1.4462 S31803 329 Stainless Steel Sheet SUS329j2l

China 1.4462 S31803 329 Stainless Steel Sheet SUS329j2l, Find details about China Steel Pipe, Steel Plate from 1.4462 S31803 329 Stainless Steel Sheet SUS329j2l

Model NO.
329
Special Use
Wear Resistant Steel
Stock
Stock
Ts (MPa)
>520
Elongation Stress (MPa)
205
Elongation
40
Eduction of Area
60
Melting Point
1380
Certificate
SGS ISO
Delivery Time
Within 15working Days
Trademark
Taixie
Transport Package
Woven Bag, Wooden Box
Specification
from 5mm--100mm
Origin
Wuxi, Jiangsu
HS Code
72222000
Model NO.
329
Special Use
Wear Resistant Steel
Stock
Stock
Ts (MPa)
>520
Elongation Stress (MPa)
205
Elongation
40
Eduction of Area
60
Melting Point
1380
Certificate
SGS ISO
Delivery Time
Within 15working Days
Trademark
Taixie
Transport Package
Woven Bag, Wooden Box
Specification
from 5mm--100mm
Origin
Wuxi, Jiangsu
HS Code
72222000
1.4462 S31803 329 Stainless Steel Sheet SUS329j2l
EN 1.4462 - 329 is a high alloy austenitic stainless steel with low carbon content. The grade is intended for use under severe corrosive conditions. The steel grade was originally developed to resist corrosion in dilute sulphuric acid. EN 1.4462 is fully austenitic, and is less sensitive to precipitation of ferrite and sigma phase than conventional austenitic grades with high molybdenum content. Due to the combination of relatively high contents of chromium, nickel, molybdenum and copper,   EN 1.4462 has good resistance to general corrosion, particulary in dilute sulphuric acid.  It is non-magnetic in the annealed condition but may become slightly magnetic as a result of cold-working or welding.
Design features  
⇒ Good resistance to uniform corrosion
⇒ Good resistance to pitting and crevice corrosion  
⇒ Very good resistance to stress corrosion cracking
⇒ Good resistance to intercrystalline corrosion
⇒ Good formability and weldability
Corrosion resistance  
Uniform corrosion Uniform corrosion is characterized by a uniform corrosion of the steel surface in contact with the corrosive medium. Resistance is normally considered good if the corrosion rate is less than 0,1 mm/year. As a result of its high chromium, nickel and molybdenum contents and its alloying with copper, EN 1.4462 is passivated even in reducing environments such as dilute sulphuric acid and formic acid. Its high nickel content contributes towards its relatively low corrosion rate in the active state.  
Intercrystalline corrosion  
EN 1.4462 has a very low carbon content. This means that there is very little risk of carbide precipitation in connection with ordinary heat treatment and welding. The risk of intercrystalline corrosion after ordinary heat treatment and welding is thereby eliminated.

1.4462 S31803 329 Stainless Steel Sheet SUS329j2l1.4462 S31803 329 Stainless Steel Sheet SUS329j2l
1.4462 S31803 329 Stainless Steel Sheet SUS329j2l1.4462 S31803 329 Stainless Steel Sheet SUS329j2l1.4462 S31803 329 Stainless Steel Sheet SUS329j2l