1100 Light Weight Insulating Castables

China 1100 Light Weight Insulating Castables, Find details about China Refractory Castable, Low Cement Castable from 1100 Light Weight Insulating Castables

Basic Info.

Model NO.

Coolcast G

Origin

Liaoning

HS Code

38160000

Model NO.

Coolcast G

Origin

Liaoning

HS Code

38160000

Product Desciption

1100 Light Weight Insulating Castables

Description
CT series of castables is made from aggregate and powder , by adding binder or other admixture in it . This product is of good workability and after construction the furnace wall is of good integrity , especially suitable for the complex shape of wall lining.

Feature
1.Low thermal capacity.
2.High compressive strength.
3.Low thermal conductivity,good thermal insulation performance.
4.Good overall performance of furnace body , long service life.
5.Easy construction , can be arbitrary shaped.

Typical Application

1.Industrial kiln wall lining or high temperature industrial kiln backing insulation, including heating furnace , reforming furnace , delayed coking , hydrocracking furnace , etc
2.Ladle cover
3.Electric heating oven door,observation hole,burning nozzle brick,etc.
4.Colored,black metal melting groove and tank.
5.Covection cell lining material of petrochemical industry furnace.
6.The ladle lining material.

Specifications

Low cement castables

Remark: A: Iron & Steel Industry, B: Cement Industry,C: Power Industry, D: Aluminium Industry, E: HPI Industry

Date sheet

Type	CTQ-0.6	CTQ-0.8	CTQ-1.0	CTQ-1.2	CTQ-1.4	CTQ-1.6
Maximum Temperature(ºC)	800	900	1000	1100	1200	1500
Density(kg/m³)	600	800	1000	1200	1400	1700
Basic material	Vermiculite/expanded perlite	Ceramsite/Lightweight refractory aggregate	Ceramsite/Lightweight refractory aggregate	Lightweight refractory aggregate	High temperature of light weight refractory aggregate	Alumina bubble
Comperssive strength110ºCx24h(Mpa)	≥1.2	≥2.6	≥5	≥6	≥7	≥15
Permanent linear change	600ºCx5h≤0.6	800ºCx5h≤0.5	1000ºCx5h≤0.5	1000ºCx5h≤0.5	1200ºCx5h≤0.5	1400ºCx5h≤0.5
Thermal cpmductivity(W/m.k)	0.15(400ºC)	0.21(400ºC)	0.25(400ºC)	0.30(400ºC)	0.40(400ºC)	0.72(400ºC)