2218 2618 2618A Aluminum Forgings Forged Product Parts
China 2218 2618 2618A Aluminum Forgings Forged Product Parts, Find details about China 2218 2618 2618A Aluminum Forgings, Aluminum Forgings Manufacturers from 2218 2618 2618A Aluminum Forgings Forged Product Parts
Basic Info.
Model NO.
2218 2618 2618A
Surface Treatment
Zinc/Chrome Plating, Anodizing
Forging Tolerance
+/-0.2mm
Standard
ANSI
Certification
CE, ISO 9001:2008
Service
OEM ODM
Trademark
Chalco Aluminum
Transport Package
Export Standard Wooden Pallet or as Your Requsts
Specification
According to Customer Requirement
Origin
Henan China
HS Code
7218100000
Model NO.
2218 2618 2618A
Surface Treatment
Zinc/Chrome Plating, Anodizing
Forging Tolerance
+/-0.2mm
Standard
ANSI
Certification
CE, ISO 9001:2008
Service
OEM ODM
Trademark
Chalco Aluminum
Transport Package
Export Standard Wooden Pallet or as Your Requsts
Specification
According to Customer Requirement
Origin
Henan China
HS Code
7218100000
Product Desciption
2218 is suitable for forging piston of aircraft engine and diesel engine, cylinder head of aircraft engine, impeller of jet engine and compressor ring.
2618 is a kind of heat-resistant and deformed aluminium alloy which can be strengthened by heat treatment. Its working temperature can be up to 250 ºC. It is used to manufacture long-term working supersonic aircraft structural parts, such as fuselage and wing skin frame, tail wing, parts and components of low-speed aircraft whose working temperature is not higher than 150 ºC, and parts of jet engine whose working temperature is not higher than 250 ºC.
2618A is an Al-Cu-Mg-Fe-Ni series heat-resistant forging aluminium alloy, which can be strengthened by heat treatment. The chemical composition of the alloy is similar to that of 2A70 alloy, and its properties are similar to that of 2A70 alloy. It has high heat resistance and good cold and hot working performance. The corrosion resistance of the alloy is obviously improved after solution treatment and artificial aging, but there is a tendency of intergranular corrosion. Its weldability is medium and its machinability is good.
2618A aluminium alloy is used to manufacture piston of internal combustion engine and complex forgings working at 200-250 ºC, such as compressor impeller, blower impeller, tire mould, high temperature working parts of aircraft engine, etc.
The Brinell hardness of 2618A alloy forgings is 115HBW under T61 condition.
When 2618A aluminium alloy is treated by solid solution heat treatment, the heating temperature of solid solution should be strictly controlled. When the temperature reaches the upper limit, the grain size of aluminium alloy will grow easily, and it is close to the dangerous temperature of overheating of aluminium alloy.
The temperature of the cooling medium has an effect on the mechanical properties and hardness of the alloy, and the water temperature should not be higher than 40 ºC during quenching.
2618A aluminium alloy has good technological plasticity under reheating condition. It can be used to manufacture various free forgings and die forgings by hammer forging and hydraulic press. Forging temperature is 450-350 ºC.
2618 is a kind of heat-resistant and deformed aluminium alloy which can be strengthened by heat treatment. Its working temperature can be up to 250 ºC. It is used to manufacture long-term working supersonic aircraft structural parts, such as fuselage and wing skin frame, tail wing, parts and components of low-speed aircraft whose working temperature is not higher than 150 ºC, and parts of jet engine whose working temperature is not higher than 250 ºC.
2618A is an Al-Cu-Mg-Fe-Ni series heat-resistant forging aluminium alloy, which can be strengthened by heat treatment. The chemical composition of the alloy is similar to that of 2A70 alloy, and its properties are similar to that of 2A70 alloy. It has high heat resistance and good cold and hot working performance. The corrosion resistance of the alloy is obviously improved after solution treatment and artificial aging, but there is a tendency of intergranular corrosion. Its weldability is medium and its machinability is good.
