

Model NO.

steel plate

Hardness Range

360hb-500hb

Alloy Steel Plate

Hot Rolled Plate

Ready Stock

Yes

Cutting and Bending

Yes

Trademark

DaJin

Specification

2mm-150mm

Origin

Shandong

Product Desciption

Wear Resistant Steel plate
Abrasion Resisant Plate AR400 AR500

Abrasive resistant steel
Hard steel plate
hard 500 hard 400
steel plate cutting and bending

Product Descrition
1.Production Process
1)Steelmaking process Flow Chart
Blast Furance+Hot Metal Ladle Truck+KR Hot Metal Treatment+Converter+LF Refining Furnace+RH Vacuum Degassing Furance+Con-cast

2.Rolling Process Flow Chart
Reheating Furance+High-pressure Water Descaling+Edger Mill+Roughing Mill+Finishing Mill+Accelerated cooling+Hot Leveler+Marking and Spray Printing+Cooling Bed+On-line UT+Crop Shear+Double-side Trimming Shear+Cut-to-length Shear+Measurement+Marking and Spray Printing+Cold Leveler/Heat treatment

3.Heat-Treatment Flow Chart
Plate+Shot Blasting+Quenching Furance+Quenching Machine+Tempering Furance+Warm Leveler+Cooling Bed+Cutting+Cold Leveler+Finishing&Packaging

4.Thickness and Width
Thickness:3mm-150mm
Width:1600mm-4100mm

5.Main Grade
Germany:XAR400,XAR450,XAR500,XAR600,Dillidur400,Dillidur500
Belgium:QUARD400,QUARD450,QUARD500
France:FORA400,FORA500,Creusabro4800,Creusabro8000
Baosteel:B-HARD360,B-HARD400,B-HARD450,B-HARD500
HBIS:NM360,NM400,NM450,NM500
Finland:RAEX400,RAEX450,RAEX500
Japan:JFE-EH360,JFE-EH400,JFE-EH500,WEL-HARD400,WEL-HARD500

6.Chemical Composition&Property

Grade	c	Si	Mn	P	S	Al	Cr+Ni+Mo	Nb+V+Ti
NM400	0.10-0.40	0.20-0.40	1.00-2.00	Max 0.015	Max 0.003	Min 0.020	Max 0.9	Trace Amount
NM450	0.10-0.40	0.20-0.40	1.00-2.00	Max 0.015	Max 0.003	Min 0.020	Max 1.2
NM500	0.10-0.40	0.20-0.45	1.00-2.00	Max 0.015	Max 0.003	Min 0.020	Max 1.5
NM550	0.10-0.50	0.20-0.45	1.00-1.50	Max 0.015	Max 0.003	Min 0.020	Max 2.0
NM600	0.10-0.50	0.20-0.45	1.00-1.50	Max 0.015	Max 0.003	Min 0.020	Max 2.5
XCHD400	0.10-0.30	0.20-0.40	1.00-2.00	Max 0.015	Max 0.003	Min 0.020	Max 0.1
XCHD450	0.10-0.40	0.20-0.40	1.00-2.00	Max 0.015	Max 0.003	Min 0.020	Max 0.9
XCHD500	0.10-0.40	0.20-0.45	1.00-2.00	Max 0.015	Max 0.003	Min 0.020	Max 1.5

Grade	Size(mm)	RP0.2(Mpa)	Rm(Mpa)	A50(%)	AKV,(ºC)	KV2(J)			HBW
NM400	100	1233	1337	15	-20	35	37	42	415
NM450	60	1345	1434	9.5	-20	72	59	58	455
NM500	50	1608	1706	10.5	-20	43	50	45	495
XCHD400	35	1025	1161	17.5	-40	52	45	40	413
XCHD450	30	1281	1400	10.5	-40	45	48	52	453
XCH500	6	1465	1529	13.5	-40	24	24	22	515

8.Cerifications
9 Classification Society
ISO 9001 Certified

9.Packaging&Shipping
Seaworthy packaging by container or bulk cargo vessel
Delievery time:stock size within 7days;new material within 40days
10.Our services
We can cut and bend steel plate according to customer's requriement or drawing,packaging according to customers' request
11.Application
By adopting the combined chemical composition design of low carbon,low sulfur,low phosphorous and micro-alloy,by applying the offline quenching and other advanced automation technologies,our wear resistant(Abrasion Resisant) plate are popular at home and abroad. Mainly used for thermal Power plant,Coal Mines ,Cement Mills,Loading Machinery,Mining Machinery,Project Machinery.Metallurgical Machinery,Wear resistant plate also can be applied in Sand Mill Cylindrical Shell, Vane, Mechanical Parts used in yard and port, Bearing Structure Parts etc.

