6mm de espesor naval hoja de aluminio 1200 h14/3003 h32/7070/5754 almg3
Specification:
Type5005 Aluminum plate
ApplicationConductor, cooking utensils, instrument panels, pieces of the shell and architectural decoration, interior or exterior building materials, vehicle interior materials
Alloy Type5005
TemperO, H14, H16, H18, H22, H24, H26, H28, H32, H34, H36, H38,
H112, F, H111, H114
Thickness0.2 -150mm
Width500mm -2300mm
Length500-10000mm
Adopted StandardGB/T 3880-2006, EN485, ASTM B209
Application: Used in construction and decoration, hardware and electric appliances manufacture, automobile manufacture and other industrial and civil purposes, such as electronic capacitor, composite cooker, rice cooker, refrigerator, computer casting, telecommunication equipment, lamp shade, air-conditioner, cosmetics cover and box, air-conditioner radiator, inner container of disinfecting cabinet, ceiling.
5005 Properties and additional information:
>General Features
5005 is a non-heat treatable alloy with magnesium content. It can be strengthened (hardened) by cold working. It scores well in weld-ability, formability, and corrosion resistance (especially when anodized).
>Forming
5005 has excellent formability, especially in softer tempers. SAF carriers 5005 H34 temper which is slightly harder and is comparable to 5052 H32 for forming.
>Welding
5005 alloy is noted for excellent welding characteristics. When 5005 material will be welded and then anodized, SAF recommends a 5356 welding wire for best color uniformity. Weld discoloration can still occur, but it is less severe than other welding alloys.
>Machining
5005 machinability is generally fairly poor. Soft 5005 tempers machine worse than harder tempers. 5005 H34 and 5005 H38 can be machined, but with much more difficulty than many other aluminum alloys.
| chemical composition (%) |
| Si | Fe | Cu | Mn | Mg | Cr | Ni | Zn | other | Al |
5005 H34 | 0.5 | 0.5 | 0.1 | 0.3-0.6 | 4.8-5.5 | - | - | 0.2 | 0.05 | remain |
| Physical specificatiom |
| Density (kg/m3) | σ 0.2 /MPa | σ b /MPa | δ/% | HB | shearing strength /Mpa | fatigue strength /Mpa | | | |
5005 H34 | 2650 | 138 | 159 | 8 | 41 | 140-180 | 105 | | | |