China Sisic Ceramic Kiln Furniture, Silicon Carbide Beam, Roller, Nozzle, Heater for Heat Furnace 1380c, Find details about China Kiln Beam, Furnace Tube from Sisic Ceramic Kiln Furniture, Silicon Carbide Beam, Roller, Nozzle, Heater for Heat Furnace 1380c
Section Size (mm) | Thickness (mm) | Concentrated Loading(kg.m/L) | Uniformly Distributed Loading(kg.m/L) | |||
W Side | H Side | W Side | H Side | W Side | H Side | |
30 | 30 | 5 | 74 | 74 | 147 | 147 |
30 | 40 | 5 | 117 | 95 | 235 | 190 |
40 | 40 | 6 | 165 | 165 | 330 | 330 |
50 | 50 | 6 | 283 | 283 | 567 | 567 |
50 | 60 | 6 | 374 | 331 | 748 | 662 |
50 | 70 | 8 | 573 | 451 | 1143 | 902 |
60 | 90 | 9 | 1060 | 799 | 2120 | 1598 |
80 | 80 | 7 | 935 | 935 | 1869 | 1869 |
100 | 100 | 8 | 1708 | 1708 | 3416 | 3416 |
110 | 110 | 10 | 2498 | 2498 | 4997 | 4997 |
Test Data | ||
Item | Unit | Data |
Max temperature of application | ºC | 1380 |
Density | g/cm³ | ≥3.02 |
Open porosity | % | <0.1 |
Bending strength | Mpa | 250(20ºC) |
Mpa | 250(20ºC) | |
Modulus of elasticity | Gpa | 330(20ºC) |
Gpa | 300(1200ºC) | |
Thermal conductivity | W/m.k | 45(1200ºC) |
Coefficient of thermal expansion | K¯1×10¯6 | 4.5 |
Rigidity | 13 | |
Acid alkaline-proof | Excellent |