2.Wear resistant steel plate

Name	Grade	Thickness(mm)	Width(mm)	Supply condition	Our Service
Hard plate/Abrasion steel plate/wear resistant steel plate	NM360/NM400/NM500	6-80	1600-3500	Q,Q+T,TMCP+T	patined/cutting/ bending according to client's drawing
	NM500/NM550	6-70
	NM600	6-70

Grade	Thickness(mm)	Tensile Strength/Mpa	Enlongation/%	-20ºC Longitudinal Impact Value/J	Hardness/HB
NM360	<80	≥1100	≥12	≥24	330-390
NM400	<80	≥1200	≥10	≥24	370-430
NM450	<80	≥1250	≥7	≥24	420-480
NM500	<70	/	/	≥24	≥470
NM550	<70	/	/	/	≥530
NM600	<60	/	/	/	≥570

Testing results of wear resistant steel plates
Grade	Thickness(mm)	Hardness/HB	Tenslile strength/MPA	Enlongation	-20ºC Longitudinal Impact Value/J
NM400	6	406	1280	16	76/87/65
NM400	20	404	1260	17.5	57/57/65
NM400	50	398	1300	25.5	40/35/45
NM400	80	417	1320	23.5	48/51/49
NM450	6	439	1320	23	43/38/30
NM450	20	448	1460	24	62/52/66
NM450	50	444	1340	21	35/37/40
NM450	80	454	1410	21.5	40/41/49
NM500	6	485	1653	11.5	33/26/32
NM500	20	505	1730	17.5	36/33/30
NM500	50	499	1569	16.5	42/38/32
NM500	70	488	1540	12.5	60/55/64
NM550	6	540	1853	10.5	/
NM550	20	545	1855	11.5	/
NM550	50	550	1900	10.5	/
NM550	70	545	1840	12	/
NM600	6	575	/	/	/
NM600	20	580	/	/	/
NM600	50	582	/	/	/
NM600	70	578	/	/	/

3.Abrasion steel plates

Application:
Crusher,sieve plate,feeding hopper,blade plate,conveyor,bucket,cutting edge,dump truck,scraper,industrial truck,railway wagon,bulldozer,excavator,screw conveyor and etc.

wear resistant steel plate NM400 property

Chemical Composition	steel plate	C	Si	Mn	P	S	Cr	Ni
	Thicness	%	%	%	%	%	%	%
	2-120mm	0.11-0.20	0.38-0.55	1.20-1.55	0.005-0.020	0.005-0.010	0.01-0.60	0.004-0.04
Hardness	370-430HB
Mechanical Properties	10mm thickness steel plate typical value		Yiled Strength		Tensile Strength		Elongation
			Re		Rm		A5
			Mpa		Mpa		%
			>1050		>1250		12
Impact Toughness	10mm thickness steel plate typical value		Test			Impact test
			Temperature			Charpy-V Longitudinal
			ºC			J
			-20			40

wear resistant steel plate NM450 property

Chemical Composition	steel plate	C	Si	Mn	P	S	Cr	Ni
	Thicness	%	%	%	%	%	%	%
	2-120mm	0.20-0.26	0.75-0.95	1.60-1.80	0.015-0.020	0.005-0.010	0.01-0.60	0.001-0.04
Hardness	420-480HB
Mechanical Properties	10mm thickness steel plate typical value		Yiled Strength		Tensile Strength		Elongation
			Re		Rm		A5
			Mpa		Mpa		%
			>1150		>1300		10
Impact Toughness	10mm thickness steel plate typical value		Test			Impact test
			Temperature			Charpy-V Longitudinal
			ºC			J
			-20			30

Application:Sieve plate,wear resistant liner,feeding hopper,powder concentrator,conveyor,scraper conveyor,dump truck,screw conveyor and etc.

