Carbon Graphitized Carburant/Recaburizer/Lubricant Scrap Used for Steelmaking
China Carbon Graphitized Carburant/Recaburizer/Lubricant Scrap Used for Steelmaking, Find details about China Graphitized Recaburizer, Carbon Graphite Scrap from Carbon Graphitized Carburant/Recaburizer/Lubricant Scrap Used for Steelmaking
Basic Info.
Model NO.
GM-1
Density
1.58-1.75g/cm3
Resistivity
Less Than 12
Compressive Strength
More Than 70MPa
Porosity
Less Than 26%
Elasticity Modulus
6-18gpa
Thermal Expansion Coefficient
1.47-4.25
Temperature Resistance
Less Than 4350 Degree
Ash Content
Less Than 0.05%
Surface Process
Machining
Trademark
L. T graphite
Transport Package
Ton Bag
Specification
personalized customized
Origin
Cn
HS Code
3801909000
Model NO.
GM-1
Density
1.58-1.75g/cm3
Resistivity
Less Than 12
Compressive Strength
More Than 70MPa
Porosity
Less Than 26%
Elasticity Modulus
6-18gpa
Thermal Expansion Coefficient
1.47-4.25
Temperature Resistance
Less Than 4350 Degree
Ash Content
Less Than 0.05%
Surface Process
Machining
Trademark
L. T graphite
Transport Package
Ton Bag
Specification
personalized customized
Origin
Cn
HS Code
3801909000
Product Desciption
A: Company profile
As a proud subsidiary of L.T Group, L.T Graphite with four producing bases located at middle of China, Henan province, and a branch producing base at Sichuan province. L.T graphite covers the entire value chain of fine
and medium grain graphite production. From raw material selection, semi-finished product manufacture, precision machining, impregnation, purification, and coating. This is how we ensure the consistent high quality and performance of our products.
B: recarburizer
In the smelting process of iron and steel products, due to factors such as smelting time, holding time, and longer overheating time, the smelting loss of carbon in the molten iron increases, resulting in a decrease in the carbon content in the molten iron, leading to The carbon content in molten iron does not reach the theoretical value expected for refining. The carbon-containing substances added in order to make up for the carbon content lost during the steel smelting process are called recarburizers. High-quality recarburizer is an indispensable auxiliary additive for the production of high-quality steel. In addition, the additives of brake pads also use recarburizers as friction materials.
There are many kinds of raw materials for recarburizers, and the production processes are also different. There are woody carbon, coal-based carbon, coke, graphite, etc., among which there are many small types under various categories. High-quality recarburizer generally refers to a recarburizer that has undergone graphitization. Under high temperature conditions, the arrangement of carbon atoms is in the microscopic form of graphite, so it is called graphitization. Graphitization can reduce the content of impurities in the recarburizer, increase the carbon content of the recarburizer, and reduce the sulfur content.
The recarburizer is used in casting, which can greatly increase the amount of scrap steel, reduce the amount of pig iron or not use pig iron. In the feeding method of electric furnace smelting, the recarburizer should be put in with the scrap steel and other charge, and small doses can be added to the surface of the molten iron. However, it is necessary to avoid large quantities of materials into the molten iron to prevent excessive oxidation and the occurrence of insignificant recarburization effects and insufficient carbon content of the castings. The amount of recarburizer added is determined according to the ratio of other raw materials and the carbon content.
The main recarburizers of L.T graphite include: coal recarburizer, graphite recarburizer, petroleum coke recarburizer, calcined petroleum coke recarburizer, graphitized petroleum coke recarburizer. The shape of the product has various shapes such as spherical/powder/block, and products of various particle sizes. Various specifications of the products can be processed and packaged according to customer requirements!
C.Features:
1. The recarburizer has moderate particle size, large porosity, easy to melt, and fast absorption.
2. The chemical composition is pure and impurity is small, the national carbon is high, low sulfur and nitrogen, the content of harmful components is very small, and the absorption rate is high.
3. The graphite crystal structure of the product is good, which can improve the nucleation ability of the original molten iron.
4. Excellent performance and stability.
and medium grain graphite production. From raw material selection, semi-finished product manufacture, precision machining, impregnation, purification, and coating. This is how we ensure the consistent high quality and performance of our products.
B: recarburizer
In the smelting process of iron and steel products, due to factors such as smelting time, holding time, and longer overheating time, the smelting loss of carbon in the molten iron increases, resulting in a decrease in the carbon content in the molten iron, leading to The carbon content in molten iron does not reach the theoretical value expected for refining. The carbon-containing substances added in order to make up for the carbon content lost during the steel smelting process are called recarburizers. High-quality recarburizer is an indispensable auxiliary additive for the production of high-quality steel. In addition, the additives of brake pads also use recarburizers as friction materials.
There are many kinds of raw materials for recarburizers, and the production processes are also different. There are woody carbon, coal-based carbon, coke, graphite, etc., among which there are many small types under various categories. High-quality recarburizer generally refers to a recarburizer that has undergone graphitization. Under high temperature conditions, the arrangement of carbon atoms is in the microscopic form of graphite, so it is called graphitization. Graphitization can reduce the content of impurities in the recarburizer, increase the carbon content of the recarburizer, and reduce the sulfur content.
The recarburizer is used in casting, which can greatly increase the amount of scrap steel, reduce the amount of pig iron or not use pig iron. In the feeding method of electric furnace smelting, the recarburizer should be put in with the scrap steel and other charge, and small doses can be added to the surface of the molten iron. However, it is necessary to avoid large quantities of materials into the molten iron to prevent excessive oxidation and the occurrence of insignificant recarburization effects and insufficient carbon content of the castings. The amount of recarburizer added is determined according to the ratio of other raw materials and the carbon content.
The main recarburizers of L.T graphite include: coal recarburizer, graphite recarburizer, petroleum coke recarburizer, calcined petroleum coke recarburizer, graphitized petroleum coke recarburizer. The shape of the product has various shapes such as spherical/powder/block, and products of various particle sizes. Various specifications of the products can be processed and packaged according to customer requirements!
C.Features:
1. The recarburizer has moderate particle size, large porosity, easy to melt, and fast absorption.
2. The chemical composition is pure and impurity is small, the national carbon is high, low sulfur and nitrogen, the content of harmful components is very small, and the absorption rate is high.
3. The graphite crystal structure of the product is good, which can improve the nucleation ability of the original molten iron.
4. Excellent performance and stability.
You Might Also Like
Triac 0-10V Dali Dimmable Recessed LED Downlight/ COB LED Ce......
GMP Factory Supply Food Grade Phycocyanin Spirulina Extract
Table Tennis Racket with Rubber + Bag Ping Pong Bat
3mh Cool Giant Fat Inflatable Cat Cartoon for Advertising
Mslfp14 17*17 Wired Box Size X-ray Digital Flat Panel Detect......
Portable Glass Shape Edge Polishing Machine
A4 A3 Paper Wrapping Machine
Stainless Steel Angle Tube Strainer
Sinchold 9220/20/45 Forged Steel Welded Crane Rail Clips
Warehouse Tent Made by Superb Tent
Thyristor Rectified CO2 MIG Mag Arc Welding Machine