Wear Resistance High Flame Retardent Heat Shrink Tubing for Auto Hoses and Wires
China Wear Resistance High Flame Retardent Heat Shrink Tubing for Auto Hoses and Wires, Find details about China Abrasion Resistant Fabric Tubing, Wear-Resisting Shrink Tubing from Wear Resistance High Flame Retardent Heat Shrink Tubing for Auto Hoses and Wires
Basic Info.
Model NO.
CL-KSD
Specification
6-100mm
Origin
Changzhou
Model NO.
CL-KSD
Specification
6-100mm
Origin
Changzhou
Product Desciption
Material(s) Description
Warp material: Polyester
Weft material: Irradiated, modified polyolefin
Coating: Modified polyolefin
Operating temperature range (3000 hours): -40°C to 125°C
Operating temperature range (1000 hours): -40°C to 150°C
Minimum recovery temperature: 110°C
Recommended recovery temperature :150°C to 200°C
Maximum storage temperature: 50°C
Standard:TL52668 TL52361 D44 1959 GMW14327
Testing organization:CTI PONY
| Product description (CL-KSD) | Inside diameter (mm) | |
| D (min.) expanded as supplied | d (max.) recovered after heating | |
| φ6/3-B | 6 | 3 |
| φ8/4-B | 8 | 4 |
| φ10/5-B | 10 | 5 |
| φ12/6-B | 12 | 6 |
| φ16/8-B | 16 | 8 |
| φ20/10-B | 20 | 10 |
| φ25/12-B | 25 | 12 |
| φ30/15-B | 30 | 15 |
| φ35/17.5-B | 35 | 17.5 |
| φ40/20-B | 40 | 20 |
| φ50/25-B | 50 | 25 |
| φ60/30-B | 60 | 30 |
| φ70/35-B | 70 | 35 |
| φ80/40-B | 80 | 40 |
| φ100/50-B | 100 | 50 |
| B:black | ||
| Other specifications can be customized | ||
| Property | Test condition(s) | Performance |
| Thermal ageing | 168 hrs at 125°C | No deterioration in abrasion resistance at 23°C |
| 24 hrs at 125°C | No deterioration in abrasion resistance at 23°C | |
| Flammability | MVSS 302 | Burning rate≤100 mm/min |
| Low temperature flexibility | 4 hours at -40°C,10X diameter mandrel | No cracking |
| Abrasion resistance (1.5N load, 0.3mm radius metal blade,60 cpm,50mm stroke, 144 000 cycles) | Environmental Chamber Temperature: -35°C | No wear to underlying rubber hose |
| Environmental Chamber Temperature: 140ºC | ||
| Temperature resistance 1) Test temperature 140 ºC, for 500 hours 2) Remove the sample and cool it to room temperature..Then place the sample at -35°C for 22 hours. 3) Then bend the sample 180 degrees around a cylinder with a radius of 30mm | Test temperature 140 ºC, for 500 hours | The protection tube is not damaged Standard: TL52668 |
You Might Also Like
Triac 0-10V Dali Dimmable Recessed LED Downlight/ COB LED Ce......
GMP Factory Supply Food Grade Phycocyanin Spirulina Extract
Table Tennis Racket with Rubber + Bag Ping Pong Bat
3mh Cool Giant Fat Inflatable Cat Cartoon for Advertising
Mslfp14 17*17 Wired Box Size X-ray Digital Flat Panel Detect......
Portable Glass Shape Edge Polishing Machine
A4 A3 Paper Wrapping Machine
Stainless Steel Angle Tube Strainer
Sinchold 9220/20/45 Forged Steel Welded Crane Rail Clips
Warehouse Tent Made by Superb Tent
Thyristor Rectified CO2 MIG Mag Arc Welding Machine