Chemical Composition	steel plate	C	Si	Mn	P	S	Cr	Ni
	Thicness	%	%	%	%	%	%	%
	2-120mm	0.25-0.35	0.25-1.75	0.40-1.60	0.015-0.020	0.005-0.010	0.20-0.80	0.001-0.03
Hardness	470-530HB
Mechanical Properties	10mm thickness steel plate typical value		Yiled Strength		Tensile Strength		Elongation
			Re		Rm		A5
			Mpa		Mpa		%
			>1250		>1500		8
Impact Toughness	10mm thickness steel plate typical value		Test			Impact test
			Temperature			Charpy-V Longitudinal
			ºC			J
			-20			20

Application:Wear resistant strip,chute,sieve plate,knives,cutting edge and etc.
NM550

Chemical Composition	steel plate	C	Si	Mn	P	S	Cr	Ni
	Thicness	%	%	%	%	%	%	%
	2-120mm	0.30-0.37	0.2-0.405	0.40-1.60	0.010-0.020	0.005-0.010	0.30-0.80	0.002-0.60
Hardness	520-580HB
Mechanical Properties	10mm thickness steel plate typical value		Yiled Strength		Tensile Strength		Elongation
			Re		Rm		A5
			Mpa		Mpa		%
			>1300		>1550		6
Impact Toughness	10mm thickness steel plate typical value		Test			Impact test
			Temperature			Charpy-V Longitudinal
			ºC			J
			-20			12

Application:Wear resitant strip,chute,sieve plate,cutting edge and etc.
NM600

Chemical Composition	steel plate	C	Si	Mn	P	S	Cr	Ni
	Thicness	%	%	%	%	%	%	%
	2-120mm	0.35-0.40	0.20-0.80	0.40-1.60	0.010-0.020	0.005-0.010	0.25-1.00	0.002-0.60
Hardness	560-620HB
Mechanical Properties	10mm thickness steel plate typical value		Yiled Strength		Tensile Strength		Elongation
			Re		Rm		A5
			Mpa		Mpa		%
			>1450		>1650		5
Impact Toughness	10mm thickness steel plate typical value		Test			Impact test
			Temperature			Charpy-V Longitudinal
			ºC			J
			-20			8

NM650

Chemical Composition	steel plate	C	Si	Mn	P	S	Cr	Ni
	Thicness	%	%	%	%	%	%	%
	2-120mm	0.40-0.50	0.20-0.80	0.40-1.60	0.010-0.020	0.005-0.010	0.80-1.50	0.002-0.60
Hardness	620-680HB
Mechanical Properties	10mm thickness steel plate typical value		Yiled Strength		Tensile Strength		Elongation
			Re		Rm		A5
			Mpa		Mpa		%
			>1500		>1750		3
Impact Toughness	10mm thickness steel plate typical value		Test			Impact test
			Temperature			Charpy-V Longitudinal
			ºC			J
			-20			6

We have CNC flame,underwater plasma,Laser cutting machine,3600tons of bending machine,1600tons,1000tons of press machine,veneer reeling machine,CNC machine center,drilling machine,wire cutting and other advanced large cutting machining equipment.

Our CNC cutting equipment

CNC Flame Cutting machine
Effective cutting length:20000mm
Effective cutting width:5000mm
Max cutting thickness:120mm
Cutting precision:+/-2mm
Cutting speed:50--6000mm/min

CNC plasma cutting machine underwater
Effective cutting length:17000mm
Effective cutting width:5000mm
Max cutting thickness:30mm
Cutting precision:+/-1mm
Cutting speed:50--6000mm/min

CNC Laser cutting machine
Effective cutting length:20000mm
Effective cutting width:5000mm
Max cutting thickness:20mm
Cutting precision:+/-0.2mm
Cutting speed:50--6000mm/min

CNC Bending equipment
3600tons of bending machine
Max bending length:12200mm
Max bending width:4400mm
Bending angle:<90 degree

4.Bulletproof steel plate
Armor plate
Armour steel plate
Ballistic armour plate,pulletproof plate
Bulletproof sheet metal /armoured steel plates against AK47 refle
Armor Ballistic Steel Plate

Grade	Thickness	C	Si	Mn	P	S	Cr	Ni	Mo	B
PRO500	2.5-20mm	0.24-0.38	Max 0.50	1.10-1.70	Max 0.025	Max 0.025	0.30-1.20	Max 1.2	Max 0.8	0.0020-0.005

