12mm White PVC Foam Board 8mm PVC Plastic Sheet 18mm PVC Rigid/Celuka/ Forex

China 12mm White PVC Foam Board 8mm PVC Plastic Sheet 18mm PVC Rigid/Celuka/Forex, Find details about China Clear PVC, PVC Foam from 12mm White PVC Foam Board 8mm PVC Plastic Sheet 18mm PVC Rigid/Celuka/Forex

Basic Info.

Origin

China

HS Code

39209990

Origin

China

HS Code

39209990

Product Desciption

PVC foam sheet/board is becoming the substitution of wood in many fields such as AD and Decoration, It made through foaming and pressing into shape with additives, the main material is PVC resin, so it covers not only features of wood plastic, but also very light and can be printed, engraved easily.
PVC Celuka Foam Sheet is a lightweight, expanded rigid PVC foam sheet that is used for a variety of applications including signs and displays, exhibit booths, photo mounting, interior design, thermoforming, prototypes, model making, and much, much more. It can be easily sawed, stamped, punched, die cut, sanded, drilled, screwed, nailed, or riveted. It can be bonded using PVC adhesives. Its properties include excellent impact resistance, very low water absorption and high corrosion resistance.
The celular structure , smooth surface polishing and excellent features make PVC Foam Board as an ideal material for architectural decorations,also it is an ideal choice for specialized printers and billboard for signs, displays and etc. The PVC Foam Board always ensures dependable, reliable performance and excellent usage.
12mm White PVC Foam Board 8mm PVC Plastic Sheet 18mm PVC Rigid/Celuka/Forex

12mm White PVC Foam Board 8mm PVC Plastic Sheet 18mm PVC Rigid/Celuka/Forex

Width	Standard size	Thickness	Density	Color	MOQ
1.22M	1.22M ×2.44M	1-40MM	0.36-0.75g/m3	White	1ton
0.625M	0.625M ×2.44M	1-40MM	0.36-0.75g/m3	White	1ton
1.56M	1.56M×3.05M	1-40MM	0.36-0.75g/m3	White	1ton
2.05M	2.05M×3.05M	1-40MM	0.36-0.75g/m3	White	1ton

Bulk Density	0.36-1.0g/cm3	Dimensional Stability	±2%
Shore Hardness	30-85D	Water Absorption	<1%
Tensile Strength	12-20Mpa	Flexural Strength	12-18Mpa
Elongation At Break	15-20%	Flexural Modulus	800-900Mpa
Impact Strength	8-15KJ/m2	Screw Holding Strength	>800N
Vicat Softening Temperature	73-76ºC	Heating Dimensional Variation Ratio	2%
Hydroscopicity	≤1%	Fire Resistance	self-extinguish
			within 5 s