INCOLOY800H/HT is an austenitic heat-resistant alloy widely used in high-temperature pressure-bearing structural parts. The high strength of 800H/HT is mainly due to the addition of carbon, aluminum, and titanium elements, and it is annealed at a minimum temperature of 1149ºC to achieve The grain size is ASTM5 grade or coarser.

Similar Grades:
GB/T NS112   UNS N08810       W.Nr  1.4876

The chemical composition of Incoloy 800H:

Alloy    %            Nickel   Chromium   Iron   Carbon Manganese Silicon Copper Sulfur Aluminum Titanium
800 minimum      30              19                                                                                            0.15         0.15
      Maximum      35              23        margin    0.10          1.5           1          0.75   0.015     0.60         0.60

800H minimum   30              19                       0.05                                                               0.15        0.15
          Maximum 35               23        margin    0.10          1.5           1          0.75   0.015      0.60        0.60

800HT minimum 30             19                       0.06                                                                0.15        0.15
          Maximum  35             23       margin     0.10           1.5           1          0.75   0.015      0.60        0.60

Aluminum + titanium is 0.85-1.20

Physical properties of Incoloy 800H:

Density 8.0 g/cm3

Melting point 1350-1400 ºC

Incoloy 800H solid solution state, the mechanical properties of the alloy at room temperature:





,