China High Hardness Sic Silicon Carbide Ceramic Silicon Nitride Aluminum Nitride Ceramic Parts Ain Si3n4, Find details about China Ceramic, Zirconia Ceramic from High Hardness Sic Silicon Carbide Ceramic Silicon Nitride Aluminum Nitride Ceramic Parts Ain Si3n4
Attribute | Zirconia | Alumina | ZTA |
Density | 5.9-6.05g/cm3 | 3.6-3.8g/cm3 | 4.8g/cm3 |
Hardness(HRC) | 88-90 | 80-86 | 86 |
Fracture Toughness | 10MPa.m½ | 4MPa.m½ | - |
Compressive Strength | 2000MPa | 1500MPa | 1700MPa |
CTE | 10.5ppm/ºC | 7.15-7.67ppm/ºC | 9.1ppm/ºC |
Maximum Operating Temperature | 1350ºC | 1700ºC | 1350ºC |
Thermal Conductivity(24ºC) | 2W/m.k | 18-28W/m.k | - |
Flexural Strength (24ºC) | 950MPa | 300MPa | 600MPa |
Water Absorption(%) | 0 | 0 | 0 |