Al/Zn Heavy Egde (Single-sided) Metallized Polypropylene Film for Capacitor Use

China Al/Zn Heavy Egde (Single-sided) Metallized Polypropylene Film for Capacitor Use, Find details about China Al/Zn Heavy Egde (Single-sided) Metallized Polypr, Heavy Egde Metallized Film from Al/Zn Heavy Egde (Single-sided) Metallized Polypropylene Film for Capacitor Use

Model NO.
MPP film
Processing Type
Multiple Extrusion
Metallized
Zinc / Alunimin Alloy
Thickness
4mic,5mic,6mic,7mic,8mic,9mic
Width
9mm-620mm
Film
Aluminum-Zinc Alloy Film
Model Number
Mpp
Margin
2.5mm,2.0mm,1.5mm
Md
2.7%
Td
0.1%
Trademark
csf capacitor film
Transport Package
Capacitor Film for Cartons Packing
Specification
ISO, CQC, SGS
Origin
Tongling City, China
HS Code
3920590000
Model NO.
MPP film
Processing Type
Multiple Extrusion
Metallized
Zinc / Alunimin Alloy
Thickness
4mic,5mic,6mic,7mic,8mic,9mic
Width
9mm-620mm
Film
Aluminum-Zinc Alloy Film
Model Number
Mpp
Margin
2.5mm,2.0mm,1.5mm
Md
2.7%
Td
0.1%
Trademark
csf capacitor film
Transport Package
Capacitor Film for Cartons Packing
Specification
ISO, CQC, SGS
Origin
Tongling City, China
HS Code
3920590000
Metallized film for capacitor use
Products:
1.Aluminum metallized polypropylene film.
2.Aluminum metallized polypropylene safety film.
3.Zinc-Aluminum alloy metallized polypropylene film with heavy edge.
4.Zinc-Aluminum alloy metallized polypropylene safety film with heavy edge.
5.Zinc-Aluminum alloy metallized polypropylene film with heavy edge and slope metallized film.
6.Aluminum metallized polyester film.
7.Zinc-Aluminum alloy metallized polyester film with heavy edge.
8.Zinc-Aluminum Alloy metallized polypropylene film with high ssquare resistance
9. According to customer requirement design to producing all kinds of metallized film for capacitor used.

Cores:
1.Material:Plastic.
2.Width:Film Slit Width±0.3mm.
3.Inner Diameter:75mm+1.0mm/-0.5mm.

Roll Outer Diameter:
Slit widths(W)Recommend outer diameter(D)
4.5mm≤W<10mm140mm≤D≤185mm
10mm≤W<25mm150mm≤D≤185mm
25mm≤W<50mm 150mm≤D≤240mm
50mm≤W150mm≤D≤350mm

Specifications of metallized film:
1)Metallized polypropylene film

Properties
Unit
Requirements
Densityg/cm30.905±0.005
Thicknessµm3.8~15

Tensile Strength		MD
(MPa)		≥100

Elongation at Break		MD
(%)		40~200

Heat Shrinkage		MD
(%)		≤5(120°C,10min)
(120°C,10min)

Break-dowm voltage		V/µm≥350(23°C,DC)

Coating square resistance		 Al1.5±0.52.0±0.52.5±0.53±1

Zn/Al		(heavy-edge area):3±1
(non heavy-edge area):(6~7.5)±30%
With gradient square(heavy-edge area):3±1
(non heavy-edge area):(2~20)

Dissipation Factor		-≤4×10-4 (20ºC,1KHz)
RCΩF≥5×104

2.)Metallized polyester Film

Properties
Unit
Requirements
Densityg/cm31.34
Thicknessµm<55~12>12

Tensile Strength		MD
(MPa)		≥84≥108≥120

Elongation at Break		MD
(%)		≥22≥33≥44

Break-dowm voltage		V/µm≥200
(23°C,DC)		≥250
(23°C,DC)

Heat Shrinkage		MD
(%)		≤3(120°C,10min)

Coating square resistance		 Al1.5±0.52.0±0.52.5±0.53±1

Zn/Al		(heavy-edge area):3±1
(non heavy-edge area):(6~7.5)±30%

Dissipation Factor		-≤60×10-4(20ºC,1KHz)
RCΩF≥1×104
         

Note: Coating square resistance annotation is a typical value,can be customized.

Packing:
1.Roll films are packed in vacuum plastic bag and heat-sealed with desiccants.
2.Bags are marked with ables of types
3.The bags are packed in carton cases.
4.The cartons are wrapped in wooden cases or reinforced carton.
Storge:
1.Metallized film should be stored in its original package until its use with temperature 5~35º Cand humidity less than 85%RH.
2.Metallized layer is easily oxidized when exposure to moisture. Therefore, the film should be used as soon as possible when opened.
3.The recommended temperature is 15-25ºC with humidity less than 60%RH after the package is open.
4.With original sealed package,and stored in the above mentioned conditions, the storage time can be as following:
Al metalized Film:12 months from the delivered date..
Al/Zn Alloy metalized Film: As Zn is relatively unstable, preservation period(from delivery date) depends on the resistance of the film:
≤10Ω/:6 months
10~15Ω/:3months
>15Ω/:1months
 
 