Submerged Arc Welding Flux Sj601 for Stainless Steel Strip
China Submerged Arc Welding Flux Sj601 for Stainless Steel Strip, Find details about China Welding Flux, Saw Flux from Submerged Arc Welding Flux Sj601 for Stainless Steel Strip
Basic Info.
Model NO.
sj601
Application
Submerged-arc Welding
Manufacturing Method
Sintering
Size
10-60mesh
OEM
Accpete
Accompanied Wire
308L, 309L, 316L, 347L Stailess Steel Wire
Applications
Stainless Steel Strip Cladding
Color
Blue Gray to Dark Gray
Suitable for
Surfacing/Hardfacing/Cladding
Brand
Panding
Free Sample
Offered
Key Word
Welding Powder
Steel
Stailess Steel
Trademark
PANDING
Transport Package
Kraft Bag with Plastic Lining Inside
Specification
En760 SA Af 2 AC H5
Origin
Laiwu, Shandong, China
HS Code
38109000
Model NO.
sj601
Application
Submerged-arc Welding
Manufacturing Method
Sintering
Size
10-60mesh
OEM
Accpete
Accompanied Wire
308L, 309L, 316L, 347L Stailess Steel Wire
Applications
Stainless Steel Strip Cladding
Color
Blue Gray to Dark Gray
Suitable for
Surfacing/Hardfacing/Cladding
Brand
Panding
Free Sample
Offered
Key Word
Welding Powder
Steel
Stailess Steel
Trademark
PANDING
Transport Package
Kraft Bag with Plastic Lining Inside
Specification
En760 SA Af 2 AC H5
Origin
Laiwu, Shandong, China
HS Code
38109000
Product Desciption
Agglomerated welding flux SJ601 for stainless steel strip cladding
Specifications:
NB/T47018-2011 GB/T17854-1999 F308-HOCr21Ni10 F309-HlCr24Ni13
F316L-H00Cr19Ni12Mo2
Description:
LH-SJ601 is stainless steel with alkali sintering flux,about 1.8 alkalinity,spherical particles,the particle size 10 to 60 mesh(1.7-0.25mm).It can be used on DC(+) or AC,when using DC(+),the wire to the positive(+),arc busing stability weld forming is smooth and beautiful,pure,deposited metal almost does not increase carbon,with the characteristics of chromium burning less suitable for low carbon and low carbon stainless steel submerged arc welding.
Usage:
when applied to appropriate welding wires such as HOCr21Ni10,HOOCr21Ni10 and HOOCr19Ni12Mo2, It can weld low-carbon steel,super-low carbon steel and highalloy heat-resisting steel,and is fit for multiway welding.
Cautions:
1.The oil soil,moisture,iron rust and other foreign substances must be removed form the welding joint.
2.The welding flux must be baked under 300-500ºC for 2 hours before welding.
Our service
1)Prime quality+Competitive price+Thoughtful Service=100% Satisfication
2)We can research and produce customerized fluxes according to your different demands.
3)SAW Welding Flux Expert- One Stop Solution For Submerged Arc Welding consumables.
Technical data sheet stainless steel welding wire
AWS A5.9 ER308
Description: The main chemical composition of stainless steel welding wire ER308 is 18Cr-8Ni. The weld metal has good mechanical properties, intergranular corrosion resistance and good crack resistance.
Application: Stainless steel welding wire ER308 can be used for welding austenitic stainless steel of type 18-8, 18-12 and 20-10. It is usually used for welding of similar composition, especially the type of 304.
Chemical Composition of Welding Wire(%)
GV=Guarantee Value
Mechanical Properties of Deposited Metal
Size & Recommended Current (AC/DC)
WA(A)=Welding Current (A)
X- ray Inspection: I
Instruction:
The wire should be kept in dry place.
The stains on the weldments, such as rust, oil stains, moisture, etc., must be cleared away.
AWS A5.9 ER308L
Description: ER308L is a extra low carbon stainless steel wire, it is used for automatic submerged
welding combining with SJ601 arc.
Application: for welding extra low carbon Cr18Ni8 stainless steel.such as ship hulls, bridges. Pressure vessels as well as H-beam structures.
Chemical Composition of Welding Wire(%)
GV=Guarantee Value
Mechanical Properties of Deposited Metal
GV=Guarantee Value
Size & Recommended Current (AC/DC)
WA(A)=Welding Current (A)
X- ray Inspection: I
Instruction:
The wire should be kept in dry place.
The stains on the weldments, such as rust, oil stains, moisture, etc., must be cleared away.
