Metalized Polyester Film Capacitors Type-Mpp

China Metalized Polyester Film Capacitors Type-Mpp, Find details about China Mpp Film, Metallized Polypropylene Film from Metalized Polyester Film Capacitors Type-Mpp

Model NO.
mpp film
Processing Type
Multiple Extrusion
Thickness
3.6-12um
Width
4.5-620mm
Types of Matallized Layer
Al/Zn Metallized Film, Al Metllized Film,
Density
0.905+/-0.005 g/cm3
Margin Value
0.5mm 1mm 1.5mm 2mm 2.5mm
Trademark
CSF
Specification
ISO9001, SGS, CQC, RHoS
Origin
Anhui China
HS Code
3921909090
Model NO.
mpp film
Processing Type
Multiple Extrusion
Thickness
3.6-12um
Width
4.5-620mm
Types of Matallized Layer
Al/Zn Metallized Film, Al Metllized Film,
Density
0.905+/-0.005 g/cm3
Margin Value
0.5mm 1mm 1.5mm 2mm 2.5mm
Trademark
CSF
Specification
ISO9001, SGS, CQC, RHoS
Origin
Anhui China
HS Code
3921909090
Metalized Polyester Film Capacitors Type-MPP




Products:
1. Aluminum metallized polypropylene film.
2.Aluminum metallized polypropylene safety film.
3.Zinc - Aluminum alloy metallized polypropylene film with heavy edge.
4. Zinc - Aluminum alloy metallized polypropylene safety film with heavy edge.
5.Zinc - Aluminum alloy metallized polypropylene film with heavy edge and slope metallized film.
6.Aluminum metallized polyester film.
7.Zinc - Aluminum alloy metallized polyester film with heavy edge.
8.Zinc-Aluminum Alloy metallized polypropylene film with high ssquare resistance
9. According to customer requirement design to producing all kinds of metallized film for capacitor used.

Cores:
1.Material:Plastic.
2.Width:Film Slit Width ±0.3mm.
3.Inner Diameter:75mm +1.0mm/-0.5mm.

Roll Outer Diameter:
     Slit widths(W)Recommend outer diameter(D)
4.5mm≤W<10mm140mm≤D≤185mm
10mm≤W<25mm 150mm≤D≤185mm
25mm≤W<50mm   150mm≤D≤240mm 
50mm≤W150mm≤D≤350mm  

Specifications of metallized film:
1)Metallized polypropylene film  

Properties

Unit

Requirements
Densityg/cm30.905±0.005
 Thicknessµm3.8 ~ 15

Tensile Strength
MD
(MPa)
≥100

Elongation at Break
MD
(%)
40 ~ 200

Heat Shrinkage
MD
(%)
≤5 ( 120°C, 10min)
( 120°C , 10 min )

Break-dowm voltage
V/µm≥350 ( 23°C, DC )

Coating square resistance

Al1.5±0.52.0±0.52.5±0.53±1

Zn/Al
(heavy-edge area):3±1
(non heavy-edge area):(6~7.5)±30%
 with gradient square (heavy-edge area):3±1
(non heavy-edge area):(2~20)

Dissipation Factor
-≤4×10-4 (20ºC,1KHz )
RCΩF≥5×104

2.)Metallized polyester Film

Properties

Unit

Requirements
Densityg/cm31.34
 Thicknessµm<55~12>12

Tensile Strength
MD
(MPa)
≥84≥108≥120

Elongation at Break
MD
(%)
≥22≥33≥44

Break-dowm voltage
V/µm≥200 
( 23°C, DC )
≥250 
( 23°C, DC )

Heat Shrinkage
MD
(%)
≤3 ( 120°C, 10min)

Coating square resistance

Al1.5±0.52.0±0.52.5±0.53±1

Zn/Al
(heavy-edge area):3±1
(non heavy-edge area):(6~7.5)±30%

Dissipation Factor
-≤60×10-4 (20ºC,1KHz )
RCΩF≥1×104

Note: Coating square resistance annotation is a typical value,can be customized.

Packing:
1. Roll films are packed in vacuum plastic bag and heat-sealed with desiccants.
2.Bags are marked with lables of types
3. The bags are packed in carton cases.
4.The cartons are wrapped in wooden cases or reinforced carton.


Storge:
1. Metallized film should be stored in its original package until its use with temperature  5 ~ 35ºC and humidity less than 85%RH.
2. Metallized layer is easily oxidized when exposure to moisture. Therefore, the film should be used as soon as possible when opened. 
 
3.The recommended temperature is 15 -25ºC with humidity less than 60%RH after the package is open.
 
4.With original sealed package, and stored in the above mentioned conditions, the storage time can be as following: 
Al metalized Film: 12 months from the delivered date..
Al/Zn Alloy metalized Film: As Zn is relatively unstable, preservation period(from delivery date) depends on the resistance of the film:
≤10 Ω/: 6 months 
10 ~15Ω/: 3 months 
>15Ω/: 1months