Cheap Annealed 1Cr13 410/410s Stainless Steel Coil for Valve

China Cheap Annealed 1Cr13 410/410s Stainless Steel Coil for Valve, Find details about China 410 Stainless Steel Price, 410 Stainless Steel Coil from Cheap Annealed 1Cr13 410/410s Stainless Steel Coil for Valve

Basic Info.

Model NO.

410/410S

Surface Treatment

2b/Ba/No.4/Hl/8K/No.1

Finish

2b/No.1/1d/2D/Ba/Sb/Hl/No.4/No.8

Color

Customized

Edge

Mill Edge/Slit Edge

Mtc

En 10204/3.1

MOQ

5 Ton

Trade Terms

Fob CIF CFR EXW etc

Stock

in Stock

Keyword

GB 410 Stainless Steel

Trademark

ZYTC

Transport Package

Wooden Package

Specification

0.3~6mm

Origin

China

HS Code

7219900000

Model NO.

410/410S

Surface Treatment

2b/Ba/No.4/Hl/8K/No.1

Finish

2b/No.1/1d/2D/Ba/Sb/Hl/No.4/No.8

Color

Customized

Edge

Mill Edge/Slit Edge

Mtc

En 10204/3.1

MOQ

5 Ton

Trade Terms

Fob CIF CFR EXW etc

Stock

in Stock

Keyword

GB 410 Stainless Steel

Trademark

ZYTC

Transport Package

Wooden Package

Specification

0.3~6mm

Origin

China

HS Code

7219900000

Product Desciption

Cheap Annealed 1Cr13 410/410s Stainless Steel Coil for Valve

Product Name	Annealed Hard 410/410S Stainless Steel Coil for Valve
Thickness	0.3mm-16mm
Width	1000mm-2000mm
Length	2000 mm , 2438 mm , 3000 mm , 6000 mm OR as reqirement
Finish	No.1 , 2B , HL , NO.4 , BA , SB ,1D , 2D , 2C , 2E , NO.5 , NO.9
Technical	Hot rolled,Cold rolled
Standard	ASTM 240 , A480 , JIS G 4304 , EN 10088-2
MOQ	5 ton
Certification	MTC Type 3.1 , PMI , CO
Delivery Time	7 days if have stock

What is 410/410S Stainlesss Steel?

Grade 410 stainless steels are general-purpose martensitic stainless steels containing 11.5% chromium, which provide good corrosion resistance properties. However, the corrosion resistance of grade 410 steels can be further enhanced by a series of processes such as hardening, tempering and polishing. Quenching and tempering can harden grade 410 steels. They are generally used for applications involving mild corrosion, heat resistance and high strength.

410S Stainless Steel is a non-hardening modification of Type 410. Control of the chemistry balance (low carbon and optional additions of Ti or Nb) minimizes austenite formation at high temperatures, restricting the alloy's ability to harden. The material remains soft and ductile even when the material is rapidly cooled from above the critical temperature. This low hardening characteristic helps to prevent cracking when the steel is welded or exposed to high temperatures.

Stainless steel grade and chemical composition(%)

Grade	C	Si	Mn	P≤	S≤	Cr	Ni	Mo	N
201	≤0.15	≤1.00	5.5-7.5	0.06	0.03	16-18	3.5-5.5	----	≤0.25
202	≤0.15	≤1.00	7.5-10.0	0.06	0.03	17-19	4-6	----	≤0.25
301	≤0.15	≤1.00	≤2.00	0.045	0.03	16-18	6-8	----	≤0.10
304	≤0.08	≤1.00	≤2.00	0.045	0.03	18-20	8-10.5	----	----
304L	≤0.03	≤1.00	≤2.00	0.045	0.03	18-20	8-12	----	----
309	≤0.2	≤1.00	≤2.00	0.045	0.03	22-24	12-15	----	----
309S	≤0.08	≤1.00	≤2.00	0.045	0.03	22-24	12-15	----	----
310	≤0.25	≤1.00	≤2.00	0.045	0.03	24-26	19-22	----	----
310S	≤0.08	≤1.00	≤2.00	0.045	0.03	24-26	19-22	----	----
316	≤0.08	≤1.00	≤2.00	0.045	0.03	16-18	10-14	2-3	----
316L	≤0.03	≤1.00	≤2.00	0.045	0.03	16-18	10-14	2-3	----
316H	0.04-0.1	≤1.00	≤2.00	0.045	0.03	16-18	10-14	2-3	----
316Ti	≤0.08	≤1.00	≤2.00	0.045	0.03	16-18	10-14	2-3	≤0.10
317	≤0.08	≤1.00	≤2.00	0.045	0.03	18-20	11-15	3-4	----
317L	≤0.03	≤1.00	≤2.00	0.045	0.03	18-20	11-15	3-4	----
321	≤0.08	≤1.00	≤2.00	0.045	0.03	17-19	9-12	----	≤0.10
321H	0.04-0.1	≤1.00	≤2.00	0.045	0.03	17-19	9-12	----	≤0.10
409	≤0.08	≤1.00	≤1.00	0.045	0.03	10.5-11.7	≤0.50	----	----
410	≤0.15	≤1.00	≤1.00	0.04	0.03	11.5-13.5	( ≤0.75)	----	----
420	≥0.15	≤1.00	≤1.00	0.04	0.03	12-14	----	----	----
430	≤0.12	≤1.00	≤1.00	0.04	0.03	16-18	----	----	----