Products Picture:
Company Brief Introduction
(1)Company Name:Shandong Hulin Welding Material Co.,Ltd
(2)Main Products:
SAW Flux&Wire, MIG Wire, FCW wire.
(3)Best Selling Product Models:
SAW Flux:SJ101,SJ101G,SJ102,SJ301,SJ501,HJ107,HJ260,HJ431
SAW Wire: EM12K,EL8,EL12
MIG Wire: ER70S-6
FCW Wire: E71T-1
(5)Quality System:ISO9001:2000
(6)Year Established:1999
(7)Brand Name:Panding Brand
(8)Application: Steel Pipe, Structural steel, LPG Cylinder, Pressure vessel, Boiler, Bridges etc.
Packing & Shipping Details:
(1)Bag:25 KGS/Kraft Bag With Plastic Lining Inside
(2)Pallet:40 Bags(1 Ton)/Plywood Pallet
(3)Container:20-24 Tons/Container
(4)OEM & buyer label is ok, and technical support can be offered
FAQ:
Q. 1 Can you provide free sample?
A: Total free sample(including freight cost) can be offered
Q. 2 What is your delivery time?
A: Within 7 days after receiving deposit.
Q: 3 Is your price competitive with other companies?
A: Our goal is to give the best price with same quality and best quality with the same price. We do everything we can to reduce your cost.
Q. 4 How about OEM?
A: OEM IS OK.
Q. 5 Why we should choose your company?
A: Firstly, we are ORIGINAL factory. We can guarantee delivery time and provide special requirements for customers.
Secondly, we have professional foreign trade team with high efficiency communications and professional solutions.
Thirdly, we have special team work for after sales services 24*7 to help you slove any kind of problem
Contact Tracy
Specifications:
NB/T47018-2011 GB/T17854-1999 F308-HOCr21Ni10 F309-HlCr24Ni13
F316L-H00Cr19Ni12Mo2
Description:
LH-SJ601 is stainless steel with alkali sintering flux,about 1.8 alkalinity,spherical particles,the particle size 10 to 60 mesh(1.7-0.25mm).It can be used on DC(+) or AC,when using DC(+),the wire to the positive(+),arc busing stability weld forming is smooth and beautiful,pure,deposited metal almost does not increase carbon,with the characteristics of chromium burning less suitable for low carbon and low carbon stainless steel submerged arc welding.
Usage:
when applied to appropriate welding wires such as HOCr21Ni10,HOOCr21Ni10 and HOOCr19Ni12Mo2, It can weld low-carbon steel,super-low carbon steel and highalloy heat-resisting steel,and is fit for multiway welding.
Cautions:
1.The oil soil,moisture,iron rust and other foreign substances must be removed form the welding joint.
2.The welding flux must be baked under 300-500ºC for 2 hours before welding.
(Chemical Composition)(%)
SiO2+TiO2 | Al2O3+MnO | CaO+MgO | CaF2 | S | P |
5-10 | 30-40 | 6-10 | 40-50 | <=0.06 | <=0.06 |
(Mechanical Performance of the Deposited Metal)
Wires | Standard Models | бb | δ5 |
HOCr21Ni10 | F308-HOCr21Ni10 | ≥520 | ≥30% |
HOOCr21Ni10 | F308L-HOOCr21Ni10 | ≥480 | ≥25% |
Our service
1)Prime quality+Competitive price+Thoughtful Service=100% Satisfication
2)We can research and produce customerized fluxes according to your different demands.
3)SAW Welding Flux Expert- One Stop Solution For Submerged Arc Welding consumables.
Technical data sheet stainless steel welding wire
AWS A5.9 ER308
Description: The main chemical composition of stainless steel welding wire ER308 is 18Cr-8Ni. The weld metal has good mechanical properties, intergranular corrosion resistance and good crack resistance.
Application: Stainless steel welding wire ER308 can be used for welding austenitic stainless steel of type 18-8, 18-12 and 20-10. It is usually used for welding of similar composition, especially the type of 304.
Chemical Composition of Welding Wire(%)
GV=Guarantee Value
| Test Item | C | Mn | Si | S | P | Cr | Ni | Mo | Cu |
| GV | ≤0.08 | 1.0~2.5 | 0.3~0.65 | ≤0.03 | ≤0.03 | 19.5~22 | 9.0~11.0 | ≤0.75 | ≤0.75 |
| Typical | 0.05 | 1.79 | 0.37 | 0.011 | 0.023 | 20.15 | 9.52 | 0.008 | 0.09 |
Mechanical Properties of Deposited Metal
| Test Item | Rm(Mpa) | ReL(Mpa) | A(%) | KV2(J) |
| Typical | 580 | - | 42 | - |
Size & Recommended Current (AC/DC)
WA(A)=Welding Current (A)
| Dia(mm) | φ2.5 | φ3.2 | φ4.0 | φ5.0 |
| Current(A) | 80~140 | 250~350 | 350~450 | 400~500 |
X- ray Inspection: I
Instruction:
The wire should be kept in dry place.
