China Vinyl Acetate Acrylic Emulsion Used for Building Seal, Find details about China Vinyl Acetate Acrylic Emulsion, Vinyl Acetate Resin from Vinyl Acetate Acrylic Emulsion Used for Building Seal
Vinyl acetate-acrylate emulsion----HN-154VE | ||
HN-154VE | Appearance | milk white liquid |
Solid content | 53±1wt% | |
Viscosity.cps(25ºC) | 100-500 | |
Particle Size(nm) | 250-450 | |
PH | 3.5-4.5 | |
Glass Transition Temperature (Tg) | -18ºC | |
Minimum Film Formation Temperature(MFT) | 0ºC |
HN-154VE | Appearance | milk white liquid |
Solid content | 53±1wt% | |
Viscosity.cps(25ºC) | 100-500 | |
Particle Size(nm) | 250-450 | |
PH | 3.5-4.5 | |
Glass Transition Temperature (Tg) | -18ºC | |
Minimum Film Formation Temperature(MFT) | 0ºC | |
HN-101D | Appearance | light blue |
Solid content | 47±1wt% | |
Viscosity.cps(25ºC) | 100-1000 | |
Particle Size(nm) | 100-180 | |
PH | 7.0-8.0 | |
Minimum Film Formation Temperature(MFT) | 25ºC | |
Ca2+ stability 5%CaCl2: emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass | |
HN-166T | Appearance | light blue |
Solid content | 50±1wt% | |
Viscosity.cps(25ºC) | 1500-3000 | |
Particle Size(nm) | 90-160 | |
PH | 6.0-7.0 | |
Minimum Film Formation Temperature(MFT) | 0ºC | |
Ca2+ stability 5%CaCl2: emulsion =1:3, 48h, No Flocculation, No Stratification. | pass |