China Smooth Textured Surface HDPE Pond Liners for Fish Shrimp Farm, Find details about China HDPE Geomembrane, HDPE Liner from Smooth Textured Surface HDPE Pond Liners for Fish Shrimp Farm
NO. | Item | Index | |
GH-HDPE | |||
GH-1 | GH-2 | ||
1 | The tensile strength Mpa | ≥ 17 | ≥ 25 |
2 | The percentage of breaking elongation rate % | ≥ 450 | ≥ 550 |
3 | Right-angle tear strength N/mm | ≥ 80 | ≥ 110 |
4 | Carbon black content 13% | ≥ 2 | |
5 | Environmental stress cracking resistance F 20h | - | ≥ 1500 |
6 | Oxidative induction time at 200 ºC min | - | ≥ 20 |
7 | The permeability coefficient of water vapor | ≤ 1.0 × 10 -13 | |
gcm/(cmsPa) | |||
8 | The impact and embrittlement property in low-temperature at 70 ºC below zero | pass the detection | |
9 | Dimensional stability percentage % | ± 3 |
No. | Properties | Test Method | Test Value | |||||||
1 | Thickness(mm) | ASTM D5199 | 0.50 | 0.75 | 1.00 | 1.25 | 1.50 | 2.00 | 2.50 | 3.00 |
2 | Density (g/cm2) | ASTM D1505 | 0.939 | |||||||
3 | Tensile Propeties | |||||||||
Yield Strength(N/mm) | ASTM D6693 | 7 | 11 | 15 | 18 | 22 | 29 | 37 | 44 | |
Break Strength(N/mm) | 13 | 20 | 27 | 33 | 40 | 53 | 67 | 80 | ||
Yield Elongation % | Type IV | 12 | ||||||||
Break Elongation % | 700 | |||||||||
4 | Tear Resistance/N | ASTM D1004 | 62 | 93 | 125 | 156 | 187 | 249 | 311 | 374 |
5 | Puncture Resistance/N | ASTM D4833 | 160 | 240 | 320 | 400 | 480 | 640 | 800 | 960 |
6 | Stress Crack resistance/hr | ASTM D5397 (App.) | 300 | |||||||
7 | Carbon Black | |||||||||
Carbon Black Content % | ASTM D1603 | 2.0-3.0 | ||||||||
Carbon Black Dispersion | ASTM D5596 | Carbon black dispersion(only near spherical agglomerates) for 10 different views 9 in categories 1 or 2 and 1 in category 3 | ||||||||
8 | Oxidative Induction Time(OIT) | |||||||||
Standard OIT/min | ASTM D3895 | 100 | ||||||||
High Pressure OIT/min | ASTM D5885 | 400 | ||||||||
9 | Oven Aging at 85°C | |||||||||
Standard OIT-% retained after 90 days | ASTM D3895 | 55 | ||||||||
High pressure OIT-% retained after 90 days | ASTM D5885 | 80 | ||||||||
10 | UV Resistance | |||||||||
Standard OIT retained after 1600 hrs | ASTM D3895 | 50 | ||||||||
High pressure OIT retained after 1600 hrs | ASTM D5885 | 50 | ||||||||
11 | Low tempreture impact brittle property at -70°C | _ | Pass | |||||||
12 | Permeability g·cm/(cm2)·Pa | _ | ≤1.0×10-13 | |||||||
13 | Dimensional Stability/% | _ | ±2 |