Alloy Steel Casting Investment Casting Leaf Spiral China Supplier with Explosive Popularity for Cement Industry, Find details about China Steel Roller, Stainless Steel Roller from Alloy Steel Casting Investment Casting Leaf Spiral China Supplier with Explosive Popularity for Cement Industry
| NO. | Chemical composition%% | Max temperatureºC | Yield Strength | Elongation%% | ||||||||||
| C | Mn | Si | Cr | Ni | P | S | Mo | W | N | |||||
| ZG30Cr24Ni7NRe | 0.32 | < | 1.3 | 23 | 7 | < | < | 0.22 | 1100 | |||||
| - | = | - | - | - | = | = | - | |||||||
| 0.42 | 2 | 2 | 25 | 8.5 | 0.035 | 0 | 0.3 | |||||||
| ZG40Cr25Ni35Mo | 0.35 | 1 | 1 | 24 | 34 | < | < | 1150 | 196 | 8 | ||||
| - | - | - | - | - | = | = | -20 | |||||||
| 0.45 | 2 | 1.8 | 27 | 36 | 0.04 | 0 | ||||||||
| ZG10Cr18Ni9Ti | < | 0.8 | < | 17 | 8 | < | < | 850 | ||||||
| = | - | = | - | - | = | = | ||||||||
| 0.12 | 2 | 1.5 | 20 | 11 | 0.04 | 0 | ||||||||
| ZG40Cr25Ni20Si2 | 0.35 | 1 | 1 | 23 | 19 | < | < | 1150 | 225.4 | 12 | 10 | |||
| - | - | - | - | - | = | = | -23 | |||||||
| 0.45 | 2 | 1.8 | 26 | 22 | 0.04 | 0 | ||||||||
| ZG40Cr28Ni48W5 | 0.4 | 1 | 1 | 27 | 47 | < | < | 4 | 1200 | 196 | 4 | |||
| - | - | = | - | - | = | = | - | -20 | ||||||
| 0.5 | 2 | 1.8 | 29 | 49 | 0.04 | 0 | 5.5 | |||||||
| ZG10Cr20Ni14Si2 | 0.35 | 1 | 1 | 19 | 13 | < | < | 900 | 240 | 25 | 10 | |||
| - | - | - | - | - | = | = | -24.5 | |||||||
| 0.45 | 2 | 1.8 | 21 | 15 | 0.04 | 0 | ||||||||
| ZG10Cr15Ni36W3Ti | < | 1 | < | 14 | 34 | < | < | 2.8 | 1 | 1160 | 40 | 15 | ||
| = | - | = | - | - | = | = | - | - | ||||||
| 0.12 | 2 | 0.8 | 16 | 38 | 0.035 | 0 | 3.2 | 1.4 | ||||||
| 10Cr18Ni9Ti | < | < | < | 17 | 8 | < | < | 55 | 40 | |||||
| = | = | = | - | - | = | = | ||||||||
| 0.12 | 2 | 1 | 19 | 11 | 0.035 | 0 | ||||||||
| 10Cr25Ni20Si2 | < | < | 1.5 | 24 | 18 | < | < | 60 | 35 | |||||
| = | = | - | - | - | = | = | ||||||||
| 0.2 | 1.5 | 2.5 | 27 | 21 | 0.035 | 0 | ||||||||
| 10Cr20Ni14Si2 | < | < | 1.5 | 19 | 12 | < | < | 60 | 35 | |||||
| = | = | = | - | - | = | = | ||||||||
| 0.2 | 1.5 | 2.5 | 22 | 15 | 0.035 | 0 | ||||||||