Jgs3 Optical IR Quartz Glass Windows for Optical Communication Fields

China Jgs3 Optical IR Quartz Glass Windows for Optical Communication Fields, Find details about China Optical Glass, Jgs3 from Jgs3 Optical IR Quartz Glass Windows for Optical Communication Fields

Basic Info.

Model NO.

JGS3

Angle of incidence

45°

Shape

Customized

Certification

RoHS, ISO, CE

Customized

Trademark

Haisheng

Transport Package

Carton Package

Specification

customized

Origin

China

HS Code

9001909090

Model NO.

JGS3

Angle of incidence

45°

Shape

Customized

Certification

RoHS, ISO, CE

Customized

Trademark

Haisheng

Transport Package

Carton Package

Specification

customized

Origin

China

HS Code

9001909090

Product Desciption

JGS3 IR optical quartz glass windows for optical communication fileds

Product description:
Haisheng Optical can produce optical quartz glass windows, it can able to bear high temperature and high pressure, mostly applied to special ray source, optical instrument, etc. It can experiment temperature up to 1200 degree, intenerate temperatures to 1730 degree.
1.JGS1( Extreme UV optical quartz glass)
It is a high-purity optical quartz glass made by oxyhydrogen flame melting. Its satisfactory UV light transmission performance surpass all the other glass types in particular in the shortwave UV zone and can achieve a 90% transmission rate at the wavelength of 185nm. Hence it is an ideal choice for applications in the wavelength range of 185-2500nm.
2.JGS2 (UV optical quartz glass)
It is an optical quartz glass made by oxyhydrogen flame melting and is suggested for applications in the wavelength range of 220-2500nm.
3. JGS3 (Infrared quartz glass)
It has a good performance of infrared light transmission with a transmittance of over 85%. It is recommended for applications in the wavelength range of 260-3500nm.

Optical constants of Quartz glass


	JGS-1	JGS-2	JGS-3
Spectral characteristics The average transmittance	180-2500nm	200-2500nm	260-3500nm
90%	85%	85%
Bubble class	0	2	2
Birefringence	1-2	1-2	1-2
Grain structure	1	2	2
Fringe	1-2	1-2	2
Uniformity	1-2	2	2
Fluorescence	1	2	2
Radiation Performance	Does not change color	Slight discoloration	Change color

Physical properties of quartz glass


Mechanical properties	Standard value
Density	2.2g/cm³
Compressive strength	1100Mpa
Bending strength	67Mpa
Tensile strength	48Mpa
Poisson's ratio μ	0.14~0.17
Young's modulus E	72000Mpa
Rigidity modulus	31000Mpa
Mohs hardness	5.5~6.5


Thermal properties	Standard value
Transformation point	1280ºC
Softening point	1780ºC
Annealing Point	1250ºC
Specific heat(20~350ºC)	670J/kg.ºC
Thermal conductivity(20ºC)	1.4W/m.ºC
Index of refraction	1.4585
Coefficient of thermal expansion	5.5×10^-7cm/cm. ºC
Thermal processing temperature	1750~2050ºC
Short-term use temperature	1300ºC
Long-term use temperature	1100ºC