The stains on the weldments, such as rust, oil stains, moisture, etc., must be cleared away.
AWS A5.9 ER308L
Description: ER308L is a extra low carbon stainless steel wire, it is used for automatic submerged
welding combining with SJ601 arc.
Application: for welding extra low carbon Cr18Ni8 stainless steel.such as ship hulls, bridges. Pressure vessels as well as H-beam structures.
Chemical Composition of Welding Wire(%)
GV=Guarantee Value
| Test Item | C | Mn | Si | S | P | Cr | Ni | Mo | Cu |
| GV | ≤0.03 | 1.0~2.5 | 0.3~0.65 | ≤0.03 | ≤0.03 | 19.5~22 | 9.0~11.0 | ≤0.75 | ≤0.75 |
| Typical | 0.023 | 1.76 | 0.51 | 0.019 | 0.018 | 19.92 | 9.56 | 0.1 | 0.11 |
Mechanical Properties of Deposited Metal
GV=Guarantee Value
| Test Item | Rm(Mpa) | ReL(Mpa) | A(%) | KV2(J) |
| GV | ≥520 | - | ≥35 | - |
| Typical | 592 | - | 42 | - |
Size & Recommended Current (AC/DC)
WA(A)=Welding Current (A)
| Dia(mm) | φ2.5 | φ3.2 | φ4.0 | φ5.0 |
| Current(A) | 80~140 | 250~350 | 350~450 | 400~500 |
X- ray Inspection: I
Instruction:
The wire should be kept in dry place.
The stains on the weldments, such as rust, oil stains, moisture, etc., must be cleared away.
Products Picture:
Company Brief Introduction(1)Company Name:Shandong Hulin Welding Material Co.,Ltd
(2)Main Products:
SAW Flux&Wire, MIG Wire, FCW wire.
(3)Best Selling Product Models:
SAW Flux:SJ101,SJ101G,SJ102,SJ301,SJ501,HJ107,HJ260,HJ431
SAW Wire: EM12K,EL8,EL12
MIG Wire: ER70S-6
FCW Wire: E71T-1
(5)Quality System:ISO9001:2000
(6)Year Established:1999
(7)Brand Name:Panding Brand
(8)Application: Steel Pipe, Structural steel, LPG Cylinder, Pressure vessel, Boiler, Bridges etc.
Packing & Shipping Details:
(1)Bag:25 KGS/Kraft Bag With Plastic Lining Inside
(2)Pallet:40 Bags(1 Ton)/Plywood Pallet
(3)Container:20-24 Tons/Container
(4)OEM & buyer label is ok, and technical support can be offered
FAQ:
Q. 1 Can you provide free sample?
A: Total free sample(including freight cost) can be offered
Q. 2 What is your delivery time?
A: Within 7 days after receiving deposit.
Q: 3 Is your price competitive with other companies?
A: Our goal is to give the best price with same quality and best quality with the same price. We do everything we can to reduce your cost.
Q. 4 How about OEM?
A: OEM IS OK.
Q. 5 Why we should choose your company?
A: Firstly, we are ORIGINAL factory. We can guarantee delivery time and provide special requirements for customers.
Secondly, we have professional foreign trade team with high efficiency communications and professional solutions.
Thirdly, we have special team work for after sales services 24*7 to help you slove any kind of problem
Contact Tracy
You Might Also Like
Inch Size R Series Open-Zz-2RS Deep Groove Ballbearings R144......
Dried Mealworms for Tropicl Fish
Wc67k Series Economic Type CNC Hydraulic Press Brake
White Cranked Espag UPVC Window Hardware Handle
VFD 37kw/45kw 380V Inverter Torque Control Motor Frequency I......
0.9mx9m 14mm Multiple Color PVC Coil Plastic Mat
Stainless Steel Broken Reverse Twill Dutch Weave Wire Mesh 1......
Factory Price of Sodium Pyrrolidone Carboxylate CAS 28874 -5......
60Hz 1800rpm 50kVA/40kw Perkins Engine Diesel Generator Set ......
Blue Simple Rubber Squeeze Shower Duck
Jaw Crusher Low Price Mining Crushing Machine Zhengzhou
25mm Sturdy Steel Cam Buckles Motorbike Tie-Down Straps Asse......