Heat Shrinkable Halogen Free Wire Identification Sleeves
Description
MSVLU series is halogen free, environmentally friendly, heat shrinkable identification sleeves. It is made of cross-linked environmentally friendly polyolefin bombarded by high power electron beam with electronic accelerators to meet high end markets where highly reliable, economical and environmentally friendly cable& wire identification is required. It accords to the requirements of UL224, CAN/CSA C22.2. Shrink ratios, both 2:1 and 3:1 are available. See the below tables.
Features
Halogen free, ideally used for electronic or electrical circuits, communications, architectural industries
Temp. Resistance: 125°C
Highly flame retardant, VW-1
ROHS compliant and meet SONY SS-00259
High reliability, permanent identification
Heat sensitive, shrinking quickly
Computerized lettering or fonts at your disposal.
Standard Color: yellow, white
Rated Temperature
Order Description | Expanded As Supplied (mm) | Recovered After Heating (mm) | |||
Inner Diameter ID1 | Flatten width G | Dual Wall Thickness H | Inner DiameterID2 | Single Wall Thickness h | |
MSVLU-2X-1.6/ | 2.00±0.20 | 3.7±0.3 | 0.48±0.10 | ≤0.79 | 0.45±0.06 |
MSVLU-2X-2.4/ | 2.79±0.20 | 5.0±0.3 | 0.48±0.10 | ≤1.18 | 0.49±0.06 |
MSVLU-2X-3.2/ | 3.64±0.23 | 6.3±0.4 | 0.48±0.10 | ≤1.59 | 0.51±0.06 |
MSVLU-2X-4.8/ | 5.26±0.25 | 8.9±0.4 | 0.49±0.10 | ≤2.36 | 0.54±0.06 |
MSVLU-2X-6.4/ | 6.92±0.28 | 11.5±0.4 | 0.50±0.10 | ≤3.18 | 0.56±0.06 |
MSVLU-2X-9.5/ | 10.2±0.32 | 16.7±0.5 | 0.51±0.11 | ≤4.75 | 0.59±0.06 |
MSVLU-2X-12.7/ | 13.5±0.36 | 21.8±0.6 | 0.52±0.11 | ≤6.35 | 0.60±0.07 |
MSVLU-2X-19/ | 20.1±0.40 | 32.2±0.6 | 0.53±0.11 | ≤9.53 | 0.62±0.07 |
MSVLU-2X-25/ | 26.7±0.45 | 42.5±0.7 | 0.55±0.12 | ≤12.7 | 0.63±0.07 |
MSVLU-2X-38/ | 39.8±0.51 | 63.2±0.8 | 0.57±0.12 | ≤19.1 | 0.64±0.07 |
MSVLU-2X-51/ | 53.0±0.56 | 83.9±0.9 | 0.58±0.13 | ≤25.4 | 0.64±0.08 |
MSVLU-2X-76/ | 79.4±0.56 | 125.3±1.0 | 0.59±0.13 | ≤38.1 | 0.64±0.09 |
Order Description | Expanded As Supplied (mm) | Recovered After Heating (mm) | |||
Internal Diameter ID1 | Flatten Width G | Dual Wall Thickness H | Inner Diameter ID2 | Single Wall Thickness h | |
MSVLU-3X-1.6/ | 2.00±0.20 | 3.7±0.3 | 0.47±0.10 | ≤0.53 | 0.52±0.06 |
MSVLU-3X-2.4/ | 2.79±0.20 | 5.0±0.3 | 0.47±0.10 | ≤0.79 | 0.57±0.06 |
MSVLU-3X-3.2/ | 3.64±0.23 | 6.3±0.4 | 0.48±0.10 | ≤1.06 | 0.61±0.06 |
MSVLU-3X-4.8/ | 5.26±0.25 | 8.9±0.4 | 0.49±0.10 | ≤1.59 | 0.67±0.06 |
MSVLU-3X-6.4/ | 6.92±0.28 | 11.5±0.4 | 0.50±0.10 | ≤2.36 | 0.71±0.06 |
MSVLU-3X-9.5/ | 10.2±0.32 | 16.7±0.5 | 0.52±0.11 | ≤3.18 | 0.77±0.06 |
MSVLU-3X-12.7/ | 13.5±0.36 | 21.8±0.6 | 0.53±0.11 | ≤4.75 | 0.80±0.07 |
MSVLU-3X-19/ | 20.1±0.40 | 32.2±0.6 | 0.55±0.11 | ≤6.35 | 0.84±0.07 |
MSVLU-3X-25/ | 26.7±0.45 | 42.5±0.7 | 0.56±0.12 | ≤8.47 | 0.86±0.07 |
MSVLU-3X-38/ | 39.8±0.51 | 63.2±0.8 | 0.57±0.12 | ≤12.9 | 0.89±0.07 |
MSVLU-3X-51/ | 53.0±0.56 | 83.9±0.9 | 0.57±0.13 | ≤17.2 | 0.90±0.08 |
MSVLU-3X-76/ | 79.4±0.56 | 125.3±1.0 | 0.59±0.13 | ≤25.8 | 0.92±0.09 |
No. | Sizes | Packaging (Pcs/Reel) | |
Box 210 | Box 146 | ||
1 | Φ1.6 | 2500 | 250 |
2 | Φ2.4 | 2500 | 250 |
3 | Φ3.2 | 2000 | 250 |
4 | Φ4.8 | 2000 | 250 |
5 | Φ6.4 | 1500 | 250 |
6 | Φ9.5 | 1000 | 250 |
7 | Φ12.7 | 500 | 250 |
8 | Φ19 | 500 | 250 |
9 | Φ25 | 500 | 250 |
10 | Φ38 | 250 | 250 |
11 | Φ51 | 250 | 250 |
12 | Φ76 | 250 | 250 |
Performance | Indicators | Test Method | ||
Typical properties | Unit | States | ||
Tensile Strength | Mpa | Unaged | ≥10.3 | ASTM G 154,MIL-DTL-23053E ISO 37,500mm/min 175°C,168h,ISO 188 |
Heat aged/ After fluids/UV aged | ≥6.9 | |||
Elongation at break | % | Unaged | ≥200 | |
Heat aged/ After fluid | ≥100 | |||
Secant Modulus | Mpa | Unaged | <173 | ASTM D 882 |
Voltage Withstand | V | Unaged / After aged | 2500V, No breakdown in 60 sec. | IEC 243,ASTM G 154 175°C,168h,ISO 188 |
Dielectric Strength | MV/m | Before aged | ≥19.7 | |
Heat aged/ After fluid/ UV aged | ≥15.8 | |||
Volume Resistivity | Ω.cm | Unaged | ≥1014 | IEC 93 |
Dielectric constant | - | Unaged | - | ASTM 150 |
Water Absorption | - | Unaged | ≤1.0 | ASTM 570,23°C,24h |
Bare Copper Corrosion | - | Unaged | No corrosion | 23°C,Rh 95±5%,24h 175°C,16h |
Heat Shock | - | Unaged | No cracks, flowing, dripping | Wind to the specified mandrel,225°C,4h |
Cold Flexibility | - | Unaged | No cracks | Wind to the specified mandrel, -30°C, 1h |
Flammability | - | Unaged | VW-1 | IEC 60332-1-3 Ed.1.0 b:2004 |
Longitudinal Change | % | Unaged | 2X: -10~+1 | 200°C,Constant 3min |
3X: -15~+5 | ||||
Smoke Density | - | Unaged | - | DIN 5510-2 |
Toxcity Index | - | Unaged | - | BS 6853:1999 |