China 150 Degrees PVDF Kynar Heat Shrinking Tubing, Find details about China High Temperature Resistant Tube, Strong Acid and Alkall Resistant PTFE from 150 Degrees PVDF Kynar Heat Shrinking Tubing
Application: | Insulators, Electrical Winding Insulation, Winding Wire Coating Insulation, Electrical Base, Shell, Connector |
Type: | Insulation Sleeve |
Chemistry: | Hybrid Insulation |
Material: | Special Fluoropolymer |
Thermal Rating: | 175degrees |
Shrink ratio: | 2:1 |
Maximum Voltage: | >100KV |
Property | Test method | Soft (150 ° C) typical | Soft (175 ° C) typical |
Tensile strength | ASTM D2671 | ≥24.5M Pa | ≥34.5M Pa |
Ultimate elongation | ASTM D2671 | ≥150% | ≥150% |
Ultimate elongation after aging | 225ºC,168h | ≥100% | ≥100% |
Heat shock | 275ºC,4h | No dripping, no cracking | No dripping, no cracking |
Cold bend | -55ºC,4h | No cracking | No cracking |
Dielectric | ASTM D2671 | ≥15.7kV/mm | ≥31.5kV/mm |
Volume resistivity | ASTM D257 | ≥1013Ω.cm | ≥1013Ω.cm |
Flammability | UL-224 | VW-1 | VW-1 |
size | As supplied(mm) | After recovered(mm) | Standard packing | ||
inch | mm | Inside diameter(min) | Inside diameter(max) | Wall thickness | (m/pc,m/roll) |
3/64 | 1.2 | 1.2 | 0.6 | 0.25+0.05 | 1.2/200 |
1/16 | 1.6 | 1.6 | 0.8 | 0.25+0.05 | 1.2/200 |
3/32 | 2.4 | 2.4 | 1.2 | 0.25+0.05 | 1.2/200 |
1/8 | 3.2 | 3.2 | 1.6 | 0.25+0.05 | 1.2/200 |
3/16 | 4.8 | 4.8 | 2.4 | 0.25+0.05 | 1.2/100 |
1/4 | 6.4 | 6.4 | 3.2 | 0.30+0.08 | 1.2/100 |
3/8 | 9.5 | 9.5 | 4.8 | 0.30+0.08 | 1.2/100 |
1/2 | 12.7 | 12.7 | 6.4 | 0.30+0.08 | 1.2/100 |
3/4 | 19.1 | 19.1 | 9.5 | 0.43+0.08 | 1.2/50 |
1 | 25.4 | 25.4 | 12.7 | 0.48+0.08 | 1.2/50 |