Polyurethane Rigid Foam Isocyanate Mdi and Blend Polyol
China Polyurethane Rigid Foam Isocyanate Mdi and Blend Polyol, Find details about China Polyol, Ab Material from Polyurethane Rigid Foam Isocyanate Mdi and Blend Polyol
Basic Info.
Material
Polyurethane
Main Agent Composition
Polyurethane Elastomer
Promoter Composition
Stabilizer
Composition
Organic Material
Trademark
wannate
Transport Package
Iron Drum
Specification
250kg/Drum
Origin
China
HS Code
3909310000
Material
Polyurethane
Main Agent Composition
Polyurethane Elastomer
Promoter Composition
Stabilizer
Composition
Organic Material
Trademark
wannate
Transport Package
Iron Drum
Specification
250kg/Drum
Origin
China
HS Code
3909310000
Product Desciption
POLYMERIC MDI 44V20L/PM200 /MR 200/ 5005S
Application
44V20L is a diisocyanate-diphenylmethane(MDI)-based composition containing some higher functionality isocyanates. The functionality is about 2.6-2.7. It is abrown liquid at ambient temperatures.
44V20L can be widely used in the production of rigid PU foam heat-insulating materials; also used in isocyanurate foam, paints, adhesives, structural foam,cellular integral skin foam, automotive bumper and interior parts, high-resilience foam and synthetic wood, etc. Due to its unique composition structure, 44V20L can provide better flowability. It is, therefore, particularly suitable for the production which require strict flowability of systems...
Typical Physical and Chemical Properties
Package(s)
210L iron drums, 250kg/drum
Storage
Since 44V20L is a reactive chemical, reaction with atmospheric moisture happens easily and leads to the formation of insoluble ureas and carbon dioxide gas, which can result in pressure build-up in closed containers and viscosity increase of the product.Containers must therefore be absolutely dry and carefully sealed after congested with nitrogen.
Containers of 44V20L should be kept properly closed and stored indoors at ambient temperature (15-35ºC) in a well-ventilated area. Storage at low temperature (below5ºC) may lead to some crystallization; this material must, therefore, be protected from frost.If crystallization does occur, the material should be heated by rolling the drum in a hot air oven at 70-80ºC to melt it out, and should then be thoroughly agitated before use. Melting in a water bath is not recommended.
Extended storage at temperatures above 50ºC is not recommended to prevent from the formation of insoluble solids and viscosity increase.
Shelf Life
Under recommended storage conditions, the shelf life of 44V20L is one year since the date of production.
The above information is for reference only. The specific value still provided by the manufacturer. Our company is not responsible for any legal liability.
Application44V20L is a diisocyanate-diphenylmethane(MDI)-based composition containing some higher functionality isocyanates. The functionality is about 2.6-2.7. It is abrown liquid at ambient temperatures.
44V20L can be widely used in the production of rigid PU foam heat-insulating materials; also used in isocyanurate foam, paints, adhesives, structural foam,cellular integral skin foam, automotive bumper and interior parts, high-resilience foam and synthetic wood, etc. Due to its unique composition structure, 44V20L can provide better flowability. It is, therefore, particularly suitable for the production which require strict flowability of systems...
Typical Physical and Chemical Properties
| Test Item(s) | Specification(s) |
| Appearance | Brown Liquid |
| Viscosity at 25ºC, mPa.S | 150-250 |
| NCO, % | 30.5-32.0 |
| Density 25ºC, g/cm3 | 1.220-1.250 |
| Acidity (HCl), % | ≤0.05 |
| Hydrolysable Chlorinea, % | ≤0.2 |
Package(s)
210L iron drums, 250kg/drum
Storage
Since 44V20L is a reactive chemical, reaction with atmospheric moisture happens easily and leads to the formation of insoluble ureas and carbon dioxide gas, which can result in pressure build-up in closed containers and viscosity increase of the product.Containers must therefore be absolutely dry and carefully sealed after congested with nitrogen.
Containers of 44V20L should be kept properly closed and stored indoors at ambient temperature (15-35ºC) in a well-ventilated area. Storage at low temperature (below5ºC) may lead to some crystallization; this material must, therefore, be protected from frost.If crystallization does occur, the material should be heated by rolling the drum in a hot air oven at 70-80ºC to melt it out, and should then be thoroughly agitated before use. Melting in a water bath is not recommended.
Extended storage at temperatures above 50ºC is not recommended to prevent from the formation of insoluble solids and viscosity increase.
Shelf Life
Under recommended storage conditions, the shelf life of 44V20L is one year since the date of production.
The above information is for reference only. The specific value still provided by the manufacturer. Our company is not responsible for any legal liability.
You Might Also Like
Zinc It Done Water-Based Galvanizing Spray Paint Aqueous Gal......
EPA/Carb Certificated Fuel Line Fuel Hose for Garden Machine......
100g high performance desiccant in Tyvek
Truck Spare Parts Weichai Engine Intake Rocker Arm Best
Art Glass Smoking Water Pipe ( AY 020)
Pdadmac 40% Cationic Polymer for Sludge Dewatering
Hot-Sale HDI Multilayer Printed Circuit Board Fr4 PCB Power ......
High-End Wall Mounted Storage Holder Rack for Kitchen Goldmi......
Rth -1100A Non Woven Sheet Cutting Machine Sheet Label Cutti......
Non Crosslinked Hyaluronic Acid Meso Filler for Lip Injectio......