China Plastics Raw Material PA6 GF15 Manufacturer for Auto Parts Factory, Find details about China Fr530 Nc010, Fr530 from Plastics Raw Material PA6 GF15 Manufacturer for Auto Parts Factory
Density | g/cm3 | ISO 1183 | 1.24 | |
Filler content | % | ISO 1172 | GF15 | |
Mold shrinkage | % | ISO 294 | Parallel | 0.4 |
Vertical | 0.9 |
Tensile strength | MPa | ISO 527 | I type sample 50mm/min | 125 |
Elongation at break | % | ISO 527 | I type sample 50mm/min Gauge length 50mm | 3.5 |
Flexural strength | MPa | ISO 178 | 23ºC 10mm/min | 160 |
Flexural modulus | MPa | ISO 178 | 23ºC 10mm/min | 5100 |
Izod impact strength(notched) | KJ/m2 | ISO 180 | 23ºC | 7 |
Charpy impact strength(unnotched) | KJ/m2 | ISO 179 | 23ºC | 55 |
Melting point | ºC | ISO 11357-1 | 220 | |
HDT | ºC | ISO 75 | 0.45MPA | 210 |
1.8MPA | 190 |
UL Flammability | Class | UL-94 | HB | |
GWIT | IEC60695-2-13 | - |
Overview:
Rynite thermoplastic polyester resins are typically used in demanding applications in the automotive, electrical and electronics, appliances where they successfully replace metals and thermosets, as well as other thermoplastic polymers.
Common features of Rynite thermoplastic polyester include mechanical and physical properties such as excellent balance of strength and stiffness, dimensional stability, creep resistance, heat resistance, high surface gloss and good inherent electrical properties at elevated temperature. It can be processed over a broad temperature range and has excellent flow properties.