63HRC Bimetallic Ground Engaging Tools Wear Buttons

China 63HRC Bimetallic Ground Engaging Tools Wear Buttons, Find details about China Bimetallic Wear Buttons, 63HRC Wear Buttons from 63HRC Bimetallic Ground Engaging Tools Wear Buttons

Model NO.
CB25. CB40, CB50, CB65, CB80, CB90, CB100, CB130.
Materials
White Iron + Mild Steel
Hardness
63HRC
Technology
Vacuum Brazing
Trademark
Hyster, OEM, Domite, Duablock, vidablock
Transport Package
Oli Film, Poly-Wood Crate, Pallets
Specification
High Grade
Origin
China Hunan
HS Code
84314991
Model NO.
CB25. CB40, CB50, CB65, CB80, CB90, CB100, CB130.
Materials
White Iron + Mild Steel
Hardness
63HRC
Technology
Vacuum Brazing
Trademark
Hyster, OEM, Domite, Duablock, vidablock
Transport Package
Oli Film, Poly-Wood Crate, Pallets
Specification
High Grade
Origin
China Hunan
HS Code
84314991
Bimetallic Wear Buttons

Laminated white iron Wear buttons are unique wear resistant materials in that they combine very high wear resistant qualities of a high chrome cast iron (15/3CrMo, 700 BHN - 63 HRC) with a weldable & high impact toughness mild steel through a metallurgical bond to create a product that is exceptionally resistant to impact and abrasion while retaining.


Very easy to use, no pre or post heating when welding. Available in diameters from 60mm up to 150mm. Develop your own layout and pattern to suit your particular wear protection solution.

Dome&Flat Shaped Round: Perfect solution for ground engaging applications as on adaptor teech, shovels, buckets, heavy earth moving equipment etc. Can well use them in conjunction with Chocky Bars, Wear Plates or individually to provide protection or security under the toughest impact and wear abrasion circumstances.

Types:

ITEM
SIZE(mm)Net weight(kg)
WB6060x270.7
WB7575x270.8
WB9090x271.4
WB110110x322.1
WB115115x322.5
WB150150x415.7

>Material,
ASTM A532 15/3 CrMo white iron casting , chemical composition ( percentage )

C
CrMoSiMnNiCuPS
2.0-3.314-18≤ 3.0≤ 1.5≤ 2.0≤ 2.5≤ 1.2≤ 0.1≤ 0.06

 
Q235 mild steel backing , chemical composition ( percentage )

C
SiMnPSCrNiMoCu
0.20.351.40.0450.050.30.30.30.3

 
>Mechanical Property,
-Minimum Hardness, 700 HBN / 63 HRC
-Minimum Tensile Strength, 630Mpa.
-Minimum Shearing Strength, 250Mpa.