Hardness after Quenching:470HB-530HB

Grade	Test thickness	Weapons&ammunition	Bullet speed(M/S)	Shooting distance (M)	Ref. Standard
PRO 500	2.5-3.0mm	Handgun&Magum 79 type-micro submachine gun 7.62X25 HC	440 500	5	N.I.J.0108.01 IIA, II, IIIA
PRO 500	4.0mm	56 type submachine gun AK47 7.62x39	720	10	CN:C
PRO 500S	5.5mm	M16 5.56 x 45 (SS109) NATO 7.62x51	950 840	10	EN1063 B6
PRO 500	6.5mm	M16 5.56 x 45 (SS109) NATO 7.62x51	950 840	10	EN1063 B6 NIJ 0108.01 III
PRO 500	8.0mm	Rifle 5.8 x 45	940	10
PRO 500S	8.2mm	M16 5.56 x 45 (M193)	980	10	STANAG 4569 I
PRO 500	10.0mm	M16 5.56 x 45 (M193)	980	10	STANAG 4569 I
PRO 500	12.5mm	7.62 x 39 API	720	30	STANAG 4569 II
PRO 500	14.5mm	7.62 x 51 HC1 API 7.62 x 39 API	850	10	EN1063 B7

PRO500,26SiMnMo(Gy5),28CrMo(Gy4),22SiMn2TiB(616),32CrNi2MoTiA(A-8),32Mn2Si2MoA(F-3),32Mn2SiA(F-2),AMFD54,AMFD56,AMFD53,AMFD16,AMFD85,AMFD95,AMFD3,AMP500,AMP550,AMBP500,AMBP790.

Delivery state
Hot-rolled flat,or finished steel plates by cutting for abnormal shape
Steel plate shape and dimensional deviation fully meet the requirement of GB/T 709-2006
Especially the steel plate thickness deviation can be controlled in actual +0.15mm
Applicable Bulletproof standard

The ministry of Pubulic Security of the People's Republic of China.Chinese Military standard(GA164-2005) Protection grade from low to high marks A,B,C
NIJ body armor standard
The United Stateds UL752 bulletproof standard
German DIN52290 bulletproof standard
Eurpean EN1063 bulletproof standard
British BS5051 bulletprood standard

Bulletproof plate
Ballistic armours plate,Bulletproof plate
Armor plate
Ballistic steel plate

Bulletproof steel plate propety sheet
Grade	Thickness range (mm)	Hardness	Tensile strength	Yield Strength	Enlogation	90ºcold bending test	,-20ºImpact Value,KV2(J)
BHFD3 (PRO500)	2.0-120	470-550HB	Min 1250Mpa	Min 1100Mpa	Min 7%	R>=8T	>=10
Chemical Composition(%)
C	Si	Mn	P	S	Cr	Mo	Ni	B
<=0.36	<=1.70	<=2.20	<=0.02	<=0.015	<=0.70	<=0.50	<=0.60	<=0.0050

Delivery state
Hot-rolled flat,or finished steel plates by cutting for abnormal shape
Steel plate shape and dimensional deviation fully meet the requirement of GB/T 709-2006
Especially the steel plate thickness deviation can be controlled in actual +0.15mm
Applicable Bulletproof standard

The ministry of Pubulic Security of the People's Republic of China.Chinese Military standard(GA164-2005) Protection grade from low to high marks A,B,C

2.NIJ body armor standard
3.The United States UL752 bulletproof standard
4.German DIN52290 bulletproof standard
5.European EN1063 bulletproof standard
6.British BS5051 bulletproof standard

Advantages:
1. Low-alloy micro-alloying,better performance.
2. VD make harmful gases, impurities to a minimum,plate can be welded, cold bend.
3. Precise hot-rolled plate type: the minimum thickness tolerance, the highest two-way flatness.
4. Self-controlled spray quenching: fine microstructure, hardness distribution

PRO 500 armored bullet-proof steel applications
☆ bullet-proof doors, bullet-proof helmets, body armor, bullet-proof shields; bank counters, confidential safes;
☆ riot cars, bullet-proof armored cars, armored personnel carriers, tanks;
Submarine, landing craft, anti-smuggling boats, helicopters and so on.

Cold bending of armor plate
Follow these guidelines to avoid cracks when cold bending:
Large enough indenter radius and mold fulcrum spacing;
Bending by the tensile side and the edge of the plate must be polished, rounded edges at right angles;
Indenter and mold fulcrum must be smooth;
Particularly necessary when heated to below 250 ºC.
Ar500 Ar400 Mn13 Wear Plate/Abrasion Resistant Steel Plate