China Incoloy Uns N08810 Alloy Incoloy 800h 1.4958 Nickel Based Alloy Seamless Pipe, Find details about China Incoloy 800h, Stainless Steel Pipe from Incoloy Uns N08810 Alloy Incoloy 800h 1.4958 Nickel Based Alloy Seamless Pipe
Product Details | |
Product name | UNS N08810 Incoloy Alloy Incoloy 800H 1.4958 Nickel Based Alloy Seamless Pipe |
Brand name | ABOOM |
Standard | ASTM A312, ASTM A554, ASTM A790, EN10216-5, EN10217-7, JIS G3468, JIS G3459 |
Material | N08367 Al-6XN 1.4501 Incoloy25-6hn NAS 255NM |
Surface | Pickling, 400grit polishing, 600grit polishing, mirror finish |
Certificate | BV, LR, GL, NK, RMRS |
Packing | In bundles with waterproof material, in wooden cases |
Shipment | By sea, by air, by express |
Material designation: Incoloy 800H nickel based alloy
German grade: X2NiCrAlTi3220
US grade: NO8810
Incoloy 800H (NO8810) nickel-based alloy applications:
Incoloy 800H (NO8810) alloy chemical industry, nuclear generator, acetic anhydride cracking tube, heat exchange equipment, heat exchange tube, etc.
Incoloy 800H (NO8810) nickel-based alloy mechanical properties: see Table-1:
Table-1
Temp ºC | σЬ/ MPa | σ0.2 / MPa | δ5 /% |
100 | 425 | 140 | 160 |
300 | 390 | 95 | 115 |
500 | 360 | 80 | 100 |
600 | 300 | 75 | 95 |
Incoloy 800H (NO8810) nickel-based alloy melting temperature range: 1350 ~ 1400 ° C.
Incoloy 800H (NO8810) nickel-based alloy specific heat capacity: 455J / (kg · ºC).
Incoloy 800H (NO8810) nickel-based alloy density: 8.0 g / cm3.
Incoloy 800H (NO8810) nickel-based alloy Magnetic: None.
Incoloy 800H (NO8810) alloy hot working:
(1) The temperature range is 1200 ºC ~ 950 ºC. The cooling method is water quenching or rapid air cooling.
(2) In order to obtain the best performance and creep resistance, a solution treatment should be performed after hot working.
(3) The material can be directly fed into a furnace that has been heated up to 1200 ° C, and it can be quickly released after holding for a sufficient time, and thermal processing is performed within a specified temperature range. When the material temperature drops below the hot working temperature, reheating is required.
specification:
Outer diameter Φ6-762mm; wall thickness: 0.5-50mm, maximum length 18000mm
Special specifications are available upon negotiation.
2.
Chemical Composition(%) | |||||||||||
Grade | C | Si | Mn | P | S | Cr | Ni | Mo | N | Cu | |
201 | ≤0.15 | ≤0.75 | 5.5~7.5 | ≤0.060 | ≤0.03 | 16.00~18.00 | 3.5~5.5 | - | - | 0.08 | 1.5 |
202 | ≤0.15 | ≤1.00 | 7.5~10.00 | ≤0.060 | ≤0.03 | 17.00~19.00 | 4.0~6.0 | - | ≤0.25 | ||
301 | ≤0.15 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 16.00~18.00 | 6.00~8.00 | - | |||
302 | ≤0.15 | ≤1.00 | ≤2.00 | ≤0.035 | ≤0.03 | 17.00~19.00 | 8.00~10.00 | - | |||
304 | ≤0.07 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 18.00~20.00 | 8.00~10.50 | - | |||
304L | ≤0.030 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 18.00~20.00 | 9.00~13.00 | - | |||
310S | ≤0.08 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 24.00~26.00 | 19.00~22.00 | - | |||
316 | ≤0.08 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 16.00~18.00 | 10.00~14.00 | 2.00~3.00 | |||
316L | ≤0.03 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 16.00~18.00 | 12.00~15.00 | 2.00~3.00 | |||
321 | ≤0.08 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 17.00~19.00 | 9.00~13.00 | - | |||
430 | ≤0.12 | ≤0.75 | ≤1.00 | ≤0.040 | ≤0.03 | 16.00~18.00 | - | ||||
2205 | ≤0.03 | ≤1.00 | ≤2.00 | ≤0.030 | ≤0.015 | 22.00~23.00 | 4.5~6.5 | 2.5~3.5 | |||
2507 | ≤0.03 | ≤0.08 | ≤1.20 | ≤0.035 | ≤0.015 | 24.00~26.00 | 6.00~8.00 | 3.0~5.0 | |||
904L | ≤0.02 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.035 | 19.00~23.00 | 23.00~28.00 | 4.0~5.0 | 1.0~2.0 | ||
INCONEL 028 | ≤0.03 | ≤1.00 | ≤2.50 | ≤0.030 | ≤0.030 | ≤28.0 | ≤34.0 | ≤4.0 | ≤1.4 | ||
MONEL 400 | ≤0.30 | ≤0.5 | ≤2.00 | - | ≤0.024 | - | ≥63.0 | - | ≤34.0 | ||
INCONEL 800 | ≤0.10 | ≤1.00 | ≤1.50 | - | ≤0.015 | ≤23.0 | ≤35 | 4.0~5.0 | - | ≤0.75 | Ti≤0.6 Al≤0.6 |
Packaging Detail | Each tube is loaded into plastic bag individual, and then several pieces were wrapped in one bundle |
Delivery Time | 30 days |