3.4 a B Glue Mdi Based Glue PU Polyurethane Selant Paste for Composite Panel

China 3.4 a B Glue Mdi Based Glue PU Polyurethane Selant Paste for Composite Panel, Find details about China Glue, Adhesive from 3.4 a B Glue Mdi Based Glue PU Polyurethane Selant Paste for Composite Panel

Model NO.
LY-8605/LY-6201
Characteristic
Weatherability
Promoter Composition
Curing Agent
Composition
Polymer
Color
Yellow
Density (Uncured)
About 1.5g/cm3
Viscosity
15000-23000MPa.S
Shaw Intensity (GB/T 531-2008)
About 65
Shear Strength(GB/T 7124-2008)
≥10MPa
Color After Being Mixed
Faint Yellow
Trademark
G-TECH@
Transport Package
Drums, IBC Drums, Tank
Specification
pure
Origin
China
Model NO.
LY-8605/LY-6201
Characteristic
Weatherability
Promoter Composition
Curing Agent
Composition
Polymer
Color
Yellow
Density (Uncured)
About 1.5g/cm3
Viscosity
15000-23000MPa.S
Shaw Intensity (GB/T 531-2008)
About 65
Shear Strength(GB/T 7124-2008)
≥10MPa
Color After Being Mixed
Faint Yellow
Trademark
G-TECH@
Transport Package
Drums, IBC Drums, Tank
Specification
pure
Origin
China
Description
The product of LY-8605/LY-6201 is two-component polyurethane adhesive. Component A is polyhydroxy mixture, and Component B is isocyanate prepolymer. This product is suitable for sandwich structure, being used for structural bonding of wood, glass epoxy, aluminum plate, steel plate and other materials with various types of honeycomb structure, polyurethane sandwich panel, polystyrene foam board, rock wool board, etc.  
Technical Index
Product No.LY-8605LY-6201
Color
Color after being mixed		WhiteBrown
Faint yellow
Density (uncured)About 1.5g/cm3About 1.2g/cm3
Viscosity15000-23000mPa.s200-300mPa.s
Shaw intensity (GB/T 531-2008)About 65
Shear strength(GB/T 7124-2008)≥10MPa
Quality guarantee period (Sealed below 25ºC)6 months3 months
Note: The above density, viscosity, applicable period and open time are measured at 23ºC, 50%RH.
Product Features
1. No foaming; no bulging; excellent bonding strength;
2. Fast curing speed; high shear strength;
3. Excellent humidity and heat resistance, weather resistance;
4. No irritant gas is generated during coating and curing.
Usage
Before using the base resin, please stir well. Mix strictly according to the required ratio. Stir quickly. After the color is uniform, stir for 1-2 minutes.
Packing Specification
Component A: 25 kg/barrel; Component B: 5 kg/barrel.
Component A: 1250 kg/barrel; Component B: 250 kg/barrel.
The products can be packed according to customer needs.
Matters Needing Attention
1. After preparation, the adhesive should be used up within pot life; if the viscosity of the remaining adhesive is too high, it can not be used.
2. Do not mix this product with other adhesives. Please consult our company's technical department if needed.
3.4 a B Glue Mdi Based Glue PU Polyurethane Selant Paste for Composite Panel3.4 a B Glue Mdi Based Glue PU Polyurethane Selant Paste for Composite Panel
3.4 a B Glue Mdi Based Glue PU Polyurethane Selant Paste for Composite Panel

---------------------------------------------Construction Cases---------------------------------------------------
3.4 a B Glue Mdi Based Glue PU Polyurethane Selant Paste for Composite Panel
 

You Might Also Like