2618A aluminium alloy is used to manufacture piston of internal combustion engine and complex forgings working at 200-250 ºC, such as compressor impeller, blower impeller, tire mould, high temperature working parts of aircraft engine, etc.
The Brinell hardness of 2618A alloy forgings is 115HBW under T61 condition.
| Chemical Composition of 2218 2618 2618A | |||||||||||||
| Alloy | Si | Fe | Cu | Mn | Mg | Cr | Ni | Zn | Ti | Zr | Others | Al | |
| Each | Total | ||||||||||||
| 2218 | 0.9 | 1.0 | 3.5~4.5 | 0.2 | 0.2~1.8 | 0.1 | 1.7~2.3 | 0.25 | ~ | ~ | 0.05 | 0.15 | Rest |
| 2618A | 0.15~0.25 | 0.9~1.4 | 1.8~2.7 | 0.25 | 1.2~1.8 | ~ | 0.8~1.4 | 0.15 | 0.20 | ~ | 0.05 | 0.15 | Rest |
| 2618 | 0.10~0.25 | 0.9~1.4 | 1.8~2.7 | 0.25 | 1.2~1.8 | ~ | 0.8~1.4 | 0.15 | 0.2 | ~ | 0.05 | 0.15 | Rest |
| Room Temperature Tensile Properties of 2618A Aluminum Alloy Forgings in T61 State | |||||
| Type | Specs/mm | Direction | Tension strength Rm/MPa | Prescribed plastic elongation strength Rp0.2/MPa | Elongation A (%) |
| Die forgings | Thickness≤100 | 400 | 310 | 4 | |
| 380 | 290 | 4 | |||
| Flat forging | ≤50 | Portrait | 400 | 325 | 7 |
| Long transverse | 380 | 290 | 5 | ||
| Short transverse | 360 | 290 | 4 | ||
| 51-76 | Portrait | 400 | 315 | 7 | |
| Long transverse | 380 | 290 | 5 | ||
| Short transverse | 360 | 290 | 4 | ||
| 77--100 | Portrait | 385 | 310 | 7 | |
| Long transverse | 365 | 275 | 5 | ||
| Short transverse | 350 | 270 | 4 | ||
| Rolling ring | Thickness≤63 | Tangential direction | 380 | 285 | 6 |
| Axial direction | 380 | 285 | 5 | ||
When 2618A aluminium alloy is treated by solid solution heat treatment, the heating temperature of solid solution should be strictly controlled. When the temperature reaches the upper limit, the grain size of aluminium alloy will grow easily, and it is close to the dangerous temperature of overheating of aluminium alloy.
The temperature of the cooling medium has an effect on the mechanical properties and hardness of the alloy, and the water temperature should not be higher than 40 ºC during quenching.
2618A aluminium alloy has good technological plasticity under reheating condition. It can be used to manufacture various free forgings and die forgings by hammer forging and hydraulic press. Forging temperature is 450-350 ºC.
| Type | Alloy | Projected area(m2)Or weight(kg) | Temper | Standard |
| Free forgings | 5 series | ≤3000kg | O,F | GBn223 ASTMB247 |
| 2,6,7 series | ≤3000kg | T6,T4,O,F | ||
| Mould forgings | 5 series | ≤2.5m2 | O,F | |
| 2,6,7 series | ≤2.5m2 | T6,T4,O,F |
You Might Also Like
Handwork Polyurea Protective Material Th -701
Gasoline Hand Held Concrete Finishing Machine Mini Power Tro......
10A An87330 Three Phase Power Analyzer
3.5" eSATA HDD External Enclosure
Food Grade 304 Stainless Steel Vacuum Flask Thermal Insulati......
CE-Approval! ! ! China DT638B Hades Down Type Dental Chair
Chinese Supplier 10dt Medium Copper Wire Drawing Equipment w......
Proximal Humeral Locking Plate, Small Fragment Plates, Titan......
Industrial Parts Usi Type Seal for Piston and Piston Rod
Long Life Miniature Micro Switch Used in Phone and Designs
N210106267AA Cover