We are professional Incoloy 901 forged rings, Incoloy 901 forging rings, Incoloy901 forged/forging rings, Incoloy 901 rolled rings, alloy 901, alloy901 forged/forging rings, UNS N09901 forged/forging rings, 1.4898 forging/forged rings factory from china
We could produce Incoloy 901, UNS N09901, 1.4898 forged/forging rings with diameters ranging from 100MM to 6000MM and with weights from 10KGS to 15000KGS
We have 1 tons, 3 tons, 6 tons, 9 tons forging hammer and 4500 tons hydraulic press, and 3 metres and 6 metre seamless rolled rings machine
Our Incoloy 901, UNS N09901, 1.4898 forged/forging rings could be 100% Ultrasonic Inspection as per the forging parts UT Test standard of ASTM A 388 or EN10228.
We could supply Incoloy 901, UNS N09901, 1.4898 forging steel material certificate as per the standard of EN10204-3.1 or EN10204-3.2 of third party
Our Incoloy 901, UNS N09901, 1.4898 forged/forging rings are widely used in chemical pump, centrifugal pumps, ball valves, check valves, heat exchangers and pressure vessels. Stripper columns, separators, splitter, columns, hydro treaters, hydro crackers, desalters. In Cement industry and sugar industry, shipping building and Aviation, drilling stations, pipelines and refineries, in power generation and power plants. In oil & gas industry. Concrete mills and mixers, processing units, mechanical equipment, crystalizer equipment and so on
Any inquiry of Incoloy 901, UNS N09901, 1.4898 forged/forging rings, please feel free to contact us. We are glad to quote the best price for every clients
Chemical composition:
Alloy |
% |
Ni |
Cu |
Al |
Fe |
Ti |
Co |
Mn |
S |
C |
Si |
P |
Cr |
Mo |
B |
N09901 |
Min. |
40.0 |
|
|
Balance |
2.35 |
|
|
|
|
|
|
11.0 |
5.0 |
0.01 |
Max. |
45.0 |
0.50 |
0.35 |
3.10 |
1.0 |
1.0 |
0.03 |
0.10 |
0.60 |
0.03 |
14.0 |
7.0 |
0.02 |
Physical properties:
Density |
8.14 g/cm3 |
Melting point |
1280-1345°C |
Minimum mechanical properties in the room temperature:
Status |
Tensile strength Rm
N/mm2 |
Yield strength RP0.2
N/mm2 |
Elongation A5
% |
N09901 |
1034 |
689 |
12 |
Description
A nickel-iron-chromium alloy containing titanium and aluminum for precipitation hardening and molybdenum for solid-solution strengthening. The alloy has high yield strength and creep resistance at temperatures to about 1110°F (600°C). A subtantial iron content enables the alloy to combine high strength with good forging characteristics. Used in gas turbines for discs and shafts. Standard products form is round.
Corrosion Resistance
It has good corrosion resistance to the atmospheres normally found in jet engine operations. It has slightly lower scaling resistance than such alloy as Types 309 and 310 stainless steel.
Workability
Hot Working
It is forged between 2050°F (1121°C) and 1850°F (1010°C), metal temperature. Light hot work may be continued down to 1600°F (871°C) but not below. Metal temperature should not exceed 2050°F (1121°C) during rapid working. Billets should be charged into a hot furnace and heated rapidly through the precipitation hardening range.
Weldability
It can be welded by the inert-gas-arc method. It is difficult to weld. All welding should be done in the solution treated condition. Cold worked parts should be re-solution treated before welding. A re-solution treatment is recommended after welding before stabilizing and aging.