China Aqueous Styrene Acrylic Polymer for Interior and Exterior Wall Paints, Find details about China Acrylic, Styrene Emulsion from Aqueous Styrene Acrylic Polymer for Interior and Exterior Wall Paints
Water based styrene acrylic emulsion----HN-996 | ||
HN-996 | Appearance | light blue liquid |
Solid content | 49±1wt% | |
Viscosity.cps(25ºC) | 500-3000 | |
Particle Size(nm) | 90-150 | |
PH | 7.0-8.0 | |
Glass Transition Temperature (Tg) | 22ºC | |
Minimum Film Formation Temperature(MFT) | 18-20ºC | |
Ca2+ stability 5%CaCl2: emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass |
Reference formula for middle and high-end interior wall latex paint | |||
Number | Raw material name | Theoretical quantity | Real quantity |
1 | Water | 410 | |
2 | dispersing agent 4100 | 6 | |
3 | wetting agent 220 | 1 | |
4 | antifoaming agents4063 | 1 | |
5 | Anatase titanium dioxide | 75 | |
6 | 1250kaolin | 70 | |
7 | 800amount talcum powder | 105 | |
8 | 800amountcoarse whiting | 200 | |
9 | cellulose ether HEC250HBR | 3.5 | |
10 | modifierAMP-95 | 1 | |
11 | coalescing agents | 5 | |
12 | glycol | 5 | |
13 | GK-102 | 110 | |
14 | preservative BIT10w | 1 | |
15 | preservative CI-15 | 1 | |
16 | antifoaming agents 4063 | 1 | |
17 | thickening agent 205 | 2 | |
18 | thickening agent 169 | 3 | |
19 | subtotal: | 1000.5 | |
HN-101 | Appearance | light blue liquid |
Solid content | 47±2wt% | |
Viscosity.cps(25ºC) | 1000-4000cps | |
Particle Size(nm) | 90-150 | |
PH | ||
Glass Transition Temperature (Tg) | 26ºC | |
Minimum Film Formation Temperature(MFT) | 22-24ºC | |
Ca2+ stability 5%CaCl2: emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass | |
HN-102 | Appearance | light blue liquid |
Solid content | 48±1wt% | |
Viscosity.cps(25ºC) | 500-3000 | |
Particle Size(nm) | 100-180 | |
PH | 7.0-8.0 | |
Glass Transition Temperature (Tg) | 24ºC | |
Minimum Film Formation Temperature(MFT) | 21-23ºC | |
Ca2+ stability 5%CaCl2: emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass | |
HN-996 | Appearance | light blue liquid |
Solid content | 49±1wt% | |
Viscosity.cps(25ºC) | 500-3000 | |
Particle Size(nm) | 90-150 | |
PH | 7.0-8.0 | |
Glass Transition Temperature (Tg) | 22ºC | |
Minimum Film Formation Temperature(MFT) | 18-20ºC | |
Ca2+ stability 5%CaCl2: emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass | |
HN-4208A | Appearance | Translucency and light blue liquid |
Solid content | 46±2wt% | |
Viscosity.cps(25ºC) | 3000-6000 | |
Particle Size(nm) | 60-100 | |
PH | 7.0-8.0 | |
Glass Transition Temperature (Tg) | 23ºC | |
Minimum Film Formation Temperature(MFT) | 22ºC | |
HN-4208 | Appearance | Translucency and light blue liquid |
Solid content | 42±1wt% | |
Viscosity.cps(25ºC) | 1000-3000 | |
Particle Size(nm) | 90-120 | |
PH | 7.0-8.0 | |
Minimum Film Formation Temperature(MFT) | 7-10ºC | |
HN-01F | Appearance | light blue liquid |
Solid content | 29±1wt% | |
Viscosity.cps(25ºC) | ≤500cps | |
Particle Size(nm) | 80-120 | |
PH | 7.5-8.5 | |
Minimum Film Formation Temperature(MFT) | 10ºC | |
HN-314T | Appearance | light blue liquid |
Solid content | 48±1wt% | |
Viscosity.cps(25ºC) | 1000-3000 | |
Particle Size(nm) | 100-500 | |
PH | 7.0-8.0 | |
Glass Transition Temperature (Tg) | -15ºC | |
Minimum Film Formation Temperature(MFT) | 0ºC | |
Ca2+ stability 5%CaCl2: emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass | |
HN-519NT | Appearance | light blue liquid |
Solid content | 48±1wt% | |
Viscosity.cps(25ºC) | 100-1000 | |
Particle Size(nm) | 90-160 | |
PH | 7.0-8.0 | |
Glass Transition Temperature (Tg) | -40ºC | |
Minimum Film Formation Temperature(MFT) | 0ºC | |
Ca2+ stability 5%CaCl2: emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass | |
HN-340T | Appearance | milk white liquid |
Solid content | 56±1wt% | |
Viscosity.cps(25ºC) | 1000-3000 | |
Particle Size(nm) | 300-400 | |
PH | 7.0-8.0 | |
Minimum Film Formation Temperature(MFT) | 0ºC | |
Ca2+ stability 5%CaCl2: emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass | |
HN-332T | Appearance | Milky white with a hint of green |
Solid content | 56±1wt% | |
Viscosity.cps(25ºC) | 1000-3000 | |
Particle Size(nm) | 200-300 | |
PH | 7.0-8.0 | |
Minimum Film Formation Temperature(MFT) | 0ºC | |
Ca2+ stability 5%CaCl2: emulsion =1:3, 48h, No Flocculation, No Stratification. | Pass |